Engineering topics
Publications and source records attributed to Ahmad, Mueed.
Abstract We report an X‐ray radiation‐induced modification of the structure and gas permeation behavior of ZIF‐8 membranes. With 300 min irradiation time, CO 2 permeance decreases by only 9 %, while N 2 and CH 4 permeances reduce by 75 and 65 %, respectively, leading to 3.7‐ and 2.6‐fold enhancements in ideal selectivity for CO 2 /N 2 and CO 2 /CH 4 .
Here, we report an X-ray radiation-induced modification of the structure and gas permeation behavior of ZIF-8 membranes. With 300 min irradiation time, CO 2 permeance decreases by only 9 %, while N 2 and CH 4 permeances reduce by 75 and 65 %, respectively, leading to 3.7- and 2.6-fold enhancements in ideal selectivity for CO 2 /N 2 and CO 2 /CH 4 .
In this study, Zeolitic Imidazolate Framework-8 (ZIF-8) is a promising material for gas separation applications. It also serves as a prototype for numerous ZIFs, including amorphous ones, with a broader range of possible applications, including sensors, catalysis, and lithography. It consists of zinc coordinated with 2-methylimidazolate (2mIm) and has been synthesized with methods ranging from liquid-phase to solvent-free synthesis, which aim to control its crystal size and shape, film thickness and microstructure, and incorporation into nanocomposites. Depending on the synthesis method and post-synthesis treatments, ZIF-8 materials may deviate from the nominal defect-free ZIF-8 crystal structure due to defects like missing 2mIm, missing zinc, and physically adsorbed 2mIm trapped in the ZIF-8 pores, which may alter its performance and stability. Infra-red (IR) spectroscopy has been used to assess the presence of defects in ZIF-8 and related materials. However, conflicting interpretations by various authors persist in the literature. Here, we systematically investigate ZIF-8 vibrational spectra by combining experimental IR spectroscopy and first-principles molecular dynamics simulations, focusing on assigning peaks and elucidating the spectroscopic signals of putative defects present in ZIF-8 material. We attempt to resolve conflicting assignments from the literature and to provide a comprehensive understanding of the vibrational spectra of ZIF-8 and its defect-induced variations, aiming towards more precise quality control and design of ZIF-8-based materials for emerging applications.
Here, motivated by the drawbacks of solution phase processing, an all‐dry resist formation process is presented that utilizes amorphous zinc‐imidazolate (aZnMIm) films deposited by atomic/molecular layer deposition (ALD/MLD), patterned with electron beam lithography (EBL), and developed by novel low temperature (120 °C) gas phase etching using 1,1,1,5,5,5‐hexafluoroacetylacetone (hfacH) to achieve well‐resolved 22 nm lines with a pitch of 30 nm. The effects of electron beam irradiation on the chemical structure and hfacH etch resistance of aZnMIm films are investigated, and it is found that electron irradiation degrades the 2‐methylimidazolate ligands and transforms aZnMIm into a more dense material that is resistant to etching by hfacH and has a C:N:Zn ratio effectively identical to that of unmodified aZnMIm. These findings showcase the potential for aZnMIm films to function in a dry resist technology. Sensitivity, contrast, and critical dimensions of the patterns are determined to be 37 mC cm −2 , 0.87, and 29 nm, respectively, for aZnMIm deposited on silicon substrates and patterned at 30 keV. This work introduces a new direction for solvent‐free resist processing, offering the prospect of scalable, high‐resolution patterning techniques for advanced semiconductor fabrication processes.
Hydrodesulfurization (HDS) is a key reaction to achieve diesel production at the specified low sulfur levels and is highly affected by a competing reaction involving nitrogen removal through hydrodenitrogenation (HDN). This work evaluated kinetic parameters of simultaneous reactions of HDS of dibenzothiophene (DBT) and HDN of quinoline (Q) using CoMoP/Al 2 O 3 and NiMoP/Al 2 O 3 catalysts under operational conditions that allow a wide range of reagent conversions. Estimated parameters were evaluated using rigorous statistical 2 analysis. Good fits for the evaluated experimental data were provided by both power-law and Langmuir-Hinshelwood models. Further, turnover frequency values highlight adsorption and competition effects between nitrogen-containing compounds and sulfur-containing compounds. NiMoP catalyst showed higher hydrogenating power than CoMoP, with larger absolute value of the estimated adsorption enthalpy (-120 kJ.mol -1 for NiMoP and -75 kJ.mol -1 for CoMoP), suggesting strong adsorption of nitrogen compounds. A catalyst with more hydrogenating power is also more capable of performing both HDN and HDS reactions simultaneously.
Surface characterization is critical for understanding the processes used for preparing catalysts, sorbents, and membranes. Nonthermal plasma (NTP) is a process that achieves high reactivity at low temperatures and is used to tailor the surface properties of materials. In this work, we combine the capabilities of infrared reflection absorption spectroscopy (IRRAS) with NTP for the in situ interrogation of zeolitic imidazolate framework-8 (ZIF-8) thin films to probe modifications in the material induced by oxygen and nitrogen plasmas. The IRRAS measurements in oxygen plasma reveal etching of organic ligands with sequential removal of the methyl group and imidazole ring and with the formation of carbonyl moieties (C═O). In contrast, nitrogen plasma induces mild etching and grafting of nitrile groups (−C≡N). Scanning electron microscopy imaging shows that oxygen plasma, at prolonged times, significantly degrades the ZIF-8 film at the grain boundaries. Treatment of ZIF-8 membranes using mild plasma conditions yields a fivefold enhancement for H 2 /N 2 and CO 2 /CH 4 ideal selectivities and an eightfold enhancement for CO 2 /N 2 ideal selectivity. Additionally, the new tools described here can be used for spectroscopic in situ tracking of plasma-induced chemistry on thin films in general.
Patterning metal-organic frameworks (MOFs) at submicrometer scale is a crucial yet challenging task for their integration in miniaturized devices. Here we report an electron beam (e-beam) assisted, bottom-up approach for patterning of two MOFs, zeolitic imidazolate frameworks (ZIF), ZIF-8 and ZIF-67. A mild pretreatment of metal oxide precursors with linker vapor leads to the sensitization of the oxide surface to e-beam irradiation, effectively inhibiting subsequent conversion of the oxide to ZIFs in irradiated areas, while ZIF growth in non-irradiated areas is not affected. Well-resolved patterns with features down to the scale of 100 nm can be achieved. This developer-free, all-vapor phase technique will facilitate the incorporation of MOFs in micro- and nanofabrication processes.