DOE OSTI2024

Corrosion evaluation of Al-Cu-Mn-Zr cast alloys in 3.5% NaCl solution

Corrosion behavior of cast Al-Cu-Mn-Zr (ACMZ) and RR350 alloys was compared to a cast 319 alloy in 3.5 wt.% NaCl. After 168 h immersion, ACMZ and RR350 alloys suffered from preferential attack adjacent to intermetallic particles decorated at grain boundaries while the attack in 319 occurred in eutectic Al-Si dendritic boundaries. Electrochemical data allowed semiquantitative comparison of alloy resistance to corrosion initiation, and ACMZ type alloys, including RR350 and three alloys with higher Cu, were considered more resistant than 319 due to the absence of deleterious Si particles. In case of 319, such Si particles presumably drove higher micro-galvanic influence to initiate and sustain Al corrosion. With lower susceptibility to corrosion initiation, ACMZ alloys should exhibit higher or at minimum similar resistance compared to cast 319.

36 MATERIALS SCIENCE↗

DOE OSTI2024

Dual X-ray computed tomography-aided classification of melt pool boundaries and flaws in crept additively manufactured parts

In metal additive manufacturing (AM), understanding the process-structure-performance relationships requires a combination of multi-scale characterization techniques that allows for the measurement of the melt pool shape and boundary and classifying various defects and flaws in the AM parts. Such approaches can be destructive, only 2D in nature, or have a small field of view and can be complex to co-register and analyze. Here, in this work, we present a non-destructive 3D inspection technique that employs dual-energy X-ray computed tomography (XCT) along with a model-based iterative reconstruction (MBIR) and a new segmentation algorithm. The proposed approach and algorithm are not only capable of classifying and quantifying flaws such as pores, cracks, and inclusions, but they also allow for the extraction of microstructural features such as melt pool boundaries (MPB) and melt pool regions (MPR), that can help understand process-structure-performance relationships for alloys under study. As an exemplar application, we employed the method for characterization of an additively manufactured aluminum alloy crept under tensile stress at 300 °C for 1064 h. Our results demonstrate high quality segmentation and classification of various flaws and MPB and MPR, for the first time, using 3D X-ray CT inspection. The delineated MPB and MPR in the crept samples reveal the preferential growth paths of cracks that formed during creep deformation. The technique was used for successfully quantifying the characteristics (number of defects, their density, volume fraction, etc.) of the manufacturing-induced pores and creep-induced cracks, which is necessary to better understand the creep failure mechanisms of the material.

36 MATERIALS SCIENCE↗

DOE OSTI2024

Effect of microalloying additions on microstructural evolution and thermal stability in cast Al-Ni alloys

Enhancement of thermal stability in Al-Ni alloys through microalloying with slow-diffusing elements, specifically Zr, has been previously reported which is attributed to Zr segregation at the Al/Al 3 Ni interface. In this study, we explore the influence of microalloying Al-Ni alloys with Zr, Ti, V, and Fe on microstructural evolution, hardness, and electrical and thermal conductivity across a range of heat-treatment temperatures from 300 to 450 °C. The distribution of microalloying elements and precipitates after heat treatment is characterized using atom probe tomography (APT). Our investigation confirms Zr segregation to the Al/Al 3 Ni interface, while similar interfacial segregation is absent with the addition of Ti, V, and Fe. Additionally, our analysis of the Al 3 Ni microfiber morphology reveals that their coarsening and spheroidization rates are similar with and without interfacial segregation; thus, retaining the fiber reinforcement through interfacial segregation of slow diffusing elements may not be an effective strategy. Precipitation of L1 2 nanoparticles was found to be the dominant mechanism affecting enhanced hardness and electrical conductivity in Al-Ni-Zr alloys, attributed to precipitation strengthening and solute depletion, respectively. Similar precipitation was not observed for additions of Ti, V, and Fe following heat treatment. We provide a thermodynamic explanation for this limitation. Furthermore, the findings of this study suggest that an effective approach for designing Al-Ni alloys should involve prioritizing microalloying elements to maximize L1 2 precipitation and minimize solute content in the FCC-Al matrix post heat treatment, rather than focusing on Al/Al3Ni interfacial segregation.

36 MATERIALS SCIENCE↗

DOE OSTI2024

Creep deformation and cavitation in an additively manufactured Al-8.6Cu-0.4Mn-0.9Zr (wt%) alloy

Creep deformation and cavitation were investigated at 300 ºC in both tension and compression for an additively manufactured Al-8.6Cu-0.5Mn-0.9Zr (wt%) alloy in the as-fabricated state and after various aging treatments (aging at 300 °C/200 h or 350 °C/24 h and overaging at 400 °C/200 h). Creep mechanisms at 300 °C were determined by relating the measured creep response to corresponding microstructural and X-ray computed tomography observations. In compression, alloys in the as-fabricated and two aging conditions exhibited similarly high creep resistance. Overaging (400 °C/200 h) led to substantial coarsening of intragranular θ-Al2Cu precipitates and an expected drop in their Orowan strengthening contribution. In tension, minimum strain rates comparable to those in compression were obtained at any given stress; however, upon accumulation of some plastic strain in the matrix, creep cavities started to form, leading to accelerated tertiary stage creep deformation and rupture. Cavitation occurred exclusively along melt pool boundaries due to locally enhanced diffusion enabled by (i) large grain-boundary area in adjacent fine-grained zones and (ii) localization of creep strain in nearby heat-affected zones. Although cavity growth was initially diffusion-controlled, its rate was determined by matrix creep rate, consistent with constrained cavity growth mechanisms. This study reveals how microstructural complexities induced by the additive manufacturing process affect the creep and cavitation behavior of Al-Cu-Mn-Zr alloys. The underlying creep and cavitation mechanisms uncovered in this study point to pathways that improve the high-temperature properties of additively manufactured alloys.

36 MATERIALS SCIENCE↗

DOE OSTI2024

An additively manufactured near-eutectic Al-Ce-Ni-Mn-Zr alloy with high creep resistance

A new additively manufactured (AM) Al-7.5Ce-4.5Ni-0.4Mn-0.7Zr (wt.%) near-eutectic alloy is reported, which shows unprecedented creep resistance up to 400 °C (a homologous temperature of 0.72). The eutectic solidification microstructure comprises ~ 27 vol% of coarsening-resistant second phase network with an ultrafine (<100 nm) inter-phase spacing. Both Mn and Zr contribute to creep resistance of the alloy. Small amount of Mn addition promotes selection of coarsening resistant phases without compromising the alloy processability. Zr not only improves hot-tearing resistance, but further enhances the second phase coarsening resistance resulting in improved creep resistance. Neutron diffraction performed during creep deformation reveals that the underlying mechanism for creep resistance in this alloy is impedance to dislocation motion stemming from the ultrafine eutectic solidification microstructure, whereas load transfer strengthening becomes less effective as the creep temperature increases. The second phase forms a continuous network in the as-fabricated condition, which is maintained during long-term creep at 300 °C. However, this network is fragmented into fine dispersoids at higher temperatures. It is proposed that the rate-limiting deformation mechanism at 300–400 °C is (i) dislocation climb for the alloy with fragmented second phase dispersoids and (ii) Orowan looping for the alloy with a continuous second phase network. In conclusion, the present design of an AM-processable multicomponent eutectic alloy with high creep resistance can be applied to other metallic systems exhibiting eutectic reactions, with expected extreme creep resistance.

36 MATERIALS SCIENCE↗

DOE OSTI2023

3D Printed eutectic aluminum alloy has facility for site-specific properties

Additive manufacturing (AM) has the ability to print structures with site-specific properties. Existing AM approaches for site-specific properties are, however, based on complex processing-microstructure relationships in conventional alloys that were not designed for this purpose. Here, in this work, we report a straightforward approach for achieving site-specific properties that takes advantage of eutectic solidification characteristics. We demonstrate that the yield strength of a eutectic Al-Cu-Ce-Zr alloy can be tuned by varying the laser scan speed in concert with hatch spacing in laser powder bed fusion AM. A faster speed increases solidification rate resulting in finer eutectic spacing and higher strength. The hatch spacing is reduced at faster speeds to ensure overlap between melt pools which become smaller with increasing scan speed. The yield strength and its anisotropy relative to build direction are further tunable with a heat treatment. The scan speed-eutectic spacing-strength relationship is successfully applied to print a complex pattern of site-specific hardness in the alloy. The generalized principle of using AM for a eutectic alloy to create site-specific properties and anisotropy in properties is demonstrated.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Progression of creep deformation from grain boundaries to grain interior in Al-Cu-Mn-Zr alloys

Creep mechanisms are studied in θ'-Al 2 Cu-strengthened Al-Cu-Mn-Zr alloys at 300 and 350°C for (i) ACMZ, a base alloy without further alloying elements and (ii) RR350, a commercial alloy with additions of Ni and Co forming distinct grain-boundary precipitates. At high stresses, creep is dominated by dislocations bypassing θ' precipitates within grains via the Orowan mechanism, as evidenced by (i) very high stress exponent (n~20-25) and (ii) α-Al and θ' lattice strains (measured via in-situ neutron diffraction) evolving during creep in a manner consistent with load transfer from the plastically-deforming α-Al matrix to elastically-deforming θ' precipitates. At intermediate stresses, both alloys exhibit a n~3 regime, where α-Al and θ' lattice strains scale near-linearly with applied stress while remaining largely unaffected by strain accumulation, indicating that Orowan looping or dislocation pile-up around θ' is now inactive within the grains. Rather, dislocation motion occurs solely in θ'-precipitate-free zones (θ'-PFZ) where high dislocation densities are observed via TEM after creep deformation. Plastic flow at θ'-PFZ and/or localized pipe diffusion are expected to enable grain-boundary sliding (GBS), which is proposed as the rate-limiting mechanism in the n~3 regime. Ni/Co-rich precipitates at RR350 grain-boundaries, with negligible θ'-PFZ around them, share load (as determined via neutron diffraction) with the α-Al matrix more effectively than θ-Al 2 Cu precipitates at ACMZ grain-boundaries, with wide surrounding θ'-PFZ. So, high creep resistance in the n~3 GBS regime of RR350 is enabled by coarsening-resistant grain-boundary precipitates, forming without concomitant development of weak θ'-PFZ, which effectively share load with the grains.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Aluminum-cerium-manganese alloy embodiments for metal additive manufacturing

Disclosed herein are embodiments of an Al—Ce—Mn alloy for use in additive manufacturing. The disclosed alloy embodiments provide fabricated objects, such as bulk components, comprising a heterogeneous microstructure and having good mechanical properties even when exposed to conditions used during the additive manufacturing process. Methods for making and using alloy embodiments also are disclosed herein.

Allard, Lawrence F.↗

DOE OSTI2023

Additively manufactured Al-Ce-Ni-Mn alloy with improved elevated-temperature fatigue resistance

Here, the high cycle fatigue behavior of an additively manufactured (AM) Al-10.5Ce-3.1Ni-1.2Mn wt% alloy was evaluated at 350 °C. The measured fatigue strength of 50 MPa at this temperature is comparable to the most fatigue resistant wrought Al alloys (2618-T6 and 7079-T6) at 315 °C. Refinement of pore populations through advanced AM processing in the examined alloy led to oxide inclusions becoming dominant fatigue crack initiation sites. The distribution of microstructural features that determine crack initiation was measured by X-ray computed tomography and served as input to make fatigue strength model predictions with various methodologies. A Monte-Carlo based approach that was previously applied to predict the fatigue strength of cast aluminum alloys through pore size distributions yielded accurate predictions for the fatigue strength of this AM alloy. Given the tunability of defect distributions in AM alloys, the sensitivity of the Al-Ce-Ni-Mn alloy fatigue behavior to defect distributions and outstanding elevated-temperature fatigue resistance of this alloy; the results together suggest the possibility of a new generation of fatigue-resistant alloys produced by the additive manufacturing route.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Heat-resistant aluminium alloys

Scandium added to Al–Cu–Mg–Ag alloys leads to an in situ phase transformation of coherent Cu-rich nanoprecipitates at elevated temperature, with Sc atoms diffusing and occupying their interstitial sites. Notably, the transformed nanoprecipitates have enhanced thermal stability while maintaining a large volume fraction and these two microstructural features enable high tensile strength of the Al alloy with creep resistance up to 400 °C.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Load shuffling during creep deformation of an additively manufactured AlCuMnZr alloy

Here, the high-temperature deformation behavior of an additively manufactured Al-Cu-Mn-Zr alloy is evaluated in the as-fabricated and heat-treated states using traditional ex-situ and in-situ neutron diffraction creep experiments performed at 300 °C. The dominant reinforcement phase in the alloy, θ-Al 2 Cu, despite its high volume fraction of ~10%, does not provide load transfer strengthening during creep deformation. Instead, the lattice strain evolution suggests a new mechanism we term “load shuffling” wherein the initial load is transferred away from precipitate-free zones along the grain boundaries where most of the θ-Al 2 Cu particles are located to precipitate-strengthened grain interiors. Notwithstanding the lack of load transfer strengthening, the as-fabricated AM Al-Cu-Mn-Zr alloy still possesses improved creep resistance at 300 °C relative to a cast alloy with similar composition. The proposed load shuffling mechanism explains the lack of observed L1 2 -Al 3 Zr strengthening at 300 °C and helps identify several strategies for improvement of elevated-temperature mechanical response of AM Al alloys.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Phase stability in cast and additively manufactured Al-rich Al-Cu-Ce alloys

Additively manufactured (AM) eutectic Al alloy systems have been studied extensively for advantageous thermal stability and mechanical properties due to their refined microstructures. Al-Cu-Ce alloys are one subset of these AM eutectic alloys. Here we studied phase stability in AM Al-Cu-Ce alloys and compared it to that of conventionally cast ones. A new phase, Al 8 Cu 3 Ce, was identified in the microstructures of both AM and cast Al-Cu-Ce alloys. This Al 8 Cu 3 Ce phase was not previously included on experimental or thermodynamically calculated phase diagrams of the Al-Cu-Ce system. Therefore, we performed additional thermodynamic modeling of the system. These models were experimentally validated with cast and subsequently heat-treated Al-Cu-Ce alloys. We found that despite the refined microstructure of the AM alloys, the phases formed were consistent with the cast alloys, suggesting that AM processing did not significantly alter the formation and stability of phases from that in the conventional alloys. In conclusion, this work has resolved inconsistent previous descriptions of the Al-Cu-Ce ternary phase diagram in the Al-rich region and resulted in the addition of the Al 8 Cu 3 Ce as an equilibrium phase above 500 °C.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Using θ' interfaces as templates for planar L1 2 precipitation in AlCuMnZr alloys

Controlled Mn and Zr additions to Al-Cu alloys have allowed for the improved retention of mechanical properties after extended 350°C exposures by stabilizing the main strengthening θ' (Al 2 Cu) phase. Ultimately, θ'/L1 2 (Al 3 Zr) co-precipitate formation stabilizes θ' most effectively; however, Zr diffuses sluggishly and has low solubility in aluminum castings. Increasing the Zr segregation rate would allow for faster and more effective θ'/L1 2 co-precipitation. It is demonstrated that the Zr segregation rate is faster when the Zr matrix content is higher. A much higher Zr matrix content was achieved by rapid cooling during additive manufacturing (AM) that produces θ'/L1 2 co-precipitation faster, which is shown by scanning transmission electron microscopy and atom probe tomography experiments. It was also found that Zr continuously segregates to θ' interfaces up to the most aggressive heat treatment studied such that planar L1 2 precipitates remain after the metastable θ' dissolves. In this manner, we demonstrate that θ' coherent interfaces serve as perfect templates to form stable planar L1 2 precipitates that can provide strength at higher temperatures than traditional θ' strengthened AlCu alloys. This work introduces an alloy design strategy that uses metastable precipitates to quickly nucleate and grow co-precipitates with a desired geometry that contain slow diffusing elements. These ideas can be applied to engineer more heat resistant alloys by taking advantage of high solute matrix contents enabled by rapid cooling during additive manufacturing.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Repurposing the θ (Al 2 Cu) phase to simultaneously increase the strength and ductility of an additively manufactured Al–Cu alloy

The Al–Cu–Mn–Zr (ACMZ) cast family of alloys offers unique properties and value propositions for higher strength, higher temperature lightweight components of future vehicles. Earlier research has demonstrated trade-offs in the selection of the alloy chemistry in which an increase in Cu content from 6 up to 9 wt% improves hot tear resistance but lowers ductility. However, a recent study has demonstrated that higher-Cu (9Cu) ACMZ fabricated with laser powder bed fusion additive manufacturing (AM) results in an increase in both ductility and strength when compared to as-aged microstructure of cast 9Cu alloys. The mechanisms of differing mechanical performance of the cast and AM ACMZ alloys are elucidated in the current paper through the utilization of in situ high energy x-ray diffraction (HEXRD) tensile testing wherein lattice strains of different phases are calculated and correlated to their stresses. The ACMZ alloys consisted of theta (θ) and theta prime (θ') phases (both Al 2 Cu in nominal composition) within an aluminum matrix. The larger micron-size θ phase which decorated the grain boundaries in 9Cu ACMZ cast alloys recorded small lattice strains, while the submicron, homogeneously distributed θ phase in the 9Cu ACMZ AM alloy recorded considerably higher lattice strains. The maximum stress reached in the θ phase for the cast 9Cu alloy was found to be ~280 MPa, which was lower than the AM 9Cu alloy which registered a maximum stress of ~1.4 GPa. These measurements indicate that delayed fracture of the finer intermetallic phases simultaneously improves the ductility and strength of AM 9Cu alloy relative to the cast 9Cu alloy, which exhibits early fracture of the larger intermetallic particles.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Effect of grain-boundary θ-Al 2 Cu precipitates on tensile and compressive creep properties of cast Al–Cu–Mn–Zr alloys

Tensile and compressive creep tests were performed at 300 °C on high-temperature Al–Cu–Mn–Zr (ACMZ) alloys with 6 wt% Cu (6Cu) and 9 wt% Cu (9Cu) to evaluate the effect on creep properties of micron-size θ-Al 2 Cu intergranular precipitates. For compressive creep, the increased volume fraction of θ-precipitates at grain boundaries (from ~0.7% in 6Cu to ~ 6% in 9Cu) does not affect deformation rates across the investigated stress range of 15–110 MPa, consistent with creep being controlled by submicron θ'-Al 2 Cu precipitates within grains, whose size and fractions are the same in both alloys. In contrast, for tensile creep, 9Cu creeps faster than 6Cu at stresses above 20 MPa, and this difference increases with the stress level. Additionally, this discrepancy between tensile and compressive creep behavior is explained by cavitation during tensile creep, which is favored by higher volume fraction and larger size of intergranular θ precipitates in 9Cu. Conversely, larger precipitates impede cavity linkage resulting in improved creep ductility of 9Cu as compared to 6Cu at 300 °C.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Microstructural evolution and strengthening mechanisms in a heat-treated additively manufactured Al–Cu–Mn–Zr alloy

In this report the microstructural and strength evolution of an additively manufactured Al-8.6Cu-0.5Mn-0.9Zr alloy upon aging at 300, 350, and 400 °C is investigated. The strengthening phases of the alloy evolve significantly upon aging, with breakdown and spheroidization of the interconnected θ-Al 2 Cu network, dissolution of metastable θ'-Al 2 Cu precipitates, and precipitation of nanometric L1 2 -Al 3 Zr from a matrix supersaturated in Zr. In the peak-aged states, the alloy displays a favorable combination of strength and ductility, with a room-temperature yield strength of 314–341 MPa and ductility of 11–13%. The measured yield strengths for microstructures with different aging treatments are compared to predictions of yield strengths from grain boundary, solid solution, and particle strengthening contributions. The observed strain hardening behavior is related to fundamental precipitate and dislocation interactions. Comparison between predicted and measured strength values indicates a continued need for strengthening models specifically developed for the heterogeneous microstructures of additively manufactured alloys.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Cavitation-resistant intergranular precipitates enhance creep performance of θ'-strengthened Al-Cu based alloys

Tensile and compressive creep properties of a quaternary Al-Cu-Mn-Zr (ACMZ) alloy and its commercial counterpart (Al-Cu-Mn-Zr with Ni, Co and Sb additions, RR350) are investigated at 300°C. At low stresses up to 30 MPa where diffusional creep dominates, creep resistance is the same in tension and compression and RR350 deforms more slowly than ACMZ, consistent with RR350 alloy's larger linear fraction of intergranular precipitates (Al7Cu2(NiFe) and Al9FeNi for RR350 vs. θ-Al2Cu for ACMZ) and a reduced fraction of precipitate-free zones near grain boundaries. At stresses between 30 and 80 MPa, dislocation creep with a stress exponent n ~ 3 becomes rate-limiting in compression, which is expected to be controlled by θ' precipitates within the grain bulk. By contrast, in tension, enhanced creep rate and higher apparent stress exponents are measured, consistent with cavitation at intergranular precipitates becoming increasingly dominant as the stress increases. In the dislocation creep regime, RR350 alloy is again more creep resistant than ACMZ alloy, which is related to three mechanisms (i) a reduced fraction of softer precipitate-free zones, (ii) more effective load transfer to intergranular precipitates, and (iii) reduced cavitation. A model for cavitation is applied to calculate tensile creep rates from compressive creep rates and the model successfully predicts the improved tensile creep resistance of the RR350 alloy. Overall, the present investigation underscores the importance of intergranular grain boundary precipitates, in addition to strengthening θ' precipitates, in enhancing the creep resistance of Al-Cu alloys.

36 MATERIALS SCIENCE↗

DOE OSTI2022

A creep-resistant additively manufactured Al-Ce-Ni-Mn alloy

Existing additively manufactured aluminum alloys exhibit poor creep resistance due to coarsening of their strengthening phases and refined grain structures. In this paper, we report on a novel additively manufactured Al-10.5Ce-3.1Ni-1.2Mn wt.% alloy which displays excellent creep resistance relative to cast high-temperature aluminum alloys at 300–400 °C. In this work, the creep resistance of this alloy is attributed to a high volume fraction (~35%) of submicron intermetallic strengthening phases which are coarsening-resistant for hundreds of hours at 350 °C. The results herein demonstrate that additive manufacturing provides opportunities for development of creep-resistant aluminum alloys that may be used in bulk form in the 250–400 °C temperature range. Pathways for further development of such alloys are identified.

36 MATERIALS SCIENCE↗