Effect of multiple strain-anneal cycles on the 1000 C creep behaviour of gamma/gamma prime-alpha
Various multiple strain-anneal cycles (1000 C) were imposed on specimens of the directionally solidified eutectic (DSE) alloy gamma/gamma prime-alpha to identify thermomechanical processing methods (TMP) which would improve the creep behavior. Specimens of the Ni-32.3Mo-6.3Al wt pct alloy were grown with a modified Bridgeman technique. Some of the cylindrical specimens were alternately heat-treated at 900 C, then strained, or heat-treated only, while other specimens were annealed at 900 C after swaging and then worked at ambient temperature. The specimens were all examined microstructurally using transmission electron microscopy, some before and after being exposed to constant-load compression tests at 1000 C. The creep strain increased for all TMP specimens for strain rates of at least 2 millionths per sec. Strain rates of about 2 ten millionths per sec were only improved with strain annealing with 13 percent work at ambient temperature. A slight improvement, compared to as-grown materials, was observed in the 1000 C creep behavior of materials annealed at 900 C. Strain-annealing was found to introduce three-dimensional dislocation networks into the gamma-prime matrix.