Mitigation of spall fracture by evolving porosity

Ductile materials subject to impact loading conditions can undergo spall fracture when an incoming compressive stress wave reflects off interfaces and free surfaces as a tensile stress wave. Experimental observations suggest that in ductile materials, spall fracture is driven by the evolution of porosity. However, the presence of initial porosity in ductile materials also introduces plastic compressibility, which can attenuate the incoming compressive stress wave and, as a result, reduce the amplitude of the reflected tensile stress wave. This, in turn, can mitigate or delay spall fracture. In this work, we report on finite deformation finite element calculations that analyze the response of porous ductile materials subjected to impact loading conditions. Two sets of calculations are carried out, in the first set the material contains initial porosity values ranging from 0% to 5% while in the second set the material also undergoes stress-controlled porosity nucleation. Both sets of calculations are carried out for a wide range of imposed impact velocities. Here, our results show that porosity in ductile materials can, under certain circumstances, mitigate spall fracture by attenuating stress waves. Results correlating the effects of impact velocity, initial porosity, and porosity nucleation on spall fracture are presented and the underlying mechanisms are discussed.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Intergranular ductile failure of materials with plastically heterogeneous grains

In several precipitation hardened alloys that are susceptible to intergranular ductile failure, precipitation does not always occur uniformly throughout the microstructure, and regions close to grain boundaries may remain precipitate-free. These precipitate-free zones (PFZs) in the material microstructures result in plastically heterogeneous grains, since PFZs are expected to have lower yield strength but higher strain-hardenability compared to the precipitate containing grain interior. Experimentally, the presence of PFZs in precipitation-hardened alloys has been associated with both increase and decrease in materials’ ductility, with or without significant change in the strength. Thus, to understand and rationalize the experimental observations, we have carried out extensive microstructure-based finite element calculations of intergranular ductile failure in materials under tensile loading conditions. In the calculations, both the grain boundaries and PFZs are discretely modeled, and a wide range of the values of yield strength, strain-hardenability and width of PFZs in the material microstructures are analyzed. Our results show that the effects of PFZs on the overall mechanical response of the material strongly depend on the values of yield strength and strain-hardenability of PFZs. Here, there exists an optimum combination of the values of these two parameters that can result in the overall ductility and tensile strength of the material microstructures with PFZs being greater than the microstructures without PFZs.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Toughening of interface networks through the introduction of weak links

The resistance of polycrystalline materials to intergranular fracture depends on the toughness of the interfaces between neighboring grains. Using finite element simulations on model, two-dimensional microstructures, we demonstrate that the steady-state crack growth resistance of a polycrystal that contains exclusively high toughness interfaces is suboptimal: its crack growth resistance may be increased by introducing a minority fraction of weak interfaces at random locations within the interface network. Furthermore, the weaker are these interfaces, the greater is their toughening effect. These weak interfaces toughen the material through crack deflection and branching, nucleation of secondary cracks, and inelastic dissipation within intact interfaces. Furthermore, our findings suggest that fracture resistance-oriented material development should not aim to eliminate all weak interfaces, but rather judiciously incorporate a low fraction of them.