Engineering topics
Publications and source records attributed to Blome, J. C..
Addition of silica fibers greatly reduces shrinkage and cracking during casting of ceramics. Fiber-reinforced slip-cast silica ceramics are also tougher and have lower dielectric loss. Silica fibers are hyperpure material containing only 1 part per million total metal-ion impurities. Hyperpure fibers ensure high reflectance and allow casting to be fired at temperature greater than 2,200 degrees F without loss of strength from devitrification.
A hyperpure vitreous silica material is being developed for use as a reflective and ablative heat shield for planetary entry. Various purity grades and forms of raw materials were evaluated along with various processing methods. Slip casting of high purity grain was selected as the best processing method, resulting in a highly reflective material in the wavelength bands of interest (the visible and ultraviolet regions). The selected material was characterized with respect to optical, mechanical and physical properties using a limited number of specimens. The process has been scaled up to produce a one-half scale heat shield (18 in. dia.) (45.72 cm) for a Jupiter entry vehicle. This work is now being extended to improve the structural safety factor of the heat shield by making hyperpure silica material tougher through the addition of silica fibers.
An experimental program to optically characterize hyperpure slip cast silica at elevated temperatures is described. This sintered ceramic material is being used in the development of a reflective heat shield for the Outer Planet Entry Probe. A unique high temperature integrating sphere reflectometer is described and reflectance data in the spectral range 0.23-2.3 micron are presented at temperatures up to 1427 C in air and helium environments. Kubelka-Munk (K-M) scattering and absorptance coefficients (K and S), using the Reichman extension of the K-M theory, are presented as is a unique method of obtaining K and S from the Reichman equations using only reflectance data. The hyperpure slip cast silica material was found to retain its high diffuse reflectance at temperatures up to 1204 C, with slight degradation occurring at higher temperatures.
A high purity slip cast silica material has been developed for use as a reflective heat shield for entries into the atmospheres of the outer planets. The several stages leading to the development of this material are described and details of raw material selection, preparation of the slip material and casting techniques are discussed. Optical (reflectance and transmittance), physical and chemical properties measurements were performed as a function of the important material and processing variables. Performance analysis of a reflective heat shield fabricated from the high purity silica slip shows that approximately 90 percent of the radiant bow shock energy incident on the heat shield during entry into the atmosphere of Jupiter will be reflected.
Measurements were made of reflectance in the vacuum ultraviolet down to 0.15 micron. Scattering coefficients (S) and absorption coefficients (K) were also measured. These coefficients express the optical properties and are used directly in a thermodynamic analysis for sizing a heat shield. The effect of the thin silica melt layer formed during entry was also studied from the standpoint of trapped radiant energy.
The mullite fiber based hardened compacted fibers (HCF) type of reusable surface insulation was further developed for use in the Space Shuttle Program. Two hundred fifty formulations of fiber mixtures, fillers, binders, and organic processing aids were made using mullite fibers as the basic ingredient. Most of the work was accomplished on 15-lb/cu ft material. It was established that higher density materials are stronger with strength values as high as 250 lb/sq in. in tension. New measurement techniques and equipment were developed for accurate determination of strength and strain to failure. Room temperature to 2300 F stress-strain relationships were made. The room temperature tensile modulus of elasticity is 61,700 lb/sq in. and the strain at failure is 0.165 percent, typically, when measured longitudinally parallel to the long axes of the fibers. Thermal insulating effectiveness was increased 20 percent by reducing the diameter of some of the fibers in the material. Improvements were made in density uniformity and strength uniformity in a block of HCF by mixing improvements and by the use of organic additives. Specifications were established on the materials and processes used in making the insulation.