Al-Cu-Ce(-Zr) alloys with an exceptional combination of additive processability and mechanical prope
Explore the source record for details and available documents.
Bahl, Sumit↗
Engineering topics
Bahl, Sumit
Publications and source records attributed to Bahl, Sumit.
Elevated temperature ductility dip in an additively manufactured Al-Cu-Ce alloy
The deformation and failure mechanisms of Al-9Cu-6Ce (wt%) based alloys fabricated with laser powder bed fusion were investigated from room temperature to 400°C. The yield and ultimate tensile strengths decreased monotonically with increase in temperature, but the tensile elongation dipped unexpectedly at elevated temperatures and exhibited a minimum at 300°C. The dip in tensile elongation occurred with a concomitant dip in strain-rate sensitivity (SRS) of deformation. The as-fabricated alloy microstructure was heterogeneous, and the heat affected zone (HAZ) underneath the melt pool boundary was prone to strain localization. At 300 °C, the reduced SRS promoted the progression of strain localization in the HAZ leading to failure initiation and the dip in tensile elongation. Furthermore, a higher SRS or strain-hardening rate at other temperatures improved the tensile elongation by slowing the progression of strain localization in the HAZ such that failure initiated by other mechanisms elsewhere in the microstructure. Notably, the tensile elongation was limited by the defect structure only in a narrow temperature range (150 - 200 °C) while at other temperatures it was limited by the inherent microstructural features. This investigation exemplifies unexpected deformation and failure mechanisms possible in heterogeneous microstructures that result from additive manufacturing.
36 MATERIALS SCIENCE↗
The role of Si in determining the stability of the θ; precipitate in Al-Cu-Mn-Zr alloys
Precipitate-strengthened Al-Cu-Mn-Zr (ACMZ) alloys demonstrate improved microstructural stability compared to conventional Al-Cu alloys. Si is typically considered an impurity in these alloys, but a systematic analysis of ACMZ alloys with a range of Si levels revealed that there is a Si content range (~0.05 wt. % < Si < ~0.10 wt. %) for achieving optimal high temperature microstructural stability. A combination of hardness testing, scanning electron microscopy, and atom probe tomography has been used to understand the relationship between Si content, aging response, and thermal stability in ACMZ alloys. It is shown that the optimum Si content range corresponds to a reduced as-aged hardness, but a greater hardness value retained by the alloy after thermal exposure to 350 °C for 200 hours. A mechanism is proposed in which optimum Si levels reduce the number density of nucleation sites for θ' precipitates, resulting in larger precipitates that, on average, provide a reduced as-aged strength but are more coarsening resistant. This inherent θ' coarsening resistance allows more time for slow-diffusing Mn and Zr to reach the θ' interface and further stabilize the precipitates. Designing the optimal as-aged microstructure for improved thermal stability of the alloy by controlling impurity levels is a concept that has implications beyond the investigated Al-Cu alloy system.
36 MATERIALS SCIENCE↗
Enhanced biomechanical performance of additively manufactured Ti-6Al-4V bone plates
As the global trauma fixation devices market expands rapidly, it is imperative to improve the production of fixation devices through enhanced design accuracy and fit for best performance and maximum patient comfort. Selective laser melting (SLM) is one of the mature additive manufacturing methods, which provides a viable route for the rapid production of such devices. In this work, the ability of SLM to produce near-net-shape parts, as desired for medical implants, was utilized for the fabrication of bone plates from Ti-6Al-4V alloy powder. Martensitic microstructure obtained after the printing of alloy resulted in poor ductility, limiting its application in the field of orthopedics. A specially designed repeated cyclic heating and cooling close to but below the β-transus was used to transform from acicular to a bimodal microstructure without the need for plastic deformation prior to heat treatment for improving the ductility. Bone plates subjected to this heat treatment were mechanically tested by means of tensile and 3-point bend tests and demonstrated large improvement in ductility, and the values were comparable to those similar plates prepared from wrought alloy. Other important properties required for implants were assessed, such as corrosion resistance in simulated body fluid and cytocompatibility in vitro using MC3T3-E1 cells. These results for the bone plate after heat treatment were excellent and similar to those of the additively manufactured and wrought plates. Taken together, the performance of the additively manufactured bone plates after subjecting to heat treatment was similar to those of bone plate manufactured using wrought alloy. These results have important implications for the fabrication of patient-specific metallic orthopedic devices using SLM without compromising their biomechanical performance by subjecting them to a tailored heat treatment.
36 MATERIALS SCIENCE↗
Aging behavior and strengthening mechanisms of coarsening resistant metastable θ' precipitates in an Al–Cu alloy
Not Available
36 MATERIALS SCIENCE↗
Influence of copper content on the high temperature tensile and low cycle fatigue behavior of cast Al-Cu-Mn-Zr alloys
The relationship between low cycle fatigue (LCF) and monotonic tensile fracture strain was investigated for cast Al-Cu-Mn-Zr alloys containing 6 and 9 wt% Cu at 250 °C. The 9% Cu alloy consisted of larger size and volume fraction of brittle intermetallic grain boundary particles that fractured during tensile tests to reduce the fracture strain by 50% compared to the 6% Cu alloy. We found that LCF life was similar between the two alloys and weakly influenced by the particles. LCF life and fracture strain were poorly correlated due to the dominant influence of particles on monotonic tensile crack but not on fatigue crack.
36 MATERIALS SCIENCE↗
Microstructure and properties of a high temperature Al–Ce–Mn alloy produced by additive manufacturing
An Al–10Ce-8Mn (wt%) alloy was designed and fabricated by laser powder bed fusion additive manufacturing (AM). The rapid cooling rates of the AM process produced a refined microstructure with a large fraction of reinforcing intermetallic phases. The tensile properties of the alloy were characterized in the as-fabricated state and following thermal exposure. The properties of the as-fabricated microstructure showed exceptional high-temperature performance and strength retention at elevated temperatures up to 400 °C relative to benchmark wrought Al and AM Al alloy properties. Characterization of the microstructure and thermodynamic modeling of the ternary Al–Ce–Mn system rationalized the solidification and solid-state phase transformations. Finally, analysis of the relevant strengthening mechanisms for both the as-fabricated and thermally exposed conditions was performed.
36 MATERIALS SCIENCE↗
Solute-vacancy clustering in aluminum
In this study, we present an extensive first-principles database of solute-vacancy, homoatomic, heteroatomic solute-solute, and solute-solute-vacancy binding energies of relevant alloying elements in aluminum. We particularly focus on the systems with major alloying elements in aluminum, i.e., Cu, Mg, and Si. The computed binding energies of solute-vacancy, solute-solute pairs, and solute-solute-vacancy triplets agree with available experiments and theoretical results in literature. We consider physical factors such as solute size and formation energies of intermetallic compounds to correlate with binding energies. Systematic studies of the homoatomic solute-solute-vacancy and heteroatomic (Cu, Mg, or Si)-solute-vacancy complexes reveal the overarching effect of the vacancy in stabilizing solute-solute pairs. The binding energy database presented here elucidates the interaction between solute cluster and vacancy in aluminum, and it is expected to provide insight into the design of advanced Al alloys with tailored properties.
36 MATERIALS SCIENCE↗
Primary solidification of ternary compounds in Al-rich Al–Ce–Mn alloys
Primary solidification of ternary compounds Al 20 Mn 2 Ce and Al 10 Mn 2 Ce were analyzed through the coupling of the thermodynamic modeling and classic nucleation theory. Thermodynamic models of Al 20 Mn 2 Ce and Al 10 Mn 2 Ce were developed using the CALPHAD approach based on first-principles calculated enthalpy of formation and experimental data obtained from this work and the literature. The analysis suggested that despite the larger thermodynamic driving force for nucleation of Al 10 Mn 2 Ce, nucleation is preferred for the Al 20 Mn 2 Ce phase in the highly undercooled liquid due to its smaller interfacial energy. Therefore, manufacturing methods with rapid cooling rates will favor primary solidification of Al 20 Mn 2 Ce for Al-rich Al–Ce–Mn alloys.
36 MATERIALS SCIENCE↗
An additively manufactured AlCuMnZr alloy microstructure and tensile mechanical properties
In this study, selective laser melting (SLM) was used to fabricate an AlCuMnZr alloy. The microstructural features that resulted from additive manufacturing (AM) were significantly refined compared to the corresponding cast alloy features. A combination of fine equiaxed and columnar grains along with in-situ formation of θ' precipitates during AM leads to enhanced yield strength (up to 300°C) in the as-fabricated AM alloy. The refinement of brittle intermetallics and a bimodal grain size distribution leads to improved tensile elongation in the AM alloy. The results illustrate the microstructural advantages that can result from additive processing over conventionally processed microstructures.
36 MATERIALS SCIENCE↗
Effect of copper content on the tensile elongation of Al–Cu–Mn–Zr alloys: Experiments and finite element simulations
Microstructures of cast aluminum alloys used in automotive engine applications often consist of intermetallic particles that can impact the tensile elongation of these alloys. Here in this paper, we investigate the effect of intermetallic grain boundary particles on tensile elongation by fabricating a series of alloys with Cu content varying between 6.0 - 9.0 wt% in cast Al–Cu–Mn–Zr (ACMZ) type compositions. The tensile elongation of as-aged ACMZ alloys decreases monotonically with increase in Cu content. While the microstructure within the grains and yield stress of the alloy remains invariant with Cu content, the decrease in tensile elongation correlates well with increase in the size and volume fraction of grain boundary particles. Microstructural observations are combined with finite element simulations to explain the trend in tensile elongation with changing Cu content. Crack initiation is found to occur by brittle fracture of the grain boundary particles. Increase in particle size promotes crack initiation by reduction in size dependent particle fracture strength. Lower inter-particle spacing at higher particle volume fraction further facilitates crack initiation by increasing stress within the particles caused by the interaction between stress fields of neighboring particles. Increase in particle volume fraction also accelerates crack propagation through the formation of macro shear zones in the microstructure. The increase in Cu content of cast ACMZ alloys, therefore, decreases tensile elongation by promoting both crack initiation and crack propagation.
36 MATERIALS SCIENCE↗