NASA NTRS2001

Microstructure, Mechanical Properties, Hot-Die Forming, and Joining of 47XD Gamma TiAl Rolled Sheets

The microstructure and mechanical properties, along with the hot-die forming and joining of Ti-47Al-2Nb-2Mn-0.8 vol% TiB, sheets (known as 47XD), produced by a low-cost rolling process, were evaluated. A near-gamma microstructure was obtained in the as-rolled condition. The microstructures of heat-treated sheets ranged from a recrystallized equiaxed near-gamma microstructure at 1,200 to 1,310 C, to a duplex microstructure at 1,350 C, to a fully lamellar microstructure at 1,376 C. Tensile behavior was determined for unidirectionally rolled and cross-rolled sheets for room temperature (RT) to 816 C. Yield stress decreased gradually with increasing deformation temperature up to 704 C; above 704 C, it declined rapidly. Ultimate tensile strength exhibited a gradual decrease up to 537 C before peaking at 704 C, followed by a rapid decline at 816 C. The modulus showed a gradual decrease with temperature, reaching approximately 72% of the RT value at 816 C. Strain to failure increased slowly from RT to 537 C; between 537 C and 704 C it exhibited a phenomenal increase, suggesting that the ductile-brittle transition temperature was below 704 C. Fracture mode changed from transgranular fracture at low temperature, to a mixture of transgranular and intergranular fracture at intermediate temperature, to ductile fracture at 816 C, coupled with dynamic recrystallization at large strains. Creep rupture response was evaluated between 649 and 816 C over the stress range of 69 to 276 MPa. Deformation parameters for steady-state creep rate and time-to-rupture were similar: activation energies of approximately 350 kJ/mol and stress exponents of approximately 4.5. Hot-die forming of sheets into corrugations was done at elevated temperatures in vacuum. The process parameters to join sheets by diffusion bonding and brazing with TiCuNi 70 filler alloy were optimized for test coupons and successfully used to fabricate large truss-core and honeycomb structures. Nondestructive evaluation methods, e.g., ultrasonic C-scans and thermography along with metallography, were used to characterize bond quality. Microstructural evaluation during heat treatment, identification of phases at the braze/matrix interface, determination of shear strengths of brazed joints, and deformation mechanisms during tensile and creep processes will be discussed.

Das, G.↗
NASA NTRS1989

Improving the low temperature ductility of NiAl

As part of a study aimed at developing a ductile NiAl-based alloy, ingots of Ni-Fe-Al alloys were cast and hot extruded to rods. The purpose of the iron additions was two-fold viz; to produce a change in the slip vector from 001 to 111 line and, in one alloy, to add a L1(2)-structured ductile second phase. Extruded Ni-20Al-30Fe was two-phase, containing a pro-eutectic B2 phase in a fine lamellar structure of B2+L1(2) phases. Room temperature tensile testing of both single extruded and double extruded alloys resulted in 8-percent and 22-percent plastic elongation and yield stresses of 850 and 760 MPa, respectively. Fracture in both cases occurred by ductile tearing of the eutectic and transgranular cleavage of the proeutectic phase at 1350 MPa. The ductility in double extruded condition is higher than that reported earlier in rapidly solidified wires by Inoue et al. (1984). By comparison, extruded single-phase B2-structured Ni-30Al-20Fe exhibited a fracture strength of 780 MPa, no plasticity, and a mixture of intergranular fracture and transgranular cleavage. This is contrast to earlier work by Inoue et al. where a yield stress of 400 MPa, 5 percent plastic strain, and a mixture of dimple and intergranular fracture was reported.

Guha, Sumit↗
NASA NTRS1990

Elevated temperature crack growth in aluminum alloys: Tensile deformation of 2618 and FVS0812 aluminum alloys

Understanding the damage tolerance of aluminum alloys at elevated temperatures is essential for safe applications of advanced materials. The objective of this project is to investigate the time dependent subcritical cracking behavior of powder metallurgy FVS0812 and ingot metallurgy 2618 aluminum alloys at elevated temperatures. The fracture mechanics approach was applied. Sidegrooved compact tension specimens were tested at 175, 250, and 316 C under constant load. Subcritical crack growth occurred in each alloy at applied stress intensity levels (K) of between about 14 and 25 MPa/m, well below K (sub IC). Measured load, crack opening displacement and displacement rate, and crack length and growth rate (da/dt) were analyzed with several continuum fracture parameters including, the C-integral, C (sub t), and K. Elevated temperature growth rate data suggest that K is a controlling parameter during time dependent cracking. For FVS0812, da/dt is highest at 175 C when rates are expressed as a function of K. While crack growth rate is not controlled by C (sub t) at 175 C, da/dt appears to better correlate with C (sub t) at higher temperatures. Creep brittle cracking at intermediate temperatures, and perhaps related to strain aging, is augmented by time dependent transient creep plasticity at higher temperatures. The C (sub t) analysis is, however, complicated by the necessity to measure small differences in the elastic crack growth and creep contributions to the crack opening displacement rate. A microstructural study indicates that 2618 and FVS0812 are likely to be creep brittle materials, consistent with the results obtained from the fracture mechanics study. Time dependent crack growth of 2618 at 175 C is characterized by mixed transgranular and intergranular fracture. Delamination along the ribbon powder particle boundaries occurs in FVS0812 at all temperatures. The fracture mode of FVS0812 changes with temperature. At 175 C, it is characterized as dimpled rupture, and at 316 C as mixed matrix superplastic rupture and matrix-dipersoid debonding.

Leng, Yang↗
NASA NTRS1978

Fractographic evaluation of creep effects on strain-controlled fatigue-cracking of AISI 304LC and 316 stainless steel

Analysis of high temperature low cycle fatigue of AISI 304LC and 316 stainless steels by the method of strainrange partitioning results in four separate strainrange versus life relationships, depending upon the way in which creep-strain and plastic strain are combined within a cycle. Fractography is used in this investigation of the creep-fatigue interaction associated with these cycles. The PP and PC-cycle fractures were transgranular. The PC-cycle resulted in fewer cycles of initiation and shorter total cyclic life for the same applied inelastic strainrange. The CC-cycle had mixed transgranular and intergranular fracture, fewer cycles of initiation and shorter cycle life than PP or PC. The CP-cycle had fully integranular cracking, and failed in fewer cycles than were required for cracks to initate for PP,PC, and CC.

Oldrieve, R. E.↗
NASA NTRS1987

The microstructure and tensile properties of extruded melt-spun ribbons of iron-rich B2 FeAl

The microstructure of extruded rods of iron-rich FeAl(B2-structure), as characterized by TEM, SEM, optical microscopy and x-ray diffractometry, consisted of elongated grains with a 111-line fibre texture containing a high dislocation density. Numerous oxide particles were found, mostly in lines which reflected the matrix flow during extrusion. In addition, some large inclusions were present. Tensile testing of annealed, relatively dislocation-free specimens as a function of increasing temperature found increasing ductility up to 900K, above which a ductility drop occurred accompanied by a change in fracture mode, from transgranular cleavage to intergranular fracture. The yield strength, which was independent of temperature up to 800K (at about 500MPa), also decreased rapidly as diffusion became more important. The predominant slip vector changed from 111-line to 100-line around 700K.

Baker, I.↗
NASA NTRS1990

A study of hydrogen environment effects on microstructure property behavior of NASA-23 alloy and related alloy systems

This work is part of the overall advanced main combustion chamber (AMCC) casting characterization program of the Materials and Processes Laboratory of the Marshall Space Flight Center. The influence of hydrogen on the tensile properties and ductility behavior of NASA-23 alloy were analyzed. NASA-23 and other referenced alloys in cast and hipped conditions were solution treated and aged under selected conditions and characterized using optical metallography, scanning electron microscopy, and electron microprobe analysis techniques. The yield strength of NASA-23 is not affected much by hydrogen under tensile tests carried at 5000 psig conditions; however, the ultimate strength and ductility properties are degraded. This implies that the physical mechanisms operating would be related to the plastic deformation process. The fracture surfaces characteristics of NASA-23 specimens tensile tested in hydrogen, helium, and air were also analyzed. These revealed surface cracks around specimen periphery with the fracture surface showing a combination of intergranular and transgranular modes of fracture. It is seen that the specimens charged in hydrogen seem to favor a more brittle fracture mode in comparison to air and helium charged specimens. The AMCC casting characterization program is to be analyzed for their hydrogen behavior. As a result of this program, the basic microstructural factors and fracture characteristics in some cases were analyzed.

Diwan, Ravinder M.↗
NASA NTRS1985

Impact wear of iron rich superalloys

The impact-sliding wear resistance of chill cast and aligned eutectic Fe-base superalloys against M42 and 17-4 PH steel counterface materials is examined. The aligned material tests were run with carbide fibers perpendicular to the counterface contact surface and the characterization focused on fracture processes as observed in the subsurface microstructure of the worn materials. Metallographic analyses were performed on specimens exposed to various numbers of repetitive impact load cycles, and for comparison, two other aligned composites were tested with the same fiber orientation under identical test conditions against hardened M42 tool steel. A strong improvement was found in wear resistance of an aligned eutectic structure as compared to the corresponding randomized chill cast structure. Experiments with the softer 17-4 counterface were characterized by transfer onto the Fe-base superalloy, and the cracks formed were oriented transverse to the relative sliding direction and occurred in a periodic fashion. Observations in subsurface regions of the worn materials indicated crack intergranularity with an occasional transgranular fracture of the M7C3 carbide phase.

Wayne, S. F.↗
NASA NTRS1986

Effect of boron on tensile properties of B2 BeAl

Small additions of boron were shown to improve the room temperature ductility of the intermetallic compound Ni3Al. Boron is believed to segregate to the gain boundaries and strengthen them, allowing the inheret ductility of the grains to be achieved. The present study was undertaken to see if boron has a similar effect on the low temperature tensile properties of the equiatomic intermetallic compound FeAl. A binary alloy without boron is compared with an alloy containing 0.78 at % B (0.2 wt %) B, by tensile testing over the temperature range of 300 K to 640 K. Both alloys were processed by powder metallurgy. Results showed that 0.78 at % B addition to FeAl does indeed change the room temperature fracture mode from intergranular to transgranular, suggesting a strengthening of grain boundaries. The alloy containing boron is, however, still brittle at room temperature. A slight decrease in the ductile to brittle transition temperature is, nevertheless, observed. In addition a significant increase in strength of the alloy is observed with boron addition.

Crimp, M.↗
NASA NTRS1986

Tensile behavior of Fe-40Al alloys with B and Zr additions

Both Fe-40Al and Fe-40Al-0.1Zr with and without B were produced by the hot extrusion of powdered metal. Tensile properties were determined from room temperature to 1100 K in air. All of the materials possessed some ductility at room temperature, and addition of B caused an increase in ductility and a change in fracture mode from intergranular to transgranular cleavage. At high temperatures, failure was caused primarily by the formation of grain boundary cavities in all of the alloys. The effect of Zr addition was unclear because of the complexity of the various microstructures. Comparison of air and vacuum testing at high temperatures revealed that an apparent oxidation assisted mechanism reduced high temperature ductility in these alloys, especially at 900 K.

Gaydosh, D. J.↗
NASA NTRS1987

Ductility and fracture in B2 FeAl alloys

The mechanical behavior of B2FeAl alloys was studied. Stoichiometric Fe-50Al exhibits totally brittle behavior while iron-rich Fe-40Al yields and displays about 3% total strain. This change in behavior results from large decreases in the yield strength with iron-rich deviations from stoichiometry while the fracture stress remains essentially constant. Single crystal studies show that these yield strength decreases are directly related to decreases in the critical resolved shear stress for a group of zone axes /111/ set of (110) planes slip. This behavior is rationalized in terms of the decrease in antiphase boundary energy with decreasing aluminum content. The addition of boron results in improvements in the mechanical behavior of alloys on the iron-rich side of stoichiometry. These improvements are increased brittle fracture stresses of near-stoichiometric alloys, and enhanced ductility of up to 6% in Fe-40Al. These effects were attributed to increased grain boundary adhesion as reflected by changes in fracture mode from intergranular to transgranular failure. The increases in yield strength, which are observed in both polycrystals and single crystals, result from the quenching in of large numbers of thermal vacancies. Hall-Petch plots show that the cooling rate effects are a direct result of changes in the Hall-Petch intercept/lattice resistance flow.

Crimp, Martin A.↗
NASA NTRS1989

Microstructure and tensile properties of Fe-40 at. pct Al alloys with C, Zr, Hf, and B additions

The influence of small additions of C, Zr, and Hf, alone or in combination with B, on the microstructure and tensile behavior of substoichiometric FeAl was investigated. Tensile properties were determined from 300 to 1100 K on powder which was consolidated by hot extrusion. All materials possessed some ductility at room temperature, although ternary additions generally reduced ductility compared to the binary alloy. Adding B to the C- and Zr-containing alloys changed the fracture mode from intergranular to transgranular and restored the ductility to approximately 5 percent elongation. Additions of Zr and Hf increased strength up to about 900 K. Fe6Al6Zr and Fe6Al6Hf precipitates, both with identical body-centered tetragonal structures, were identified as the principal second phase in these alloys. Strength decreased steadily as temperature increased above 700 K, as diffusion-assisted mechanisms became operative. Although all alloys had similar strengths at 1100 K, Hf additions significantly improved high-temperature ductility by suppressing cavitation.

Gaydosh, D. J.↗
NASA NTRS1989

Cryogenic mechanical properties of low density superplastically formable Al-Li alloys

The aerospace industry is considering the use of low density, superplastically formable (SPF) materials, such as Al-Li alloys in cryogenic tankage. SPF modifications of alloys 8090, 2090, and 2090+In were tested for strength and Kahn tear toughness. The results were compared to those of similar tests of 2219-T87, an alloy currently used in cryogenic tankage, and 2090-T81, a recently studied Al-Li alloy with exceptional cryogenic properties (1-9). With decreasing temperature, all materials showed an increase in strength, while most materials showed an increase in elongation and decrease in Kahn toughness. The indium addition to 2090 increased alloy strength, but did not improve the strength-toughness combination. The fracture mode was predominantly intergranular along small, recrystallized grains, with some transgranular fracture, some ductile rupture, and some delamination on large, unrecrystallized grains.

Verzasconi, S. L.↗
NASA NTRS1981

The fracture morphology of nickel-base superalloys tested in fatigue and creep-fatigue at 650 C

The fracture surfaces of compact tension specimens from seven nickel-base superalloys fatigue tested at 650 C were studied by scanning electron microscopy and optical metallography to determine the nature and morphology of the crack surface in the region of stable growth. Crack propagation testing was performed as part of an earlier study at 650 C in air using a 0.33 Hz fatigue cycle and a creep-fatigue cycle incorporating a 900 second dwell at maximum load. In fatigue, alloys with a grain size greater than 20 micrometers, HIP Astroloy, Waspaloy, and MERL 76, exhibited transgranular fracture. MERL 76 also displayed numerous fracture sites which were associated with boundaries of prior powder particles. The two high strength, fine grain alloys, IN 100 and NASA IIB-7, exhibited intergranular fracture. Rene 95 and HIP plus forged Astroloy displayed a mixed failure mode that was transgranular in the coarse grains and intergranular in the fine grains. Under creep-fatigue conditions, fracture was found to be predominantly intergranular in all seven alloys.

Gayda, J.↗
NASA NTRS1992

The effect of strain rate and temperature on the tensile properties of NiAl

Tensile testing of cast and extruded binary NiAl was performed from 300 to 900 K at strain rates of 0.00014 to 0.14/s. The brittle-to-ductile transition temperature (BDTT) was dependent on strain rate, with a three-order-of-magnitude increase in strain rate resulting in approximately a 200-K increase in transition temperature. Regardless of strain rate, at temperatures just above the BDTT the fracture strength increased significantly and the fracture morphology changed from mostly intergranular to predominantly transgranular. It was also determined that the mechanism responsible for the brittle-to-ductile transition in NiAl had an apparent activation energy of approximately 118 kJ/mol. These results support the argument that the mechanism for the brittle-to-ductile transition in NiAl is associated with the onset of thermally activated deformation process. This process is probably dislocation climb controlled by short circuit diffusion.

Noebe, R. D.↗
NASA NTRS1993

Low cycle fatigue behavior of polycrystalline NiAl at 300 and 1000 K

The low cycle fatigue behavior of polycrystalline NiAl was determined at 300 and 1000 K - temperatures below and above the brittle- to-ductile transition temperature (BDTT). Fully reversed, plastic strain-controlled fatigue tests were conducted on two differently fabricated alloy samples: hot isostatically pressed (HIP'ed) prealloyed powder and hot extruded castings. HIP'ed powder (HP) samples were tested only at 1000 K, whereas the more ductile cast-and-extruded (C+E) NiAl samples were tested at both 1000 and 300 K. Plastic strain ranges of 0.06 to 0.2 percent were used. The C+E NiAl cyclically hardened until fracture, reaching stress levels approximately 60 percent greater than the ultimate tensile strength of the alloy. Compared on a strain basis, NiAl had a much longer fatigue life than other B2 ordered compounds in which fracture initiated at processing-related defects. These defects controlled fatigue life at 300 K, with fracture occurring rapidly once a critical stress level was reached. At 1000 K, above the BDTT, both the C+E and HP samples cyclically softened during most of the fatigue tests in air and were insensitive to processing defects. The processing method did not have a major effect on fatigue life; the lives of the HP samples were about a factor of three shorter than the C+E NiAl, but this was attributed to the lower stress response of the C+E material. The C+E NiAl underwent dynamic grain growth, whereas the HP material maintained a constant grain size during testing. In both materials, fatigue life was controlled by intergranular cavitation and creep processes, which led to fatigue crack growth that was primarily intergranular in nature. Final fracture by overload was transgranular in nature. Also, HP samples tested in vacuum had a life three times longer than their counterparts tested in air and, in contrast to those tested in air, hardened continuously over half of the sample life, thereby indicating an environmentally assisted fatigue damage mechanism. The C+E samples were tested only in air. At 1000 K, NiAl exhibited a superior fatigue life when compared to most superalloys on a plastic strain basis, but was inferior to most superalloys on a stress basis.

Lerch, Bradley A.↗
NASA NTRS1986

The effect of diffusive hydrogen segregation on fracture of polycrystalline nickel

Hydrogen embrittlement of polycrystalline nickel was studied under conditions which allowed the diffusion and segregation of hydrogen to grain boundaries to be controlled. It was shown that even at high solute concentrations of hydrogen, the fracture mode was ductile shear rupture, if transport of hydrogen to the grain boundaries was not allowed. As the amount of hydrogen segregation to the grain boundaries was increased, the fracture mode became increasingly intergranular. Analysis of the temperature dependence of this transition from ductile rupture to transgranular fracture yields a hydrogen segregation enthalpy of 11.6 kJ/mol. The transition in the fracture mode was also observed at a constant aging temperature by increasing the solute hydrogen concentration. The kinetics of this fracture transition suggest that the hydrogen segregation layer extends about 35 nm from the grain boundary. It is suggested that the fracture mechanism is a softening of the material in this segregation region due to the high hydrogen concentration.

Lassila, D. H.↗
NASA NTRS1992

Correlation of deformation mechanisms with the tensile and compressive behavior of NiAl and NiAl(Zr) intermetallic alloys

To identify the mechanisms controlling strength and ductility in powder-extruded NiAl and NiAl + 0.05 at. pct Zr, tensile and compressive testing was performed from 300 to 1300 K for several grain sizes. Grain size refinement significantly increased yield stress in both alloys and, in some cases, slightly lowered the ductile-to-brittle transition temperature (DBTT), although no room-temperature tensile ductility was observed even in the finest grain size specimens. The small Zr addition increased the DBTT and changed the low-temperature fracture mode from intergranular in NiAl to a combination of intergranular and transgranular in the Zr-doped alloy. Scanning electron microscopy of compression specimens deformed at room temperature revealed the presence of grain-boundary cracks in both alloys. These cracks were due to the incompatibility of strain in the polycrystalline material, owing to the lack of five independent slip systems. The tendency to form grain-boundary cracks, in addition to the low fracture stress of these alloys, contributed to the lack of tensile ductility at low temperatures.

Bowman, R. R.↗
NASA NTRS1961

Effect of Strain Rate on Mechanical Properties of Wrought Sintered Tungsten at Temperatures above 2500 F

Specimens of wrought sintered commercially pure tungsten were made from 1/8-inch swaged rods. All the specimens were recrystallized at 4050 F for 1 hour prior to testing at temperatures from 2500 to 4000 F at various strain rates from 0.002 to 20 inches per inch per minute. Results showed that, at a constant temperature, increasing the strain rate increased the ultimate tensile strength significantly. The effects of both strain rate and temperature on the ultimate tensile strength of tungsten may be correlated by the linear parameter method of Manson and Haferd and may be used to predict the ultimate tensile strength at higher temperatures, 4500 and 5000 F. As previously reported, ductility, as measured by reduction of area in a tensile test, decreases with increasing temperature above about 3000 F. Increasing the strain rate at temperatures above 3000 F increases the ductility. Fractures are generally transgranular at the higher strain rates and intergranular at the lower strain rates.

Sikora, Paul F.↗