Engineering topics
Publications and source records attributed to Baskaran, Karthikeyan.
Different sorbents, including activated carbons, an aerogel, xerogels, an alumina, a zeolite, and a carbon foam were investigated for static I 2(g) loading at 71 °C for 56 d followed by 4.7 d of desorption.
Not Available
Bismuth-containing carbon materials have been shown to be highly promising sorbents for the capture of radioiodine. However, there is still a need to understand the effects of carbon and bismuth on the iodine sorption mechanism. In this study, we show the relationship between the physical and chemical sorption of iodine under different bismuth loading conditions. Here, highly porous and non-friable conductive carbon foams were prepared and bismuth was electrodeposited to provide strong iodine binding sites. For pure carbon foams, equal ratios of physisorbed and chemisorbed iodine-carbon phases were detected before desorption. As the concentration of bismuth increased, the chemisorption between bismuth and iodine dominated the total capture mechanism and physisorption was almost completely eliminated. Additionally, chemisorption of iodine depended upon the size and specific surface area of the bismuth particles present within the framework of the foam.
Not Available
The dynamic immiscibility between vegetable oil and organic silica precursors during sol-gel synthesis was used to tailor the microstructure of gels made with tetraethoxysilane (TEOS) or tetraethoxysilane+methyltrimethoxysilane (MTMS). Vegetable oil was investigated as an environmentally friendly and cheaper alternative to many other porogens. Oil concentrations of 9.09 v/v% and 33.33 v/v% were studied. For both TEOS and TEOS+MTMS gels, the miscibility of the oil and precursor decreases as the silica gel network forms, leading to oil-rich regions within the silica matrix. Gels containing MTMS maintained partial miscibility with the oil during gel formation due to the non-hydrolysable methyl groups on the MTMS. The pore structure of MTMS gels appeared more interconnected compared to the isolated pores observed in gels made with only TEOS. To create membranes with hierarchical pore structures, solvent exchanges were performed on gels or dried gels (i.e., xerogels) were calcined. The effect of the methyl group was also observed in the results of the time sweep rheology, as the addition of oil to the TEOS+MTMS gels caused an increase in the time to form the spanning gel. The trend was the opposite for oil additions to TEOS gels, which only contained polar groups. Xerogel membranes made with TEOS+MTMS had higher specific surface areas (SSAs) than those made with TEOS. For oil concentrations of 33.33 v/v%, xerogels made from TEOS+MTMS had an average SSA of 1068 + 113 m2 g-1, an order of magnitude higher than the average SSA of 103 + 6 m2 g-1 for xerogels made with TEOS.
Many natural plant tissues, such as pinecones, utilize structures to transduce changes in humidity into movement or strain. These often employ layered structures with aligned features in order to create differential stress across the material as different portions swell at different rates. Here, by replicating these types of structures in synthetic materials we can create structures that respond to humidity in a similar manner. Taking these aligned features as inspiration, silica aerogels with tailored humidity reactive properties were created. This behavior was achieved by creating aligned features in these aerogels using a Helmholtz coil to produce a uniform magnetic field that aligned ferrofluid droplets into chains and needle like features. These magnetite-based structures were shown to retain their superparamagnetic properties, allowing them to easily be removed from the aerogels, leaving a large number of aligned channels. Aerogels with the removed needles experienced significantly different strains than both unmodified aerogels and aerogels with the aligned features still in place. Aerogels with these tunable aligned features could be used in humidity sensors that can transduce changes in humidity into strain and could be used in applications such as volatile organic compound capture.