Alter, W. S.

Publications and source records attributed to Alter, W. S..

8 records

NASA NTRS1992

Conditions Of Directional Solidification Affect Superalloy

Report describes experiments to determine effects of gradient of temperature and rate of solidification on microstructure and fatigue properties of nickel-based superalloy MAR-M246(Hf). Enhancement of properties extends lifespans of objects, including turbo-pump blades of Space Shuttle Main Engines. Results indicate significant improvements in fatigue properties derived through manipulation of parameters of directional solidification. Particularly MAR-M246(Hf) for turbine blades contains small, well-dispersed blocky carbide and microstructure with small distances between dendrite arms, and without eutectic phase.

Schmidt, D. D.↗

NASA NTRS1989

The effects of temperature gradient and growth rate on the morphology and fatigue properties of MAR-M246(Hf)

MAR-M246(Hf) is a nickel based superalloy used in the turbopump blades of the Space Shuttle main engines. The effects are considered of temperature gradient (G) and growth rate (R) on the microstructure and fatigue properties of this superalloy. The primary dendrite arm spacings were found to be inversely proportional to both temperature gradient and growth rate. Carbide and gamma - gamma prime morphology trends were related to G/R ratios. Weibull analysis of fatigue results shows the characteristic life to be larger by a factor of 10 for the low gradient/fast rate pairing of G and R, while the reliability (beta) was lower.

Schmidt, D. D.↗

NASA NTRS1989

Effect Of Solidification Speed On Fatigue Properties

Fast solidification increases fatigue life, but failure distribution becomes less predictable. Report describes effects of rate of solidification on nickel-based super-alloy MAR-M246(Hf) used in turbine blades. Based on experiments in which specimens directionally solidified at 5 cm/h and 30 cm/h, then tested for high cycle fatigue. Specimens also inspected by energy-dispersive x-ray (EDX) analysis and optical and electron microscopy.

Mccay, M. H.↗

NASA NTRS1986

Low-Gravity Alloy Studies on Aircraft

Controlled solidification continued through many dives. Since each dive gives 20 to 30 seconds in which gravity is 0.001 to 0.1 its normal value, and aircraft may make about ten low-gravity maneuvers in mission, technique allows substantial time to conduct a low-gravity experiment. In directional solidification, liquid/solid interface advanced slowly through rod of sample alloy. Solidification continues during several aircraft maneuvers. Known solidification rate of sample correlated with accelerometer data to find gravity value during solidification for any point in sample. Thermal gradient and solidification rate controlled independently.

Curreri, P. A.↗

NASA NTRS1985

Superalloy microstructural variations induced by gravity level during directional solidification

The Ni-base superalloy MAR-M246 (Hf) was directionally solidified during low gravity maneuvers aboard a NASA KC-135 aircraft. Gravity force variations during this process yielded a concomitant variation in microstructure and microsegregation. Secondary dendrite arm spacings are noted to be larger in the low-g portion; this, in turn, decreases the extent of interdendritic segregation. The amount of Hf in both the carbides and interdendritic eutectic increases as the gravity force diminishes. Fewer carbides are present in the low-g regions.

Johnston, M. H.↗

NASA NTRS1985

High-pressure hydrogen testing of single crystal superalloys for advanced rocket engine turbopump turbine blades

A screening program to determine the effects of high pressure hydrogen on selected candidate materials for advanced single crystal turbine blade applications is examined. The alloys chosen for the investigation are CM SX-2, CM SX-4C, Rene N-4, and PWA1480. Testing is carried out in hydrogen and helium at 34 MPa and room temperature, with both notched and unnotched single crystal specimens. Results show a significant variation in susceptibility to Hydrogen Environment Embrittlement (HEE) among the four alloys and a marked difference in fracture topography between hydrogen and helium environment specimens.

Parr, R. A.↗

NASA NTRS1984

High-pressure hydrogen testing of single crystal superalloys for advanced rocket engine turbopump turbine blades

Alter, W. S.↗

NASA NTRS1982

Investigation of surface tension phenomena using the KC-135 aircraft

The microgravity environment of the KC-135 aircraft was utilized in three experiments designed to determine the following: (1) the feasibility of measuring critical wetting temperatures; (2) the effectiveness of surface tension as a means of keeping the cushioning heat transfer liquid in the furnace during ampoule translation; and (3) whether a non-wetting fluid would separate from the ampoule wall under low gravity conditions. This trio of investigations concerning surface phenomena demonstrates the effectiveness of the KC-135 as a microgravity research environment for small-scale, hand-held experiments.

Alter, W. S.↗