Improvement of Reusable Surface Insulation (RSI) materials

Abstract

The mullite fiber based hardened compacted fibers (HCF) type of reusable surface insulation was further developed for use in the Space Shuttle Program. Two hundred fifty formulations of fiber mixtures, fillers, binders, and organic processing aids were made using mullite fibers as the basic ingredient. Most of the work was accomplished on 15-lb/cu ft material. It was established that higher density materials are stronger with strength values as high as 250 lb/sq in. in tension. New measurement techniques and equipment were developed for accurate determination of strength and strain to failure. Room temperature to 2300 F stress-strain relationships were made. The room temperature tensile modulus of elasticity is 61,700 lb/sq in. and the strain at failure is 0.165 percent, typically, when measured longitudinally parallel to the long axes of the fibers. Thermal insulating effectiveness was increased 20 percent by reducing the diameter of some of the fibers in the material. Improvements were made in density uniformity and strength uniformity in a block of HCF by mixing improvements and by the use of organic additives. Specifications were established on the materials and processes used in making the insulation.