Earlier experimental findings concluded that electromigratin voids in these meandering stripe test structures were not randomly distributed and that void nucleation frequenly occurred sub-surface at the metal/thermal oxide interface.
The ultrasonic wave propagation characteristics were measured for IN-100, a powder metallurgy alloy used for aircraft engine components. This material was as a model system for testing the feasibility of characterizing the microstructure of a variety of inhomogeneous media including powder metals, ceramics, castings and components. The data were obtained for a frequency range from about 2 to 20 MHz and were statistically averaged over numerous volume elements of the samples. Micrographical examination provided size and number distributions for grain and pore structure. The results showed that the predominant source for the ultrasonic attenuation and backscatter was a dense (approx. 100/cubic mm) distribution of small micropores (approx. 10 micron radius). Two samples with different micropore densities were studied in detail to test the feasibility of calculating from observed microstructural parameters the frequency dependence of the microstructural backscatter in the regime for which the wavelength is much larger than the size of the individual scattering centers. Excellent agreement was found between predicted and observed values so as to demonstrate the feasibility of solving the forward problem. The results suggest a way towards the nondestructive detection and characterization of anomalous distributions of micropores when conventional ultrasonic imaging is difficult. The findings are potentially significant toward the application of the early detection of porosity during the materials fabrication process and after manufacturing of potential sites for stress induced void coalescence leading to crack initiation and subsequent failure.
Specimens of PMR-15 polyimide neat resin were aged in air at temperatures of 288, 316, and 343 C. Weight losses and dimensional changes were monitored during the course of the exposure time. Physical changes were also observed by optical and electron microscopy. It was found that polyimide polymer degradation occurred within a thin surface layer that developed and grew during thermal aging. The cores of the polymer specimens were protected from oxidative degradation, and they were relatively unchanged by the thermal treatment. Surface cracking was observed at 343 C and was probably due to an interaction between voids and stresses that developed in the surface layer.
Specimens of PMR-15 polyimide neat resin were aged in air at temperatures of 288, 316, and 343 C. Weight losses and dimensional changes were monitored during the course of the exposure time. Physical changes were also observed by optical and electron microscopy. It was found that polyimide polymer degradation occurred within a thin surface layer that developed and grew during thermal aging. The cores of the polymer specimens were protected from oxidative degradation, and they were relatively unchanged by the thermal treatment. Surface cracking was observed at 343 C and was probably due to an interaction between voids and stresses that developed in the surface layer.
Composite Overwrapped Pressure Vessels (COPVs) are frequently used for storing pressurized gases aboard spacecraft and aircraft when weight saving is desirable compared to all-metal versions. Failure mechanisms in fibrous COPVs and variability in lifetime can be very different from their metallic counterparts; in the former, catastrophic stress-rupture can occur with virtually no warning, whereas in latter, a leak before burst design philosophy can be implemented. Qualification and certification typically requires only one burst test on a production sample (possibly after several pressure cycles) and the vessel need only meet a design burst strength (the maximum operating pressure divided by a knockdown factor). Typically there is no requirement to assess variability in burst strength or lifetime, much less determine production and materials processing parameters important to control of such variability. Characterizing such variability and its source is crucial to models for calculating required reliability over a given lifetime (e.g. R = 0.9999 for 15 years). In this paper we present a case study of how lack of control of certain process parameters in COPV manufacturing can result in variations among vessels and between production runs that can greatly increase uncertainty and reduce reliability. The vessels considered are 40-inch ( NASA Glenn Research center, Cleveland, OH, 44135 29,500 in3 ) spherical COPVs with a 0.74 in. thick Kevlar49/epoxy overwrap and with a titanium liner of which 34 were originally produced. Two burst tests were eventually performed that unexpectedly differed by almost 5%, and were 10% lower than anticipated from burst tests on 26-inch sister vessels similar in every detail. A major observation from measurements made during proof testing (autofrettage) of the 40-inch vessels was that permanent volume growth from liner yielding varied by a factor of more than two (150 in3 to 360 in3 ), which suggests large differences in the residual stress gradient through their overwraps. This resulted in large uncertainty in true fiber stress ratio (fiber stress at operating pressure divided by fiber stress at burst) which governs lifetime. The vessels were originally designed with tight safety margins, so it became crucial to develop a non-destructive evaluation (NDE) technique to directly measure the overwrap residual stress state of each vessel, and to identify those vessels at highest risk of having poor reliability. This paper describes a Raman Spectroscopy technique for measuring certain patterns of fluctuation in fiber elastic strains over the outside vessel surface (where all but one wrap is exposed at certain locations) that are shown to directly correlate to increased fiber stress ratios and reduced reliability.
Molecular dynamics simulations of carbon nanotube (CNT) composites, in which the CNTs are continuous across the periodic boundary, overestimate the experimentally measured mechanical properties of CNT composites along the fiber direction. Since the CNTs in these composites are much shorter than the composite dimensions, load must be transferred either directly between CNTs or through the matrix, a mechanism that is absent in simulations of effectively continuous CNTs. In this study, the elastic and fracture properties of high volume fraction discontinuous carbon nanotube/amorphous carbon composite systems were compared to those of otherwise equivalent continuous CNT composites using ReaxFF reactive molecular dynamics simulations. These simulations were used to show how the number of nanotube-matrix interfacial covalent bonds affect composite mechanical properties. Furthermore, the mechanical impact of interfacial bonding was decomposed to reveal its effect on the properties of the CNTs, the interfacial layer of matrix, and the bulk matrix. For the composites with continuous reinforcement, it was found that any degree of interfacial bonding has a negative impact on axial tensile strength and stiffness. This is due to disruption of the structure of the CNTs and interfacial matrix layer by the interfacial bonds. For the discontinuous composites, the modulus was maximized between 4%-7% interfacial bonding and the strength continues to increase up to the highest levels of interfacial bonding studied. Areas of low stress and voids were observed in the simulated discontinuous composites at the ends of the tubes, from which fracture was observed to initiate. Experimental carbon nanotube yarn composites were fabricated and tested. The results were used to illustrate knockdown factors relative to the mechanical performance of the tubes themselves.
Reliable applications of adhesively bonded joints require understanding of the stress distribution along the bond-line and the stresses that are responsible for the joint failure. To properly evaluate factors affecting peel strength, effects of defects such as voids on the stress distribution in the overlap region must be understood. In this work, the peel stress distribution in a single lap joint is derived using a strength of materials approach. The bonded joint is modeled as Euler-Bernoulli beams, bonded together with an adhesive. which is modeled as an elastic foundation which can resist both peel and shear stresses. It is found that for certain adhesive and adherend geometries and properties, a central void with the size up to 50 percent of the overlap length has negligible effect on the peak peel and shear stresses. To verify the solutions obtained from the model, the problem is solved again by using the finite element method and by treating the adherends and the adhesive as elastic materials. It is found that the model used in the analysis not only predicts the correct trend for the peel stress distribution but also gives rather surprisingly close results to that of the finite element analysis. It is also found that both shear and peel stresses can be responsible for the joint performance and when a void is introduced, both of these stresses can contribute to the joint failure as the void size increases. Acoustic emission (AE) activities of aluminum-adhesive-aluminum specimens with different void sizes were monitored. The AE ringdown counts and energy were very sensitive and decreased significantly with the void size. It was observed that the AE events were shifting towards the edge of the overlap where the maximum peeling and shearing stresses were occurring as the void size increased.
During the last decade, ground-based microgravity facilities have been utilized in order to obtain predictions for spacecraft system designers and further the fundamental understanding of two-phase flow. Although flow regime, pressure drop and heat transfer coefficient data has been obtained for straight tubes and a limited number of fittings, measurements of the void fraction, film thickness, wall shear stress, local velocity and void information are also required in order to develop general mechanistic models that can be utilized to ascertain the effects of fluid properties, tube geometry and acceleration levels. A review of this research is presented and includes both empirical data and mechanistic models of the flow behavior.
Reliable applications of adhesively bonded joints require an effective nondestructive evaluation technique for their bond strength prediction. To properly evaluate factors affecting bond strength, effects of defects such as voids and disbonds on stress distribution in the overlap region must be understood. At the same time, in order to use acousto-ultrasonic (AU) technique to evaluate bond quality, the effect of these defects on dynamic response of single lap joints must be clear. The stress distribution in a single lap joint with and without defects (void or disbond) is analyzed. A bar-Theta parameter which contains adherend and adhesive thickness and properties is introduced. It is shown for bonded joints with bar-Theta greater than 10, that a symmetric void or disbond in the middle of overlap up to the 70 percent of overlap length has negligible effect on bond strength. In contrast frequency response analyses by a finite element technique showed that the dynamic response is affected significantly by the presence of voids or disbonds. These results have direct implication in the interpretations of AU results. Through transmission attenuation and a number of AU parameters for various specimens with and without defects are evaluated. It is found that although void and disbond have similar effects on bond strength (stress distribution), they have completely different effects on wave propagation characteristics. For steel-adhesive-steel specimens with voids, the attenuation changes are related to the bond strength. However, the attenuation changes for specimens with disbond are fairly constant over a disbond range. In order to incorporate the location of defects in AU parameters, a weighting function is introduced. Using an immersion system with focused transducers, a number of AU parameters are evaluated. It is found that by incorporating weighting functions in these parameters better sensitivities (AU parameters vs. bond strength) are achieved. Acoustic emission (AE) activities of steel-adhesive-steel specimens with bar-Theta equal to 3.4 are monitored. Two different formats of energy vs. time have resulted, each corresponding to the perfect specimens or the specimens with void or disbond. The relative acoustic energy and the number of events at failure are found to be a means for predicting the bond strength.
An acoustic-ultrasonic method is described that was successful in ranking unidirectional graphite-polyimide composite specimens according to variations in interlaminar shear strength. Using this method, a quantity termed the stress wave factor was determined. It was found that this factor increases directly with interlaminar shear strength. The key variables in this investigation were composite density, fiber weight fraction, and void content. The stress wave factor and other ultrasonic factors that were studied were found to provide a powerful means for nondestructive evaluation of mechanical strength properties.
Ultrasonic techniques that have demonstrated potential for material characterization are reviewed. These techniques rely on physical acoustic properties of materials and the interaction of elastic stress waves with morphological factors in the ultrasonic regime. The speed of wave propagation and energy loss by interaction with material microstructure and geometrical factors underlie ultrasonic determination of material properties. Two categories of ultrasonic measurements are discussed: those related to material strengths (e.g., elastic moduli, tensile strength, and fracture toughness) and those related to morphology and material conditions that govern strength and performance (e.g., microstructure, void content, residual stress, fatigue damage). It is shown that large-scale industrial application of ultrasonic NDE will depend on advancement in such areas as theory development, instrumentation, system automation, standardization, and coordination with design.
The final report consists of 5 published papers in referred journals and a technical letter to the technical monitor. These papers include the following: (1) Comparison of the effects of debonds and voids in adhesive; (2) On the peak shear stresses in adhesive joints with voids; (3) Nondestructive evaluation of adhesively bonded joints by acousto-ultrasonic technique and acoustic emission; (4) Multiaxial fatigue life evaluation of tubular adhesively bonded joints; (5) Theoretical and experimental evaluation of the bond strength under peeling loads. The letter outlines the progress of the research. Also included is preliminary information on the study of nondestructive evaluation of composite materials subjected to localized heat damage. The investigators studied the effects of localized heat on unidirectional fiber glass epoxy composite panels. Specimens of the fiber glass epoxy composites were subjected to 400 C heat for varying lengths of time. The specimens were subjected to nondestructive tests. The specimens were then pulled to their failure and acoustic emission of these specimens were measured. The analysis of the data was continuing as of the writing of the letter, and includes a finite element stress analysis of the problem.
An analytical model is developed to compare the effects of voids an debonds on the interfacial shear stresses between the adherends and the adhesive in simple lap joints. Since the adhesive material above the debond may undergo some extension (either due to applied load or thermal expansion or both), a modified shear lag model, where the adhesive can take an extensional as well as shear deformation, is used in the analysis. The adherends take on only axial loads and act as membranes. Two coupled nondimensional differential equations are derived, and in general, five parameters govern the stress distribution in the overlap region. As expected, the major differences between the debond and the void occur for the stresses near the edge of the defect itself. Whether the defect is a debond or a void, is hardly discernible by the stresses at the overlap region. If the defect occurs precisely at or very close to either end of the overlap, however, differences of the order of 20 percent in the peak stresses can be obtained.
PTFE made thermally compatible with aluminum without changing dielectric constant. Manufactured with fillers and pores to reduce coefficient of thermal expansion by factor of 6 to match aluminum. Material retains 2.1 dielectric constant of pure PTFE. Combines filler and micropore concepts. Particles and voids embedded in PTFE matrix function cooperatively. Particles take up compressive stress imposed by contracting PTFE, and voids take up expanding material. Increases dielectric constant, while voids reduce it.
Study of the kinetics of hydrogen-induced cracking in the Ti-5Al-2.5Sn titanium alloy, which has a structure of acicular alpha platelets in a beta matrix. The crack-growth rate at low stress-intensity levels was found to be exponentially dependent on stress intensity but essentially independent of temperature. The crack-growth rate at intermediate stress-intensity levels was found to be independent of stress intensity but dependent on temperature in such a way that crack-growth rate was controlled by a thermally activated mechanism having an activation energy of 5500 cal/mole and varied as the square root of the hydrogen pressure. The crack-growth rate at stress-intensity levels very near the fracture toughness is presumed to be independent of environment. The results are interpreted to suggest that crack growth at high stress intensities is controlled by normal, bulk failure mechanisms such as void coalescence and the like. At intermediate stress-intensity levels the transport of hydrogen to some interaction site along the alpha-beta boundary is the rate-controlling mechanism. The crack-growth behavior at low stress intensities suggests that the hydrogen interacts at this site to produce a strain-induced hydride which, in turn, induces crack growth by restricting plastic flow at the crack tip.
The three dimensional soft particles (such as sulfides, silicates and voids) present in most materials are modelled by circular voids in sheet metal. Relationships are sought between the shape and orientation of a hole after rolling and testing in tension. Then, the effect of hole shape and size on mechanical properties is considered experimentally. The presence of voids has a negligible influence on the ultimate tensile stress of ductile materials based on the unperforated area because plastic flow neutralizes the stress intensification present in the elastic region. However, the shape and orientation of the defects are found to play an important role relative to strain at fracture. In certain engineering applications the strain at fracture is more important than the stress at fracture and in this sense the presence of voids are considered to influence the strength of a ductile material.
Stress, fatigue, and workload affect worker performance. NSF reported that 61% of respondents state losing concentration at work while 79% occasionally or frequently made errors as a result of being fatigued. Shift work, altered work schedules, long hours of continuous wakefulness, and sleep loss can create sleep and circadian disruptions that degrade waking fundions causing stress and fatigue. Review of the literature has proven void of information that links the combined effects of fatigue, stress, and workload to human performance. This paper will address which occupational factors within stress, fatigue, and workload were identified as occupational contributors to performance changes. The results of this research will be apglied to underlying models and algorithms that will help predict performance changes in control room operators.
Divecha et al. (1981) have discussed the advantages of materials obtained by adding silicon carbide whiskers to commercial aluminum alloys, taking into account also certain problems which are related to poor ductility and low fracture toughness. The present investigation has the objective to advance the understanding of the deformation at the whisker ends in reinforced aluminum composites through both observation and analysis. It is suggested that the low fracture toughness of the considered materials is the result of the rapid accumulation of damage at the whisker ends. It is pointed out that the whisker ends are sites of severe stress concentration and intense localized plastic strain. In connection with this situation, voids nucleate and grow at relatively low macroscopic stress levels. The reported studies include an examination of the deformation microstructure beneath the fracture surfaces of specimens with the aid of transmission electron microscopy.