Asmussen, Robert M. (ORCID:0000000159777728)

DOE OSTI2026

Semi-Dynamic Leach Testing of Densified Silicon-based Iodine Waste Forms

Iodine waste forms (IWF) require a conceptual corrosion release model (CCRM) to provide iodine (I) release rates for performance modeling nuclear waste disposal repositories. To develop a CCRM, an understanding of the corrosion mechanisms of the IWF are required along with data from consistent test methods to parameterize the model. The present study has advanced both areas by providing and assessing the corrosion resistance of IWF types based on their processing history in minor variations of semi-dynamic leach tests. The test included a series of semi-dynamic leach tests using monolithic IWFs in deionized water (leachant). Several experiments were conducted under alternate test conditions with changes to temperature, leachant replacement, leachant pH, leachant volume, masking, and surface finish to elucidate if varying these conditions impacted IWF corrosion behavior. Tests were conducted on two classes of IWFs: (1) I-bearing silver-mordenite (AgZ) materials processed by hot isostatic pressing (HIP) at different temperatures, pressures, sizes, and times; and (2) I-bearing silver-functionalized silica aerogels (SFA) processed by either HIP or spark plasma sintering (SPS). The corrosion susceptibility of AgZ samples was influenced by HIP temperature and pressure. The SPS SFAs retained I far better than HIP SFAs. Additional findings in this study include: (1) The iodine dissolution rate decreased with decreasing temperature, (2) a common ion effect may occur and slow dissolution of the host phase if the leachant is not regularly replaced, (3) pH controls the dissolution rate, and (4) the iodine dissolution rate slows with extended test time (up to 224 days). Based on this work, these parameters should thus be represented when developing a CCRM.

corrosion↗

DOE OSTI2026

A Kinetic Model of the Long-Term Corrosion of Glass-Ceramic Materials

Multiphase waste forms show promise for increased waste loading and for the ability to dispose of contaminated solid and particulate waste through direct densification. However, achieving predictive capability for long-term durability of multiphase waste forms, and thus assessing their possible deployment, requires expanding the current, limited knowledge base. Here, we describe the development of a corrosion model of a two-phase waste form consisting of crystals of known volume fraction embedded in a glass matrix. This model accounts for the dissolution of both the crystalline and glass phases as well as the hydration of the glass phase through an ion exchange reaction. Because of the large difference in solubility between the two phases, the reactive surface of the crystalline phase is a function of the extent of dissolution of the glass phase in this model. Model parameterization was performed using corrosion data, such as from single-pass flow-through tests, for the individual phases. The parameterized corrosion model was evaluated against static dissolution test data for a glass-ceramic multiphase waste form. This evaluation demonstrated the model’s ability to reproduce the time-dependent release of key tracers of glass and crystalline phase dissolution. Hence, the development of a kinetic model provides a pathway for long-term durability predictions and thus the use of multiphase waste forms in nuclear cleanup missions.

Kerisit, Sebastien N.↗