DOE OSTI2021

Advancements Toward ASME Nuclear Code Case for Compact Heat Exchangers

Our research team proposes to advance the state of the ASME section III code (nuclear service) for Compact Heat Exchangers (CHX). This work will improve the technical state of CHXs and lay the foundation necessary for these heat exchangers to be certified for use in nuclear service. During the course of this work, we will advance the understanding of the performance, integrity, and lifetime of the CHXs for use in any industrial application, making their use more attractive and accessible to the industry. We will do this by developing qualification and inspection procedures that utilize Non-destructive evaluation (NDE) and advanced in-service inspection techniques, with insight from the industrial utility leader EPRI. We have enlisted colleagues at MPR Associates (MPR), an elite nuclear code consulting firm, who are experts on the ASME section III code and who, with input from members of the ASME section III committee, will direct the testing and help develop a series of documents that define the rules and regulations for use of the CHX. Colleagues at North Carolina State University (NCSU) and Oregon State University (OSU) will conduct extensive tensile, creep, and fatigue experiments on diffusion bonded samples (manufactured by US-based Vacuum Process engineering) along with modeling using the elastic perfectly plastic assumptions and comprehensive full inelastic finite element analysis (FEA). This work will allow analysis by design and confidence in the strength of different internal structures. To ensure industry acceptance and long term confidence, team members at the University of Wisconsin–Madison (UW), University of Michigan (UM), Georgia Tech (GT), and the University of Idaho (UI) will extensively test prototypic heat exchangers manufactured by US-based manufactures CompRex and Vacuum Process Engineering (VPE), a leader in the development of advanced CHX. This testing will include the use of various working fluids (salt, sodium, helium, and sCO2) to evaluate operational issues as well as structural integrity under the most severe conditions. Post-test analysis of the tested CHXs coupled with pre/in-service/post NDE (ultrasonic and radiography) led by the Electric Power Research Institute (EPRI) will be incorporated into the development of the rules and regulations for their use in nuclear service.

42 ENGINEERING↗
DOE OSTI2021

Corrosion resistive materials, systems, and methods of forming and using the materials and systems

A method to reduce corrosion rates of materials at high temperatures may include heating a mixture and applying the heated mixture to a material to be rendered thermodynamically noble. The mixture may include carbon monoxide and carbon dioxide and the material rendered thermodynamically noble may include copper or other material having similar physical properties. The copper or other similar material may be applied to a structural material and provide a surface interfacing with the mixture of carbon monoxide and carbon dioxide to prevent corrosion of the structural material. In some cases, the structural material may form a heat exchanger defining passageways for a working fluid of a power system and/or may form other passageways of the power system. The copper may be applied to the passageways as a protective coating and then made thermodynamically noble at high temperatures after interactions with the mixture of carbon monoxide and carbon dioxide.

Anderson, Mark↗
DOE OSTI2021

Evolution of Microstructure and Surface Characteristics of FeCrAl alloys when Subjected to Flow Boiling Testing

FeCrAl alloys are candidate materials for manufacturing accident-tolerant fuel (ATF) cladding intended for light water reactors to increase fuel reliability and safety during design-basis and beyond-design-basis accident scenarios. The evolution of the materials' surface characteristics, microstructure, and mechanical properties when exposed to the Critical Heat Flux (CHF) in flow boiling testing is crucial for safety analysis while providing insights into their thermal-hydraulic performance in nuclear reactors. After CHF, the surface chemistry of two FeCrAl alloys, APMT and C26M, was studied to understand their evolution at the early stage of high-temperature excursions in short time periods. The results indicated a thin layer composed of oxides and hydroxides of Al, Cr, and Fe with varying proportions at different depths in the layer, as indicated by X-ray photoelectron spectroscopy (XPS) and depth profiling. The cross-sections prepared by focused ion beam (FIB) revealed the growth of an oxide layer, in the range of 90-180 nm thick, on the alloys' surfaces. The evolution of the materials' surface chemistry also led to a noticeable post CHF excursion increase in their wettability, with a slight increase in roughness. Further, the investigation of the materials' mechanical properties indicated a modest increase in hardness by 10-15% as well as an increase in their yield strength, as evidenced by the microindentation and ring compression tests conducted before and after CHF testing. Scanning electron Microscopy (SEM) and X-ray diffraction (XRD) were used to investigate microstructural features of the materials and their changes after CHF treatment.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Final Technical Report

Explore the source record for details and available documents.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗
DOE OSTI2021

High Temperature Sodium Submersible Flowmeter Design and Analysis

This work details the design and analysis of a permanent magnet flowmeter designed to be submerged in a pool type sodium fast reactor environment. Recently developed Samarium Cobalt rare earth magnets were utilized that have demonstrated resilience to temperature and neutron flux up to 550 °C and 10 18 n/cm 2 , respectively. This paper will discuss the theory, design, calibration and uncertainty quantification of the flowmeter. The flowmeter was calibrated over a flowrate range of 11.4 - 90.9 LPM at temperatures of 220 and 400 °C, yielding an uncertainty in calibration of 2-3.6%. Here, a finite element model was developed and validated experimentally, yielding <; 3.2% error.

47 OTHER INSTRUMENTATION↗
DOE OSTI2021

Perseverance’s Scanning Habitable Environments with Raman and Luminescence for Organics and Chemicals (SHERLOC) Investigation

The Scanning Habitable Environments with Raman and Luminescence for Organics and Chemicals (SHERLOC) is a robotic arm-mounted instrument on NASA’s Perseverance rover. SHERLOC has two primary boresights. The Spectroscopy boresight generates spatially resolved chemical maps using fluorescence and Raman spectroscopy coupled to microscopic images (10.1 μm/pixel). The second boresight is a Wide Angle Topographic Sensor for Operations and eNgineering (WATSON); a copy of the Mars Science Laboratory (MSL) Mars Hand Lens Imager (MAHLI) that obtains color images from microscopic scales (~13 μm/pixel) to infinity. SHERLOC Spectroscopy focuses a 40 μs pulsed deep UV neon-copper laser (248.6 nm), to a ~100 μm spot on a target at a working distance of ~48 mm. Fluorescence emissions from organics, and Raman scattered photons from organics and minerals, are spectrally resolved with a single diffractive grating spectrograph with a spectral range of 250 to ~370 nm. Because the fluorescence and Raman regions are naturally separated with deep UV excitation (<250 nm), the Raman region ~ 800 – 4000 cm -1 (250 to 273 nm) and the fluorescence region (274 to ~370 nm) are acquired simultaneously without time gating or additional mechanisms. SHERLOC science begins by using an Autofocus Context Imager (ACI) to obtain target focus and acquire 10.1 μm/pixel greyscale images. Chemical maps of organic and mineral signatures are acquired by the orchestration of an internal scanning mirror that moves the focused laser spot across discrete points on the target surface where spectra are captured on the spectrometer detector. ACI images and chemical maps (< 100 μm/mapping pixel) will enable the first Mars in situ view of the spatial distribution and interaction between organics, minerals, and chemicals important to the assessment of potential biogenicity (containing CHNOPS). Single robotic arm placement chemical maps can cover areas up to 7x7 mm in area and, with the < 10 min acquisition time per map, larger mosaics are possible with arm movements. This microscopic view of the organic geochemistry of a target at the Perseverance field site, when combined with the other instruments, such as Mastcam-Z, PIXL, and SuperCam, will enable unprecedented analysis of geological materials for both scientific research and determination of which samples to collect and cache for Mars sample return.

46 INSTRUMENTATION RELATED TO NUCLEAR SCIENCE AND ↗
DOE OSTI2021

Mechanical and Corrosion Response of 316SS in Supercritical CO 2

The supercritical carbon dioxide (s-CO 2 ) Brayton cycle is currently being explored as a replacement for the steam Rankine cycle due to its potential for higher efficiency and lower cycle cost. 316 stainless steel is a candidate alloy for use in s-CO 2 up to roughly 600 °C, but the mechanical effects of prolonged exposure of base and welded material in s-CO 2 have not been analyzed. The potential for carburization makes this an important concern for the implementation of 316 and similar austenitic stainless steels in the s-CO 2 environment. In this study, welded and base material of two types of 316–316L and 316H–were exposed in either s-CO 2 or argon at 550 °C or 750 °C for 1000 h. 550 °C s-CO 2 exposure yielded a thin (< 1 µm) Cr oxide with occasional nodules of duplex Fe oxide and Fe–Cr spinel that were up to 5 microns thick. However, tensile results from s-CO –2 exposure matched those of 550 °C thermal aging in Ar, indicating that no mechanically detrimental carburization occurred in either 316 variant after 1000 h exposure. Conversely, 750 °C s-CO 2 exposure produced roughly 10 × the oxide thickness, with a more substantial Fe oxide (3–5 µm) on the majority of the surface and nodules of up to 40 µm thick. In comparison to aged samples, tensile testing of 750 °C CO 2 -exposed samples revealed ductility loss attributed to carburization. As a result, projections of 316L performance in s-CO 2 indicate that mechanically detrimental carburization—equal to that shown here for 750 °C, 1000 h—will likely be present after 7–14 years of service at 550 °C.

316 stainless steel↗
DOE OSTI2021

Tribology Test Bed: NiWC3b Cermet, Chloride Salts (Technical Report)

In this project, the best material and processes that we have available now are used build a pump for validation testing and to be able to provide a quotation for a pump for the Gen3 CSP Phase 3 test facility. Enough high temperature and aged material data is collected to be able to safely design a pump with a high level of confidence of good performance. Manufacturing processes for the nano-composite material including spray coating and joining methods are investigated. These processes enable application of this novel material to pump components.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Validation Salt Pump: NiWC3B Cermet, H230, Chloride Salts (Technical Report)

In this project, the best material and processes that we have available now are used build a pump for validation testing and to be able to provide a quotation for a pump for the Gen3 CSP Phase 3 test facility. Enough high temperature and aged material data is collected to be able to safely design a pump with a high level of confidence of good performance. Manufacturing processes for the nano-composite material including spray coating and joining methods are investigated. These processes enable application of this novel material to pump components.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Static Corrosion Summary: Static Corrosion Testing, Haynes 230 Recession Rate, Chloride Salts

In this project, the best material and processes that we have available now are used build a pump for validation testing and to be able to provide a quotation for a pump for the Gen3 CSP Phase 3 test facility. Enough high temperature and aged material data is collected to be able to safely design a pump with a high level of confidence of good performance. Manufacturing processes for the nano-composite material including spray coating and joining methods are investigated. These processes enable application of this novel material to pump components.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Flexible hose interconnect testing for parabolic troughs with nitrate salt

The use of molten salt as a heat transfer fluid in parabolic trough concentrated solar power plants, in lieu of oil-based heat transfer fluids, presents the possibility to increase the plant's operating temperature and corresponding Rankine cycle efficiency, improve dispatchability, and decrease costs. However, several barriers still exist to commercialization of the technology. This paper discusses meaningful progress toward overcoming two specific barriers to commercialization; 1) the lack of a reliable interconnect solution for molten salt service to connect rotating collectors with stationary header pipes and 2) the limitations of publicly available system modeling tools for a plant using molten salt as both the heat transfer fluid and energy storage medium.

14 SOLAR ENERGY↗
DOE OSTI2020

Enhanced flow boiling heat transfer on chromium coated zircaloy-4 using cold spray technique for accident tolerant fuel (ATF) materials

Flow boiling heat transfer tests were conducted to evaluate the Critical Heat Flux (CHF) and Heat Transfer Coefficient (HTC) of conventional and accident tolerant fuel (ATF) cladding materials, i.e., bare Zircaloy-4 (Zr4), and Zircaloy-4 coated with Chromium using physical vapor deposition (PVD) (Zr4-Cr-PVD) and cold spray process (Zr4-Cr-CS), respectively. The tests were performed on a single heater rod with a uniform heat flux profile, at the atmospheric pressure, inlet temperature (24 °C) and mass flow rate (750 kg/m 2 s). HTC’s were increased by 5.2% and 3.3% on Zr4-Cr-CS compared to bare Zr4 and Zr4-Cr-PVD. Improved HTCwas attributed to the increased void fraction and high roughness (Ra = 532 nm) of the Zr4-Cr-CS. In detail, the micro-cavities, which act as bubble seeds, were entirely distributed on the Zr4-Cr-CS, and these micro-cavities generated smaller and faster bubbles, thus the void fraction increased by 10.9% compared to bare Zr4. HTC is improved by these smaller and faster bubbles which can remove heat from the heater rod surface more efficiently. To identify the exact location of CHF, the surface temperature profile was measured using advanced fiber-optic sensors which have high temporal/spatial resolution (distance between point to point: ~2.5 mm, frequency ~100 Hz). CHF occurred at 80–95% along the heated length and showed an 11.6% reduction on Zr4-Cr-CS compared to bare Zr4. We hypothesize the CHF reduction was caused by the lower wettability of the Zr4-Cr-CS which reduces the liquid supply to the surface, and vigorous bubble accumulation owing to high void fraction near the outlet, which results in early formation of the vapor film. During the post-CHF quenching phase, the rougher Zr4-Cr-CS showed larger cooling rates compared to the bare Zr4 and Zr4-Cr-PVD, preventing of oxidation by chromium layer. In conclusion, we demonstrate that the high roughness on the Zr4-Cr-CS increased the number of micro-cavities on the surface, resulting in 5.2% increase in HTC and improvement in the quenching heat transfer performance whereas CHF was 11.6% reduced compared to bare Zr4. Overall statistically there is little effect in the coating with regards to CHF and slight improvement in HTC.

42 ENGINEERING↗
NASA NTRS2020

Preparing for Mars 2020 and Future Space Missions: Technology Advancements Driving Contamination Control Requirements and Cleanroom Protocols

Future space exploration missions will force contamination control requirements to become more strict to support increasingly sensitive instrumentation and search for life missions. Driving issues for these extremely clean requirements include increased instrument sensitivity, return sample science, and protecting ambitious mission science objectives. Preparing to meet these requirements mandates that contamination control provide new guidelines and more involved support for the cleanrooms during flight hardware assembly, including establishing better methods for setting cleanroom personnel limits to reduce particle fall out in cleanrooms. Limited literature exists for universal methods of determining cleanroom personnel limits, and what does exist includes mostly theory and assumptions on determining the limit. In this work, published method will be assessed against particle fall out data collected from the ISO 5 cleanrooms of the Mars 2020 Perseverance Rover assembly. Additional evaluations will assess contamination control required cleanroom protocols and the overall success of meeting strict cleanliness requirements of the Adaptive Caching Assembly (ACA) and sample tubes to safeguard future scientific endeavors.

Chen, Nicole↗
DOE OSTI2020

Mechanical and chemical properties of PVD and cold spray Cr-coatings on Zircaloy-4

In this paper, accident-tolerant fuel (ATF) cladding materials aim to improve fuel reliability and safety during accident scenarios in water-cooled reactors. These ATF cladding should also perform comparable or better than the current zirconium alloy cladding under reactor normal operating conditions. Surface-modified Zircaloy-4 was produced by depositing a protective coating of chromium by two different coating techniques, Physical Vapor Deposition (PVD) and Cold Spray (CS). The coating thickness, structure, composition, and mechanical properties of the coated Zircaloy were assessed with advanced materials characterization techniques. Results showed a strengthening effect of the Cr-coating, along with ~83% higher hardness compared to that of the Zircaloy-4 substrate. Surface topography and surface chemistry of the Cr-coated Zircaloy-4 were assessed with contact profilometry, atomic force microscopy, contact angle goniometry, and X-ray photoelectron spectroscopy. Deposited Cr-coating significantly improved surface wettability compared to the substrate Zircaloy-4. The formation of surface oxides on the coatings by prolonged exposure to ambient air showed a further increase in the hydrophobic behavior. Surface parameters and surface chemistry after flow boiling critical heat flux tests, conducted at atmospheric pressure, evidenced a slight increase in surface roughness with notable changes in wettability associated with the formation of surface oxides.

36 MATERIALS SCIENCE↗
DOE OSTI2020

An Experimental Study of Design and Performance for the Water-Based Reactor Cavity Cooling System

The document summarizes the test activity conducted at the Texas A&M University water-cooled Reactor Cavity Cooling System experimental facility. Flow and temperature characterization of the risers' panel is conducted using advanced measurement techniques. Steady-state and transient scenarios are studied, analyzed, and discussed in the report. The experimental work is complemented with modeling and simulations using system level codes.

21 SPECIFIC NUCLEAR REACTORS AND ASSOCIATED PLANTS↗