Characterization of Engineered Pinholes in Dielectric Stacks of High-Performance Poly-Silicon Passivating Contacts
Passivating contact structures are expected to be implemented in > 50 % of industrially manufactured silicon photovoltaics produced over the next decade. One type of passivating contact utilizes a c-Si/dielectric/doped poly-Si layer stack. In cases where the dielectric layer/s are thick enough to impede tunneling of charge carriers, it was shown that disruptions (pinholes) in the dielectric are required to facilitate transport.[1] Pinholes in SiOx layers have typically been formed via high temperature annealing that allows localized breakup of this layer. This approach has drawbacks; 1) high temperature annealing increases cost and 2) pinhole formation is sensitive to both the SiOx thickness and wafer surface morphology making control of density and dimensions difficult. Recently, an alternative method of pinhole formation relying on metal assisted chemical etching (MACE) was shown to allow control over pinhole areal densities.[2] Such control is critical as both the density and dimensions of the pinholes determine saturation current density and contact resistivity. The contacts formed with the MACE process are known as polysilicon on locally etched oxide or PLEO and also result in low saturation current densities and low contact resistivity due to SiOx passivation and engineered pinhole enabled charge carrier transport, respectively. Photovoltaic devices with efficiencies greater than 20 % have recently been produced with these contacts, demonstrating the viability of contacts with engineered pinholes. Experimentally, preferential local collection of excess charge carriers has been observed and definitively connected to thermally induced pinholes in thick SiOx layers within c-Si/SiOx/poly-Si contact structures.[3] Recent work has shown that enhanced local collection of excess carriers can result from enhanced diffusion of dopants through pinholes in SiOx layers.[4] This study was restricted to simulation and characterization of poly-Si with the same dopant type as the c-Si substrates. In this work we focus our analysis on boron doped poly-Si with different stacks of dielectric layers (PLEO and PLENO where the N refers to a SiNy layer on top of the SiOx) on n-type crystalline silicon. This provides insight into how engineered pinholes affect charge collection across the p-n junction. Like previous observations of locally enhanced carrier transport through thermally induced pinholes, the EBIC images in Figure 1 shows that engineered pinholes in PLENO (1a) and PLEO (1b) also exhibit locally enhanced carrier transport at pinhole locations (bright spots in the images). We will also present detailed correlative nanoscale structural and chemical analysis using TEM imaging and EELS analysis with sample preparation guided by EBIC imaging. This allows us to connect the density and dimensions of engineered pinholes with charge carrier transport and measured photovoltaic device parameters. Our findings will accelerate the adoption of PLEO and PLENO contacts in industrially manufactured photovoltaic devices.
Spectroscopic Investigation of Shallow Hole Traps in Ga- and B-doped Czochralski Silicon: Insight into Light-Induced Degradation
We report the minority carrier lifetime in B-doped Czochralski (Cz) Si declines upon carrier injection due to light-induced degradation (LID), which is attributed to the formation of a recombination-active boron-oxygen complex. Ga-doped Cz Si does not undergo LID. Previously, we showed that B-doped Cz Si undergoes a transition from paramagnetic to diamagnetic due to LID. Herein, we show that Ga-doped Cz Si remains paramagnetic upon carrier injection. This suggests that either the shallow hole traps that are formed in B-doped Cz Si are absent in Ga-doped Cz Si, or the negative-U centers in Ga-doped Cz Si do not transform into a recombination-active configuration, because the shallow acceptor trap state is shallower than the Ga acceptor level in the forbidden gap. In contrast to B-doped Cz Si, the defect signatures in Ga-doped Cz Si do not change upon light exposure, as detected by both electron paramagnetic resonance and deep-level transient spectroscopy.
Electrical Analysis of Pulsed Laser Annealed Poly-Si:Ga/SiOx Passivating Contacts
High-efficiency single crystalline silicon (c-Si) solar cells require precise control of dopant diffusion profiles and highly active doping concentrations through thermal annealing. Conventional furnace annealing has been successfully employed for dopant diffusion in aluminum back-surface field (Al-BSF), passivated emitter and rear contact (PERC), and Topcon cells. However, furnace annealing limits some next-generation polycrystalline silicon (poly-Si) on SiOx passivating contacts. This limitation largely affects p-type passivating contacts by not being able to: 1) control the dopant diffusion accurately to prevent B segregation at the SiOx and c-Si interface; and 2) provide highly activated doping concentrations for low contact resistivity. In this contribution, we use a nanosecond excimer laser to examine the passivation quality and electrical performance of both B- and Ga-doped poly-Si/SiOx passivating contacts. The core of this method is to take advantage of the nonequilibrium nature of the anneal through rapid melting and recrystallizing the poly-Si in a short timescale and to achieve doping concentrations above the solid solubility limit. Simulations were performed on polished surfaces to visualize the doping diffusion profiles under different laser conditions, and secondary ion mass spectrometry (SIMS) was used to verify the experimental diffusion profiles post pulsed laser melting (PLM). The results show the dopant diffusion profiles can be tuned precisely through PLM. The electrical analysis using VdP-Hall measurements reveals that the active doping concentration reached 10^21 cm-3 for B and ~2×10^21 cm-3 for Ga in poly-Si, far exceeding their solid solubility limit in Si, with a nearly 100% dopant activation achieved for B, and 20% for Ga. This highly activated dopant profile results in a low contact resistivity of <15 mO·cm^2 for B-doped contacts and <40 mO·cm^2 for Ga-doped contacts. We demonstrate that the passivation quality of the laser annealed contacts shows a linear dependency with the laser energy density and the number of pulses. PLM was also performed on random pyramid textured samples, and we found that preferential melting exists for the tips of pyramids, which can be pursued further for selective pinhole opening. Additionally, we perform thermal stability tests of these hyperdoped passivating contacts and show that under certain laser conditions, the B-doped samples exhibit good thermal stability with near full activation for temperatures up to 800°C. Lastly, we transfer this technique to a larger area by overlapping laser spots and show uniform passivation quality and electrical performance. We are currently implementing this PLM annealed p-type passivating contacts into double-side back-junction poly-Si/SiOx passivating contact devices. Our results show that PLM can not only enable the next generation of high-efficiency c-Si photovoltaics technology but can also benefit the c-Si integrated circuit industry through hyperdoping other semiconductors with atoms that may otherwise have a low solubility.
Nafion Passivation of c-Si Surface and Edge for Electron Paramagnetic Resonance
Effective surface passivation of crystalline silicon (c-Si) surface by reducing the carrier recombination rate has led to modern c-Si solar cells with efficiencies > 25% in both laboratory and industrial settings. Typical mainstream surface passivation techniques include high-temperature silicon oxide (SiOx), amorphous silicon (a-Si:H), hydrogen-rich silicon nitride (SiNx), and aluminum oxide (Al2O3) [1]. They have demonstrated excellent surface recombination velocity of < 1 cm/s owing to both chemical passivation (via the hydrogen saturation of Si dangling bonds at the c-Si surface), and field-effect passivation (via the band bending from the fixed charge of the dielectric layers). Recently, several groups have studied solution-based organic materials for c-Si passivation, including bis(trifluoromethane)sulfonimide (TFSI), polystyrenesulfonate, and Nafion [2, 3] via spin or dip coating. All films were processed at ambient room temperature, and a high lifetime of 12 ms, as well as a low saturation current density (J0) of 16 fA/cm2, have been demonstrated using Nafion passivation [2]. However, despite the air instability, Nafion has several advantages when introduced to PV applications: (a) Wafer quality can be measured at high throughput after several process stages. (b) It is compatible with PL mapping, compared to HF liquid passivation which cannot be performed in room ambient. (c) Nafion process is fast and poses fewer constraints on process complexity, and cleanness, compared to Al2O3 and a-Si:H passivation. (d) Nafion is the ideal room temperature passivation, which can be applied onto a small fragment of a degraded module to investigate microscopic mechanisms when studying degradation mechanisms. Edge passivation is needed for advanced characterization tests such as Electron Paramagnetic Resonance (EPR), Electrically Detected Magnetic Resonance (EDMR), Deep Level Transient Spectroscopy (DLTS), local cell current-voltage (J-V), and Suns-Voc. In such cases, the laser-damaged minicell edges will obscure the true degradation mechanisms, and Nafion can effectively passivate them without causing further degradation through elevated-temperature processes. In this contribution, we show the passivation results of Nafion on bare nCz and compare it with a Al2O3 witness. We highlight the importance of edge pre-treatment before Nafion to achieve good passivation. We show that Nafion can reach decent passivation without undergoing high-temperature processes. We also explore the temperature dependency of Nafion through photoluminescence (PL) study and demonstrate the application of Nafion under cryogenic temperature (~6 K) through EPR. Our results reveal that Nafion can reduce surface and edge Si dangling bonds at low temperatures. Thus, it can be used as an effective room temperature passivation technique for advanced characterization methods.
Room Temperature, Dip Coating Organic Passivation for c-Si Surfaces
Surface passivation of crystalline Si (c-Si) to reduce recombination rate is crucial to obtain high-efficiency c-Si solar cells. A fast passivation technique that can be performed at room temperature is needed when studying the degradation behaviors using various characterization methods to not destroy the degraded states. In this contribution, we explore Nafion via dip coating on n-type Cz wafers. We show that both the Nafion concentration and the conditions of surface and edge affect the passivation quality, and we achieve excellent passivation quality of iVoc of 716 mV, with a saturation current density (J0) of 7 fA/cm2. Additionally, electron paramagnetic resonance (EPR) shows Nafion can be used under cryogenic temperature and reveals the reduction of Si dangling bond after Nafion treatment.
Controlling Pinhole Radius and Areal Density in a-Si/SiOx Using Metal-Assisted Chemical Etching
Polysilicon on silicon oxide (poly-Si/SiOx) passivating contacts with predominant charge-carrier transport via pinholes are currently prepared via a>1000 degrees C thermal step to induce oxide break-up. Herein, we develop the precursor of a pinhole-enabled poly-Si/SiOx contact utilizing room temperature metal-assisted chemical etching (MACE) to form pinholes in the SiOx. The pinholes were created via electroless Ag nanoparticle (Ag NP) deposition followed by the MACE of intrinsic amorphous hydrogenated silicon (a-Si:H) on SiOx, creating isolated mesopores through the film stack. By varying the MACE etching solution (HF:H2O2) concentration, we were able to vary the pinhole areal density over four orders of magnitude (104-107 cm-2). We observed the Ostwald ripening of the Ag NP to enable control over the pinhole radii. Our work demonstrates proof-of-concept for a-Si:H/SiOx with mesopores across the film stack, which may serve as precursor for the development of poly-Si/SiOx passivating contacts of both polarities.
Dopant Compensation within the Intrinsic Poly-Si Isolation Region in Poly-Si/SiOx Passivated IBC Si Solar Cells
We report on the effect of dopant compensation within intrinsic poly-Si regions between p- and n-type fingers of poly-Si/SiOx passivated interdigitated back contact (IBC) solar cells using intrinsic poly-Si as the isolation region between the doped poly-Si fingers. First, we show that dopants from the doped fingers contaminate the intrinsic gap, resulting in doping of the entire intrinsic gap and overlap of the dopant tails from each finger. Next, we show that despite this doping across the gap, shunting between the doped fingers does not occur. We show that this is a result of trap-assisted compensation creating a highly resistive intrinsic region, preventing shunt. We simulate shunt resistance across the gap based on local carrier concentration and deep trap density. We show that trap defects within the poly-Si enhance compensation between the dopant tails. We experimentally confirm these predictions by scanning spreading resistance microscopy of the gap showing ~20 um domain with resistivity ~10^7 ..omega.. cm. Additionally, Kelvin probe force microscopy are compared to finite element simulations which result in the same approximate shape for potential profile, indicating diode behavior across the isolation region. These results demonstrate the powerful effect that trap defects have within the poly-Si isolation region and suggest that precision patterning is not as essential as once thought.
Non-Equilibrium Doping of Poly-Si:Ga/SiOx Passivating Contacts Solar Cells
In this contribution, we show that Ga-hyperdoped poly-Si/SiOx contacts are realized by pulsed laser annealing and post-hydrogenation. The motivation behind this work is to improve the inferior performance of boron-doped poly- Si/SiOx contacts when compared to the phosphorus-doped contacts. Here we used Ga as a novel p-type dopant to replace B, as B is known to accumulate at the interface between the oxide and the crystalline silicon and cause recombination. Due to a high diffusivity of Ga in oxide and a much higher segregation coefficient (Si:SiOx), Ga is shown to be immune to the oxide pileup phenomenon. However, Ga has a low solid solubility limit in Si (5x10^19 cm-3), which is not enough to form a low resistivity contact. To overcome this problem, we explored pulsed laser annealing via excimer laser by varying the laser energy densities and pulses. The passivation and electrical properties are studied systematically using photoluminescence (PL), secondary ion mass spectrometry (SIMS), and Van der Pauw-Hall measurements. We show an active Ga doping concentration above 1x10^20 cm^-3, which is above the solid solubility limit of Ga in Si. Good passivation quality is demonstrated with the highest implied Voc (iVoc) of 721 mV on single side polished samples. Furthermore, a low diode contact resistivity of ~22 m..omega.. cm^2 is obtained using Ti/Ag contacts, with minimal metal-to-semiconductor contact resistivity of 0.9 m..omega.. cm^2.
Hydrogen Transport from Dielectrics to poly-Si/SiOx Passivating Contacts Measured by Mass Spectrometry and Vibrational Spectroscopy
We demonstrate the relationship between Si solar cell passivation and hydrogen content of various passivating films, including hydrogenated amorphous silicon (a-Si:H), aluminum oxide (Al2O3), silicon nitride (SiNx) and combinations thereof. Through isotopic studies using quadrupole mass spectrometry (QMS), Fourier transform infrared spectroscopy (FTIR), and Raman spectroscopy, we determine how hydrogen content and stability within each type of film relates to final passivation quality of solar cell test structures. Si solar cells using polycrystalline silicon on silicon oxide (poly-Si/SiOx) passivating contacts are at the forefront of Si solar cell research and emerging as top performers within industrial production. Performance of passivating contact Si solar cells is largely determined by a parameter known as the open-circuit voltage Voc, which directly relates to material quality within the bulk of the device and at surfaces. High Voc is achieved when defects within the bulk crystalline silicon (c-Si) and at interfaces are passivated, preventing them from acting as charge carrier recombination centers. One of the most important means of passivating defects within Si solar cells is via hydrogenation, injecting the cells with large amounts of H to satisfy dangling bonds in the bulk and at interfaces. Hydrogen is especially important in deactivating a prevalent defect in industrial p-type devices which leads to decreased device performance over long-term exposure to light, called light-induced degradation (LID). Some of the most common materials used to supply H to devices are a-Si:H, Al2O3, and SiNx, which can contain very large amounts of H. Upon annealing at elevated temperatures, the hydrogen becomes mobile enough to find and disable defect sites. However, too much hydrogen can also be problematic, sometimes leading to an effect called light and elevated temperature induced degradation (LeTID). It has been shown that these films passivate the interfaces of poly-Si passivating contacts differently, leading to differing performance. Though Al2O3 is a well-defined dielectric material, SiNx can have many different values of x depending on precursor gases and deposition conditions. We observe different FTIR and Raman spectra from different SiNx over a range of x values films to determine the bonding environments within them and further correlate the relative concentrations of Si, N, and H to the stability of H within SiNx and the passivation performance of each film. Because deuterium is chemically identical to hydrogen within these systems, but gives different signals in FTIR and Raman spectroscopy as well as in QMS, isotopic substitution can be used as an excellent tool to probe the H within films. In addition to measuring the H and D bonding within films using FTIR and Raman spectroscopy, we will use such isotopic experiments to observe H and D movement out of these hydrogenating films at elevated temperatures using QMS to determine the stability of H bonding within such systems. With these films characterized based on elemental composition, we will relate such measurements to passivation quality of these films and combinations thereof on poly-Si/SiOx contact structures using quasi-steady state photoconductance decay measurements to obtain implied open-circuit voltage (iVoc) and saturation current density J0 values. Such investigations into the performance of different passivating films and film stacks will lead to greater understanding of dielectrics in semiconductor devices, further improvements in passivated contact design, and eventually, greater proliferation of renewable solar energy worldwide.
Self-Aligned Selective Area Front Contacts on Poly -Si/SiO x Passivating Contact c -Si Solar Cells
We report both polarity poly-Si/SiO x passivating contacts in a front/back device configuration may represent the next solar cell architecture after tunnel oxide passivating contacts (TOPCon) cells, but high parasitic absorption in the front poly -Si layer often limits its performance. This work explores a wet etching technique to remove the front poly -Si in the nonmetallized regions using self-aligned metal grids as an etch mask. We systematically examine various dielectric layers (SiN x ,Al 2 O 3 , and stacks thereof) to study the repassivation of the etched n + surface, and find that an SiN x /Al 2 O 3 passivation stack can effectively repassivate the etched surface, which we attribute to field-effect passivation from the positive fixed charge from the SiN x layer, and excellent chemical passivation property from Al 2 O 3 in the form of atomic H. We demonstrate a front/back poly-Si/SiO x passivating contact device, with an open-circuit voltage (V oc ) of 690 mV, short-circuit current density (J sc ) of 39.8 mA/cm 2 , fill factor of 78%, and power conversion efficiency of 21.4%. Furthermore, simulations using SunSolve and Quokka 3 show good agreement with both the optical and electrical properties of the experimental device. The power loss analysis reveals improvements in the optical loss from the back Ti adhesion and front SiN x layers would lead to a 23.5% device. Lastly, a techno-economic model compares the production cost of this improved cell with the current TOPCon cells. Our results highlight that further cost reductions in single-sided doped poly -Si layers are needed to compete with mainstream passivated emitter and rear cell, and TOPCon technologies.
Measurement of Poly-Si Film Thickness on Textured Surfaces by X-Ray Diffraction in Poly-Si/SiOx Passivating Contacts for Monocrystalline Si Solar Cells
Polycrystalline Silicon on tunneling silicon oxide (poly-Si/SiOx) passivating contacts have shown great potential for the next-generation monocrystalline Si (c-Si) industrial photovoltaic technology. However, these cells typically suffer from strong parasitic absorption in the thick front poly-Si layer, which is designed to reduce metal-induced recombination. In previous work, we demonstrated an improved short-circuit current density, Jsc, by thinning the front poly-Si film in an SF6 plasma using the front metal grids as a self-aligned mask, but the sub - 100 nm thick poly-Si film is difficult to measure on an alkaline textured surface. Conventional optical techniques such as spectroscopic ellipsometry cannot be used due to the high scattering nature of the random pyramids. At poly-Si thicknesses below 50 nm, secondary electron microscopy (SEM) has difficulty distinguishing the poly-Si from the underlying c-Si substrate. Here, we demonstrate X-ray diffraction as an effective method to quantitatively measure the front poly-Si thickness. The thickness calculated from the diffraction peak height of the Si(111) crystallographic plane agrees well with the cross-section SEM analysis and simulations using SunSolve. We show that by thinning the front poly-Si from 200 to 60 nm, Jsc increased by 2.4 mA/cm2, while maintaining the same Voc. This led to an absolute efficiency gain of 1.73%. In addition, we also discuss possible reasons for the premature loss of passivation before the removal of all poly-Si, which prevented an even higher gain in Jsc.
Effective Dielectric Passivation Scheme in Area-Selective Front/Back Poly-Si/SiOx Passivating Contact Solar Cells
Explored different dielectric passivation schemes on lifetime samples after removing poly-Si completely. Showed that SiNx/Al2O3 had the best passivation properties on SiOx/n+ c-Si in diffused surface. Applied SiNx/Al2O3 stack on poly-Si/SiOx passivating contact device and showed large improvement in Jsc, with best device efficiency of 21.8%. Future work: CV measurement of dielectric stacks to obtain Qf and Dit.
Fabrication of Poly-Si on Locally Etched SiOx as Passivating Contacts for c-Si Solar Cells
Proof-of-concept for polysilicon on locally etched oxide (PLEO) contacts. Room temperature approach (via MACE) to engineer pinholes decouples charge-carrier transport across contact from passivation scheme of choice. 19 and 17% PLEO devices fabricated on double-side textured and saw-damage etched n Cz wafers, respectively. Preliminary work on polysilicon on locally etched nitride/oxide (PLENO) contacts. 0.2 fA/cm2 achieved with p PLENO; contact displays Ohmic behavior but still very resistive due to low pinhole density.
Effects of Plasma Etching on Dopant Compensation between p- and n-Type Poly-Si Fingers in Passivated Interdigitated Back Contact Solar Cells
Efficiencies surpassing 26% have been achieved for single-junction Si solar cells based on the interdigitated back contact (IBC) architecture. However, the possibility of lateral shunting between the doped fingers has limited industrial adoption thus far. To avoid this possibility of shunt, complicated patterning techniques of the doped rear fingers have been developed, but spreading can still occur through multiple pathways during cell processing. Patterning can be simplified by using masked plasma-enhanced chemical vapor deposition (PECVD), but spreading during deposition will also lead to contamination of the isolation region between doped fingers. We significantly reduce the effect of this spreading through a short, gentle plasma etching step, which enables a trap-assisted compensation mechanism to take effect more easily than without the plasma etch. These two effects combined allow for the use of a simple patterning technique while still maintaining a highly resistive region between the doped fingers, and will reduce the complexity of IBC cell fabrication overall.
Novel Poly-Si:Ga/SiOx Passivating Contacts through Non-Equilibrium Doping
Poly-Si/SiOx passivating contacts are one of the key enablers for high-efficiency, low-cost c-Si solar cells. In recent years, record devices have reached efficiencies of 26% in the laboratory and 25% in the industry. The current cell structure utilizing a tunneling oxide passivating contact structure with a back phosphorus-doped poly- Si/SiOx passivating contact and a front boron diffused emitter suffers from large emitter recombination. Thus, replacing the front B diffused emitter with a p-type passivating contact is a route to overcome this deficiency. This gives rise to front/back poly-Si based passivating contacts. To address the low passivation performance of the B-doped poly-Si passivating contacts, we replace B with Ga as a novel p-type dopant to avoid dopant accumulation in the tunneling oxide, which is known to lead to large degradation loss in passivation quality. Here, we introduce a non-equilibrium method via pulsed laser melting to thermally melt and recrystallize the poly-Si and redistribute the dopants, achieving doping concentrations above the solid solubility limit (~4E19 cm-3). We demonstrate a good passivation quality with an iVoc of 721 mV with an active Ga doping concentration in poly-Si >1020 cm-3. Furthermore, we show a low contact resistivity of 33.2 +/- 9.3 mO cm2 using a diode model calculation. Finally, cross-section scanning spreading resistance microscopy was performed to determine the resistance profile across the non-homogeneously doped poly-Si layer.
Designing Anion-Exchange Ionomers with Oriented Nanoscale Phase Separation at a Silver Interface
We report performance of polymer electrolyte-based energy systems is significantly impacted by transport within the electrode catalyst layer, where ionomer thin films coat catalyst particles. Proton exchange ionomer thin films have been thoroughly characterized, but few studies have critically examined anion-exchange ionomer (AEI) thin films. Further, none have reported nanoscale phase separation for hydrocarbon AEIs, which is critical to mitigate transport resistances. In this work, a set of hydrocarbon-based AEIs with nanoscale phase separation are developed from tunable block copolymer systems composed of polyisoprene (PIp) and polychloromethylstyrene (PCMS). The effect of the PIp/PCMS ratio, architecture, and thickness on the thin-film morphology of the neutral block copolymer precursors on silicon and silver substrates is investigated using grazing-incidence small-angle X-ray scattering (GISAXS) and atomic force microscopy (AFM). AEIs are prepared by quaternizing with trimethylamine or methylpiperidine and their cation-dependent morphology is characterized at 60 °C and 95% RH. A perpendicularly aligned morphology is observed on silver, while no phase separation is observed on silicon, indicating that silver-polymer interfacial interactions drive phase separation. After quaternization, dipole-dipole interactions induce some disorder, but nanoscale phase separation is still maintained. GISAXS patterns are modeled using a Unified Fit approach to understand water uptake and swelling, and recommendations for AEI design are presented.
Trap-Assisted Dopant Compensation Prevents Shunting in Poly-Si Passivating Interdigitated Back Contact Silicon Solar Cells
Using a trap-assisted compensation model, we explain why polycrystalline Si (poly-Si) passivating contacts are able to achieve low leakage current between the doped fingers of interdigitated back contact (IBC) monocrystalline Si solar cells despite mixing of boron and phosphorus dopants in the isolation region. The fill factor of IBC solar cells is strongly affected by the electrical isolation region between n- and p-type fingers, as this region is critical in minimizing shunting losses. During fabrication of monocrystalline Si solar cells with poly-Si passivating contacts, the intrinsic poly-Si isolation region inevitably gets contaminated with both p- and n-type dopants. Using dopant profiles measured with time-of-flight secondary ion mass spectrometry and scanning probe measurements of the isolation region, we demonstrate that despite the dopant spreading during cell processing, a well-compensated region between the doped fingers exists that prevents shunting. The trap-assisted dopant compensation mechanism significantly widens the compensated region to tens of microns, where the residual dopant densities are below the trap density. This enables a high-resistivity region, resulting in low shunt current. Using one-dimensional (1-D) finite element diode simulations, we identify the design parameters and experimental conditions under which a sufficiently resistive region can form. Furthermore, our measurements of 2-D local resistivity and work function maps across the isolation region using scanning spreading resistance microscopy and Kelvin probe force microscopy demonstrate the existence of a highly resistive, wide compensated region and confirm our proposed compensation mechanism. For our structures, this region is ~25 µm in width within a ~150 µm wide finger isolation region with nearly 3 orders of magnitude higher resistivity than the regions dominated by a single type of dopant.