Multiscale Modeling of Fracture Strength in Fibrous Thermal Protection System Materials
Explore the source record for details and available documents.
Jaehyun Cho↗
SEARCH · Search NASA
Results for “system strength”
Search indexed NASA NTRS and DOE OSTI research on propulsion, heat transfer, battery materials and energy systems. Follow report and document links to the original sources.
Quote a phrase for an exact phrase match. Source license links do not imply unrestricted reuse.
Multiscale Modeling of Fracture Strength in Fibrous Thermal Protection System Materials
This work presents a multiscale modeling approach to predict the fracture strength of fibrous Thermal Protection System (TPS) materials. The model assumes that system failure is initiated at the joints between individual fibers. We investigated three distinct TPS compositions: amorphous silica, alumina and aluminosilicate fibers. Molecular dynamics (MD) simulations were employed to determine the fracture strength values of these fiber joints for both material systems. These fracture strength values were then integrated into simulations of 3D randomly populated fiber structures, where tensile load transfer occurs through the fiber joints. These microscale properties are upscaled through a renormalization approach [1] to predict macroscale tensile strength of 3D random fiber networks, accounting for joint-dominated failure and effective load-bearing area. The study concludes by demonstrating the resulting strength variation as a function of material composition, fiber density, and morphology. We also show validation of results by comparing them against explicit fiber finite element (FE) modeling [2] where fiber joint fracture is represented by cohesive elements.
Jaehyun Cho↗
Quantifying System Strength From Grid-Forming Resources Using Frequency Scan Approach: Preprint
Current industry practices for quantifying the system strength contribution from grid-forming (GFM) resources to ensure stability of power systems dominated by inverter-based resources (IBRs) are primarily based on iterative electromagnetic transient (EMT) time-domain simulation studies. While feasible, these approaches are resource-intensive, lack scalability and intuition, and might not evaluate the system strength contribution over the entire frequency range of interest. This paper introduces a novel, frequency-domain approach to quantify system strength support provided by a GFM resource using frequency scans. The proposed method uses transfer functions from the grid voltage magnitude (V) and phase (?), respectively, to the reactive (Q) and active power (P) output of a GFM resource for quantifying its contribution to system strength. These transfer functions provide a direct measure of the ability of a GFM resource to behave as a stiff voltage source behind a reactance over a specified frequency range, enabling robust quantification of its system strength contribution. The key innovation of this work is the development of a frequency domain system strength metric called the dynamic short-circuit ratio (dSCR) that is suitable for IBR-dominated power systems and is directly related with the familiar short circuit ratio (SCR) metric. The new metric, dSCR, enables the assessment of system strength contributions from both synchronous machines and converter-based GFM resources using a unified benchmark, which is not possible with the traditional SCR metric. The paper also demonstrates how impedance scans could identify if an unstable condition observed during weak grid conditions is a result of the lack active or reactive power support or both. By leveraging the proposed frequency-domain dSCR metric for quantifying system strength contribution from GFM IBRs, the paper demonstrates targeted mitigation strategies for weak grid instabilities without resorting to repeated, time-consuming time-domain simulations. The result is a scalable and efficient approach to remediate stability challenges in power systems with high shares of IBRs and accelerating the integration of GFM technologies for system strength support in power systems.
24 POWER TRANSMISSION AND DISTRIBUTION↗
Computationally Accelerated Materials Development for Ultra High Strength Lightweight Structures
Explore the source record for details and available documents.
Mia Siochi↗
Vanishing dynamic strength measured in a transient high-pressure phase of tin
This work reports two independent experimental estimations of the dynamic strength of the body-centered tetragonal (bct) 𝛾 phase of tin, which occurs at pressures above about 9 GPa and transforms promptly back to the ambient 𝛽 phase upon pressure release. Measuring strength in such a transient high-pressure phase is challenging. One measurement used free-surface Richtmyer-Meshkov instabilities generated with gas gun impact. Another set of measurements used ramp-release loading in a pulsed-power facility. Strength estimations came from comparison to simulations using a comprehensive multiphase modeling framework that includes equation of state, shear moduli, and strength separately for each phase, and treats mixed-phase regions. Both experimental methods found the 𝛾-phase strength to be very low, within experimental uncertainty of zero. The existing literature on other materials, by contrast, almost universally reports higher strength in transient high-pressure phases compared with ambient phases. Recent Molecular-Dynamics simulations on tin in the literature showed almost zero deviatoric strength during a deformation-induced bct → bct transformation in which one of the 𝛾-phase 𝑎 axes “flips” to the 𝑐 axis. This reorientation currently provides the most plausible explanation for the low observed strength in 𝛾-phase tin.
36 MATERIALS SCIENCE↗
Effect of Thermodynamic and Environmental Factors on Crystallization of DNA‐Origami Superlattices
The directed self‐assembly of nanoscale materials into ordered superlattices presents a powerful strategy for creating next‐generation materials with programmable mechanical, optical, and photonic properties. Deoxyribonucleic acid (DNA) origami has emerged as a versatile scaffold for encoding nanoscale geometry and guiding the crystallization of complex 3D architectures. However, a systematic understanding of the parameters that govern the efficiency and quality of superlattice formation remains limited. In this study, we utilize octahedral DNA nanoscale frames as a model system to investigate the relative influence of key factors, including buffer composition, ionic strength, frame concentration, and thermal annealing protocols, on the size, order, and reproducibility of the resulting superlattices. Our findings provide a quantitative framework to rationally optimize DNA‐based assembly pathways. Structural characterization via small‐angle x‐ray scattering (SAXS), scanning electron microscopy (SEM), and optical microscopy validates the quality and fidelity of the assembled lattices. Moreover, by templating these DNA frameworks into inorganic replicas, we establish general design principles that extend beyond biomolecular systems, providing a foundation for the synthesis of programmable materials in broader nanofabrication contexts.
77 NANOSCIENCE AND NANOTECHNOLOGY↗
Ramp-release experiments for strength measurements: Strain-rate dependence
This paper presents an enhanced analysis method for investigating material properties at high strain rates, extending the capability of established experimental techniques to gain more information. The ramp-release method has been applied to many experiments reported at high (≈10 5 − 10 6 s −1 ) strain-rates. More recent data gathered at the National Ignition Facility (NIF) has enabled higher (≈10 8 s −1 ) strain-rates to be studied. Here, we present an initial application of ramp-release analysis to NIF ramp-compression data, illustrating both the opportunities and the practical challenges of extending these methods to laser-driven platforms. The higher strain-rates accessed at the NIF mean that there is more strain-rate enhancement to strength, and the experimental configuration means that this enhancement is more readily seen in the data. This is enabled by the capability of avoiding peak-compression attenuation through the sample thickness with a designed hold period made possible by the pulse-shaping capability of NIF. We propose that this combination of experimental conditions and an enhanced analysis method enables the strain-rate enhancement to strength to be studied, and potentially for this to inform physics models at smaller scales than the continuum.
36 MATERIALS SCIENCE↗
Softening the Gap between Wöhler and Paris – New Approaches for Fatigue Analysis –
Fatigue analysis tools can vary across industries. For example, automotive engineers often use the Wöhler (S-N) approach to design for safe-life, while aerospace engineers prioritize damage tolerance and inspection intervals, relying instead on crack growth models such as Paris’ law. Although both approaches may deal with the control of cracks in similar materials, their analysis tools and material characterizations are fundamentally distinct. This divide mirrors the classic split between stress-based strength analysis and linear elastic fracture mechanics. However, modern nonlinear models that incorporate material softening, such as cohesive laws, blur this boundary and capture fracture behaviors across scales. This presentation describes the CF23 fatigue model, which uses cohesive softening to link S-N crack initiation with crack propagation rates. CF23 spans the full fatigue spectrum, from initial propagation transients to steady-state growth and threshold conditions, offering a unified framework that bridges Wöhler and Paris-based methodologies. Example applications include fatigue crack propagation transients in adhesive interfaces and skin/stiffener separation.
cohesive elements↗
Corrosion Resistance of Lignin-Based Thermoplastic Adhesive-Bonded Aluminum Joints
Adhesive-bonded joints are essential for lightweight, multimaterial automotive structures. We developed a lignin-based thermoplastic adhesive with adhesion strength comparable to conventional epoxy adhesives (20–23 MPa), while offering exceptional durability, recyclability, and corrosion resistance. Unlike commercial epoxy adhesives requiring refrigerated storage, our adhesive retains its bonding potential after a year of ambient conditioning. Bonded joints can be repeatedly disassembled and rejoined with less than 2% strength loss. After 500 h of salt fog exposure, the adhesive-bonded aluminum joints exhibited a 24% strength reduction, compared to 61% reduction in strength of joints based on a commercial epoxy adhesive.
Yu, Zeyang [ORNL] (ORCID:0000000209002374)↗
Influence of Processing Parameters on the Mechanical Properties of 3D Printed Borosilicate Particulate Reinforced Polymer Composites
Emerging composite materials are expanding the potential of additive manufacturing and enabling applications previously restricted by traditional manufacturing methods. The multi-phase nature of these composite materials combined with the complex in-ternal geometry of additively manufactured parts have enabled unique behavior, and potentially new applications. Additionally, these materials can be pyrolyzed to create dense metal, ceramic, and glass parts with geometries typically not achievable by tra-ditional processes. Additive manufacturing of borosilicate glass-based systems can open new applications in nuclear engineering, astronomy, and bone regrowth therapy. To elucidate the process-parameter relationship of borosilicate-polylactic acid (PLA) composites, mechanical testing was conducted and compared with a pure polylactic acid polymer baseline. Test specimens were fabricated by fused-filament fabrication with minimal post-processing. Yield strength, ultimate strength, and elastic modulus were calculated from stress-strain curves. Optical and scanning electron microscopy were conducted to observe the specimen microstructure before and after testing. The highest compressive yield strength for the composite was 28.22 MPa, and the highest compressive yield strength for PLA was 49.30 MPa. Print orientation was found to benefit the composite material but have a detrimental effect on the pure matrix material. An elastic modulus of 2.66 GPa was recorded for the borosilicate-PLA composite at 100% infill, 1 shell wall, and layer lines parallel to compression axis. Microscopy revealed that lower modulus composite specimens had the particulates re-distributed within the matrix. Tensile testing was done according to a polymer testing standard, which caused difficulties obtaining consistent fracture within the gauge length.
mechanical testing↗
Mechanical properties of glasses impacted by debris or micrometeorites
Mechanical strength measurements on five glasses and one glass ceramic exposed on the Long Duration Exposure Facility (LDEF) have revealed no damage exceeding experimental limits of error after exposure. The measurement technique subjected less than 5 percent of the sample surface area to stresses above 90 percent of the failure strength. Seven micrometeorite or space debris impacts occurred at locations which were not in that portion of the sample subjected to greater than 90 percent of the applied stress. In consequence of this, the impact events on the sample were not detected in mechanical strength measurements. The physical form and structure of the impact sites was carefully examined to determine the influence of those events upon stress concentration associated with the impact and the resulting mechanical strength influence. The size of the impact site insofar as it determines flaw size for fracture purposes was examined. Surface topography of the impacts reveals that six of the seven sites display impact melting. The classical melt crater structure is surrounded by a zone of fractured glass. Residual stresses arising from shock compression and from cooling of the impact fused zone cannot be included in fracture mechanics analyses based on simple flaw size analyses. Strategies for refining estimates of mechanical strength degradation by impact events are presented.
Donald L. Kinser↗
Effect of Barely Visible Impact Damage on Thermoplastic Welded Structure
Spirit Aerosystems recently conducted screening tests on thermoplastic skin/stringer panels manufactured with Automated Fiber Placement (AFP) and stamp forming which were joined using Spirit’s Co-Fusion process. Skin and stringer gauge were both set to 0.168 cm. The resulting panel design is 48 cm tall, 49 cm wide, and has 3 stringers welded at a 21.5 cm pitch. Barely Visible Impact Damage (BVID) and Residual Compressive Strength were chosen to conduct a damage tolerance study. Zee stringers, made with IM8/PEKK-FC material, were Co-Fusion welded to a T1100/TC1225 skin. Out of these 5 panels, 1 was chosen to be a BVID survey panel, 1 for pristine compressive strength determination, and 3 to be impacted to create BVID followed by testing for residual compressive strength. On the survey panel, impacts ranged in energy from 40J – 65J and dent depth measurements were conducted at 24 hours, 48 hours, and two weeks after impacting. The residual compressive strength panel failed near the predicted load of 214 MPa. For the residual compressive strength panels, BVID was created at two different mid-bay locations: 1) striking the OML coincident with the stringer and 2) striking the skin IML 2.5 cm away from the stringer flange. Pulse Echo Ultrasonic Testing was used to inspect the panels before and after creating BVID.
HiCAM↗
The effect of dogbone sample size in the tensile testing of TATB-based plastic‑bonded explosive materials
Mechanical properties are of interest for many plastic‑bonded explosive (PBX) materials with tensile properties being of particular interest. Direct tensile measurements using dogbone-shaped samples are considered the gold standard, but they are fairly large, making testing more costly and less desirable from a safety perspective. We investigated whether the measured tensile strength depends on the dogbone specimen size, which to our knowledge, has not been reported in the literature for PBX materials. Understanding this should inform the feasibility of employing smaller samples and how sample size should be considered when comparing PBX dogbone values in the literature. The TATB-based PBX dogbone sample size was varied by (a) scaling all dimensions proportionally and (b) varying only the length of the samples. It was observed that the measured tensile peak stress (strength) was a function of the sample size, and was more dependent on the diameter (cross-sectional area) than the length of the samples. Since peak stress is calculated as peak force normalized to the diameter of the sample, one might not expect an explicit diameter dependence for the peak stress. Therefore, these results suggest there may be an additional strengthening effect as the sample diameter is increased.
37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
Reliability Analysis of Single Crystal NiAl Turbine Blades
As part of a co-operative agreement with General Electric Aircraft Engines (GEAE), NASA LeRC is modifying and validating the Ceramic Analysis and Reliability Evaluation of Structures algorithm for use in design of components made of high strength NiAl based intermetallic materials. NiAl single crystal alloys are being actively investigated by GEAE as a replacement for Ni-based single crystal superalloys for use in high pressure turbine blades and vanes. The driving force for this research lies in the numerous property advantages offered by NiAl alloys over their superalloy counterparts. These include a reduction of density by as much as a third without significantly sacrificing strength, higher melting point, greater thermal conductivity, better oxidation resistance, and a better response to thermal barrier coatings. The current drawback to high strength NiAl single crystals is their limited ductility. Consequently, significant efforts including the work agreement with GEAE are underway to develop testing and design methodologies for these materials. The approach to validation and component analysis involves the following steps: determination of the statistical nature and source of fracture in a high strength, NiAl single crystal turbine blade material; measurement of the failure strength envelope of the material; coding of statistically based reliability models; verification of the code and model; and modeling of turbine blades and vanes for rig testing.
Joseph Palko↗
Advanced Materials Testing Plan for the Space Suit Portable Life Support System
The Space Suit Portable Life Support System (PLSS) has a tight mass requirement to meet while also meeting other requirements for supporting a crewmember in space, on the Moon, or on Mars. To meet these requirements, atypical materials must be considered to close the mass budget allocations. However, many of these materials and processes are relatively new and untested. Therefore, initial analysis and testing of some new and advanced processes have been conducted following a roadmap presented last year. This material testing has focused primarily on thermoplastics, both additively manufactured and machined, to assess plating and fastening operations that will be required. These processes will provide additional strength and shielding capability typically only achieved with metallics. This testing has also helped to define a forward plan to certify these materials and processes for critical spaceflight applications. This report will review testing plated thermoplastics both for strength and thermal properties. It will also review fastener and fastening options and look at insert and fastener testing. It will also review state-of-the-art methods being considered elsewhere and some additional testing being conducted. Using the testing results researched here, there will be recommendations on applications for each of these types of methods going forward.
Ryan Ogilvie↗
Advanced Materials Testing Plan for the Space Suit Portable Life Support System
The Space Suit Portable Life Support System (PLSS) has a tight mass requirement to meet while also meeting other requirements for supporting a crewmember in space, on the Moon, or on Mars. To meet these requirements, atypical materials must be considered to close the mass budget allocations. However, many of these materials and processes are relatively new and untested. Therefore, initial analysis and testing of some new and advanced processes have been conducted following a roadmap presented last year. This material testing has focused primarily on thermoplastics, both additively manufactured and machined, to assess plating and fastening operations that will be required. These processes will provide additional strength and shielding capability typically only achieved with metallics. This testing has also helped to define a forward plan to certify these materials and processes for critical spaceflight applications. This report will review testing plated thermoplastics both for strength and thermal properties. It will also review fastener and fastening options and look at insert and fastener testing. It will also review state-of-the-art methods being considered elsewhere and some additional testing being conducted. Using the testing results researched here, there will be recommendations on applications for each of these types of methods going forward.
Ryan Ogilvie↗
Polymer Composite Material Screening for a Cryotank Application
Composite cryotanks will play a key role in enabling the next generation of efficient aircraft. Carbon fiber reinforced polymer (CFRP) composites have the benefits of reduced weight and potentially higher structural strength compared to traditional metallic fuel tanks. A material screening study was conducted to inform material selection for liquid hydrogen (LH2) fuel storage. Three composite materials were considered because of their aerospace grade toughness, strength, and existing data to compare against. These materials were a thermoplastic low-melt polyaryletherketone (LM-PAEK)/carbon fiber (CF), thermoset/CF, and hybrid thermoset/thermoplastic polyurethane (TPU) veil/CF composite. Mechanical screening tests included tension, compression, in-plane shear (IPS), and tensile-tensile fatigue (TTF). Each material was tested at both a baseline (no liquid nitrogen/LN2 cycling) and 100 LN2-cycled conditions to determine the knockdown factor, if any, of each material when exposed to environmental loading effects in a cryotank. Results show minimal effects of the LN2-cycling compared against baseline values. The three materials behaved similarly in tension; however, the thermoplastic/CF had the highest IPS toughness. The hybrid thermoset/TPU/CF composite had the lowest IPS strength, compressive strength, and toughness. LN2-cycling had minimal effects on tensile-tensile fatigue performance of the thermoplastic/CF material. Mechanical data was captured to guide material down selection for future commercially viable hydrogen aircraft design.
Composites↗
Evaluating Fracture Behavior of Bioinspired Alumina-YSZ Composites through Static and Dynamic Mechanical Testing
Ceramic materials are known for their high hardness and strength but are limited by low toughness and sudden failure. Inspired by the microstructure of dental enamel, which features undulating rods that promote crack deflection and energy absorption, architected specimens were designed and manufactured. A bespoke ball-on-ring (BoR) testing apparatus measured the static biaxial rupture strength of these bioinspired materials. Additionally, impact testing with spherical steel projectiles assessed their behavior under dynamic conditions. Monolithic alumina specimens were compared to architected alumina reinforced with yttria-stabilized zirconia (YSZ) rods produced via direct ink write 3D printing. BoR tests revealed that monolithic alumina had a Weibull modulus of 10.53 and a characteristic strength of 372.3 MPa, while the composite specimens showed a Weibull modulus of 5.46 and a characteristic strength of 213.3 MPa. Although the composite failed at lower stresses and projectile velocities, it exhibited notable crack deflection and fracture resistance, with cracks being effectively interrupted by the rod inclusions. The composite specimens also resulted in fewer and larger fragments upon impact. Finite element simulations confirmed the effectiveness of the rod structures in enhancing fracture resistance.
Bioinspired materials↗