Search NASA⌕ Search

Engineering topics

Busch, R.

Publications and source records attributed to Busch, R..

8 records
All sourcesNASA NTRSDOE OSTI
NASA NTRS1995

(abstract) Determination of the Specific Heat and Total Hemispherical Total Emissivity of the Highly Undercooled Zr(sub 41.2)Ti(sub 13.8)Cu(sub 12.5)Ni(sub 10.0)Be(sub 22.5) Alloy

High temperature high vacuum electrostatic levitation was combined with DSC experiments to determine the specific heat C(sub p) of the undercooled Zr(sub 41.2)Ti(sub 13.8)Cu(sub 12.5)Ni(sub 10.0)Be(sub 22.5) liquid as a function of temperature. The containerless approach made it possible to undercool the melt to the glass transition temperature without inducing nucleation. Because the cooling process was purely radiative, noncontact temperature measurement techniques could be used to determine the specific heat to total hemispherical emissivity ratio, C(sub p)/epsilon(sub t), for the undercooled liquid region. Using C(sub p) values which were independently obtained by DSC, epsilon(sub t) could be determined. With knowledge of C(sub p) of the undercooled liquid it was possible to determine other thermodynamic properties such as Gibbs free energy and entropy as a function of undercooling.

levitation thermodynamic properties undercooled al↗
NASA NTRS1995

(abstract) Undercooling Studies of the Bulk Metallic Glass Forming Zr(sub 41.2)Ti(sub 13.8)Cu(sub 12.5)Ni(sub 10.0)Be(sub 22.5) Alloy During Containerless Electrostatic Levitation Processing

Bulk glass forming metallic alloys have long been desired for technological applications and for investigation into liquid undercooling, solidification processes, and thermophysical properties. A glass forming alloy Zr(sub 41.2)Ti(sub 13.8)Cu(sub 12.5)Ni(sub 10.0)Be(sub 22.5) was used to investigate the thermal treatments affecting undercooling and vitrification. The experiments were performed using the high temperature high vacuum electrostatic levitator at JPL. A sample approximately 3 mm in diameter was melted, superheated, undercooled, and solidified while levitated in high vacuum. The results show that when the sample was held above its melting temperature for a sufficient period of time to dissolve oxides and then cooled faster than a critical cooling rate, it undercooled to the glass transition temperature, T(sub g), and formed a glassy alloy. The required critical cooling rate for metallic glass formation was obtained to be between 0.9 K per second and 1.2 K per second for the 42.4 mg sample.

levitation vitrification↗
NASA NTRS1978

Development of sputtering process to deposit stoichiometric zirconia coatings for the inside wall of regeneratively cooled rocket thrust chambers

Thermal barrier coatings of yttria stabilized zirconia and zirconia-ceria mixtures were deposited by RF reactive sputtering. Coatings were 1-2 mils thick, and were deposited on copper cylinders intended to simulate the inner wall of a regeneratively cooled thrust chamber. Coating stoichiometry and adherence were investigated as functions of deposition parameters. Modest deposition rates (approximately 0.15 mil/hr) and subambient sustrate temperatures (-80 C) resulted in nearly stoichiometric coatings which remained adherent through thermal cycles between -196 and 400 C. Coatings deposited at higher rates or substrates temperatures exhibited greater oxygen deficiences, while coatings deposited at lower temperatures were not adherent. Substrate bias resulted in structural changes in the coating and high krypton contents; no clear effect on stoichiometry was observed.

Busch, R.↗
NASA NTRS1976

Development of sputtered high temperature coatings for thrust chambers

Adherent insulating coatings were developed for thrust chamber service. The coatings consisted of nickel and a ceramic, and were graded in composition from pure nickel at the thrust chamber wall to pure ceramic at the coating surface. The coatings were deposited by rf sputtering from a target with a reversed composition gradient, which was produced by plasma spraying powder mixtures. The effect of deposition parameters on coating characteristics and adherence is discussed.

Busch, R.↗
NASA NTRS1974

Fabrication of thick structures by sputtering

Deposit, 5500-gram of Cu-0.15 wt % Zr alloy, sputtered onto copper cylinder to average thickness of 12.29 mm. Structure was achieved with high-rate sputter deposition for about 100 hours total sputtering time. Material had twice the strength of unsputtered material at temperatures to 723 K and equivalent strength at nearly 873 K.

Kazaroff, J. M.↗
NASA NTRS1973

Property investigation and sputter deposition of dispersion-hardened copper for fatigue specimen fabrication

Sputter-deposited alloys of dispersion-hardenable Cu-0.25 vol% SiC and Cu-0.50 vol% SiC and precipitation-hardenable Cu-0.15 wt% Zr and Cu-0.05 wt% Mg-0.15 wt% Zr-0.40 wt% Cr were investigated for selection to evaluate fatigue specimen performance with potential application in fabricating regeneratively cooled rocket thrust chambers. Yield strengths in the 700 to 1000-MN/sq m range were observed with uniform elongation ranging from 0.5 to 1.5% and necking indicative of greater ductility. Electrical conductivity measured as an analog to thermal conductivity gave values 90% IACS for Cu-0.15 wt% Zr and Cu-0.05 wt% Mg-0.15 wt% Zr-0.40 wt% Cr. A 5500-g sputtered deposit of Cu-0.15 wt% Zr alloy, 12.29 mm (0.484 in.) average thickness in the fatigue specimen gage length, was provided to NASA on one of their substrates.

Mcclanahan, E. D.↗