Engineering topics

Crews, J. H., Jr.

Publications and source records attributed to Crews, J. H., Jr..

At least 19 records

NASA NTRS1994

Variations of a global constraint factor in cracked bodies under tension and bending loads

Elastic-plastic finite-element analyses were used to calculate stresses and displacements around a crack in finite-thickness plates for an elastic-perfectly plastic material. Middle- and edge-crack specimens were analyzed under tension and bending loads. Specimens were 1.25 to 20 mm thick with various widths and crack lengths. A global constraint factor alpha(sub g), an averaged normal-stress to flow-stress ratio over the plastic region, was defined to simulate three-dimensional (3D) effects in two-dimensional (2D) models. For crack lengths and uncracked ligament lengths greater than four times the thickness, the global constraint factor was found to be nearly a unique function of a normalized stress-intensity factor (related to plastic-zone size to thickness ratio) from small- to large-scale yielding conditions for various specimen types and thickness. For crack length-to-thickness ratios less than four, the global constraint factor was specimen type, crack length and thickness dependent. Using a 2D strip-yield model and the global constraint factors, plastic-zone sizes and crack-tip displacements agreed reasonably well with the 3D analyses. For a thin sheet aluminum alloy, the critical crack-tip-opening angle during stable tearing was found to be independent of specimen type and crack length for crack length-to-thickness ratios greater than 4.

Newman, J. C., Jr.↗

NASA NTRS1991

Strain energy release rate distributions for double cantilever beam specimens

A 24-ply composite double cantilever-beam specimen under mode I (opening) loading has been analyzed by a 3D FEM code that calculated along a straight delamination starter for several different specimen materials. An isotropic specimen was found to have a strain-energy release rate distribution which varied along its delamination front due to the boundary-layer effect and another effect associated with the anticlastic curvature of the bent specimen arms. A 0-deg graphite-reinforced epoxy specimen had a nearly-uniform strain-energy release rate distribution which dropped only near the edge, due to the boundary-layer effect, and a +/- 45-deg graphite/epoxy specimen exhibited a pronounced strain-energy release rate variation across the specimen width.

Crews, J. H., Jr.↗

NASA NTRS1991

Fracture mechanics analysis for various fiber/matrix interface loadings

Fiber/matrix (F/M) cracking was analyzed to provide better understanding and guidance in developing F/M interface fracture toughness tests. Two configurations, corresponding to F/M cracking at a broken fiber and at the free edge, were investigated. The effects of mechanical loading, thermal cooldown, and friction were investigated. Each configuration was analyzed for two loadings: longitudinal and normal to the fiber. A nonlinear finite element analysis was performed to model friction and slip at the F/M interface. A new procedure for fitting a square-root singularity to calculated stresses was developed to determine stress intensity factors (K sub I and K sub II) for a bimaterial interface crack. For the case of F/M cracking at a broken fiber with longitudinal loading, crack tip conditions were strongly influenced by interface friction. As a result, an F/M interface toughness test based on this case was not recommended because nonlinear data analysis methods would be required. For the free edge crack configuration, both mechanical and thermal loading caused crack opening, thereby avoiding frictional effects. A F/M interface toughness test based on this configuration would provide data for K(sub I)/K(sub II) ratios of about 0.7 and 1.6 for fiber and radial normal loading, respectively. However, thermal effects must be accounted for in the data analysis.

Naik, R. A.↗

NASA NTRS1991

Nonlinear analysis and redesign of the mixed-mode bending delamination test

The Mixed Mode Bending (MMB) test uses a lever to simultaneously apply mode I and mode II loading to a split beam specimen. An iterative analysis that accounts for the geometric nonlinearity of the MMB test was developed. The analysis accurately predicted the measured load displacement response and the strain energy release rate, G, of an MMB test specimen made of APC2 (AS4/PEEK). The errors in G when calculated using linear theory were found to be as large as thirty percent in some cases. Because it would be inconvenient to use a nonlinear analysis to analyze MMB data, the MMB apparatus was redesigned to minimize the nonlinearity. The nonlinear analysis was used as a guide in redesigning the MMB apparatus. With the redesigned apparatus, loads were applied through a roller attached to the level and loaded just above the midplane of the test specimen. The redesigned apparatuus has geometric nonlinearity errors of less than three percent, even for materials substantially tougher than APC2. This apparatus was demonstrated by measuring the mixed mode delamination fracture toughness of APC2.

Reeder, J. R.↗

NASA NTRS1991

Fracture mechanics analysis for various fiber/matrix interface loadings

Fiber/matrix (F/M) cracking was analyzed to provide better understanding and guidance in developing F/M interface fracture toughness tests. Two configurations, corresponding to F/M cracking at a broken fiber and at the free edge, were investigated. The effects of mechanical loading, thermal cooldown, and friction were investigated. Each configuration was analyzed for two loadings: longitudinal and normal to the fiber. A nonlinear finite element analysis was performed to model friction and slip at the F/M interface. A new procedure for fitting a square-root singularity to calculated stresses was developed to determine stress intensity factors (K sub I and K sub II) for a bimaterial interface crack. For the case of F/M cracking at a broken fiber with longitudinal loading, crack tip conditions were strongly influenced by interface friction. As a result, an F/M interface toughness test based on this case was not recommended because nonlinear data analysis methods would be required. For the free edge crack configuration, both mechanical and thermal loading caused crack opening, thereby avoiding frictional effects. An F/M interface toughness test based on this configuration would provide data for K(sub I)/K(sub II) ratios of about 0.7 and 1.6 for fiber and radial normal loading, respectively. However, thermal effects must be accounted for in the data analysis.

Naik, R. A.↗

NASA NTRS1991

Redesign of the mixed-mode bending test for delamination toughness

The mixed-mode bending (MMB) test uses a lever to simultaneously apply mode I and mode II loading to a split-beam specimen. A nonlinear, iterative analysis that accurately predicts the measured load-displacement response and the strain energy release rate, G, of an MMB test, has shown that the errors in G calculated using linear theory can be quite large. The nonlinear analysis was used as a guide in redesigning the MMB apparatus. With the redesigned apparatus, loads are applied through a roller attached to the lever and loaded just above the midplane of the test specimen. The redesigned MMB apparatus has geometric nonlinearity errors of less than 3 percent, even for materials substantially tougher than APC2 (AS4/PEEK). This apparatus was demonstrated by measuring the mixed-mode delamination fracture toughness of APC2. The data from the redesigned MMB apparatus were analyzed with a linear analysis which yielded results similar to those found with the original apparatus and the nonlinear analysis.

Reeder, J. R.↗

NASA NTRS1990

An apparatus for bearing-bypass testing of bolted joints

A dual-control test system measuring the strength of graphite/epoxy specimens under tension and compression for a wide range of bearing-bypass load ratios is presented. The bearing-bypass strengths of single-fastener specimens are measured for damage onset and ultimate failure and are plotted against one another. The results indicate that an initiated damage grows to failure in the same mode for most cases. However, if the damage is initiated in the compression-reacted-bearing mode, the specimens fail in the offset-compression mode. It is concluded that this type of transition can occur in multi-fastener joints under compression and complicate the strength predictions.

Crews, J. H., Jr.↗

NASA NTRS1990

Ply-level failure analysis of a graphite/epoxy laminate under bearing-bypass loading

A combined experimental and analytical study was conducted to investigate and predict the failure modes of a graphite/epoxy laminate subjected to combined bearing and bypass loading. Tests were conducted in a test machine that allowed the bearing-bypass load ratio to be controlled while a single-fastener coupon was loaded to failure in either tension or compression. Onset and ultimate failure modes and strengths were determined for each test case. The damage-onset modes were studied in detail by sectioning and micrographing the damaged specimens. A two-dimensional, finite-element analysis was conducted to determine lamina strains around the bolt hole. Damage onset consisted of matrix cracks, delamination, and fiber failures. Stiffness loss appeared to be caused by fiber failures rather than by matrix cracking and delamination. An unusual offset-compression mode was observed for compressive bearing-bypass loading in which the specimen failed across its width along a line offset from the hole. The computed lamina strains in the fiber direction were used in a combined analytical and experimental approach to predict bearing-bypass diagrams for damage onset from a few simple tests.

Naik, R. A.↗

NASA NTRS1989

Effects of T-tabs and large deflections in DCB specimen tests

A simple strength of materials analysis was developed for a double-cantilever beam (DCB) specimen to account for geometric nonlinearity effects due to large deflections and T-tabs. A new DCB data analysis procedure was developed to include the effects of these nonlinearities. The results of the analysis were evaluated by DCB tests performed for materials having a wide range of toughnesses. The materials used in the present study were T300/5208, IM7/8551-7, and AS4/PEEK. Based on the present analysis, for a typical deflection/crack length ratio of 0.3 (for AS4/PEEK), T-tabs and large deflections cause a 15 percent and 3 percent error, respectively, in the computer Mode 1 strain energy release rate. Design guidelines for DCB specimen thickness and T-tab height were also developed in order to keep errors due to these nonlinearities within 2 percent. Based on the test results, for both hinged and tabbed specimens, the effects of large deflection on the Mode 1 fracture toughness (G sub Ic) were almost negligible (less than 1 percent) in the case of T300/5208 and IM7/8551-7; however, AS4/PEEK showed a 2 to 3 percent effect. The effects of T-tabs G sub Ic were more significant for all the materials with T300/5208 showing a 5 percent error, IM7/8551-7 a 15 percent error, and, AS4/PEEK a 20 percent error.

Naik, R. A.↗

NASA NTRS1989

Stress analysis method for clearance-fit joints with bearing-bypass loads

Within a multi-fastener joint, fastener holes may be subjected to the combined effects of bearing loads and loads that bypass the hole to be reacted elsewhere in the joint. The analysis of a joint subjected to search combined bearing and bypass loads is complicated by the usual clearance between the hole and the fastener. A simple analysis method for such clearance-fit joints subjected to bearing-bypass loading has been developed in the present study. It uses an inverse formulation with a linear elastic finite-element analysis. Conditions along the bolt-hole contact arc are specified by displacement constraint equations. The present method is simple to apply and can be implemented with most general purpose finite-element programs since it does not use complicated iterative-incremental procedures. The method was used to study the effects of bearing-bypass loading on bolt-hole contact angles and local stresses. In this study, a rigid, frictionless bolt was used with a plate having the properties of a quasi-isotropic graphite/epoxy laminate. Results showed that the contact angle as well as the peak stresses around the hole and their locations were strongly influenced by the ratio of bearing and bypass loads. For single contact, tension and compression bearing-bypass loading had opposite effects on the contact angle. For some compressive bearing-bypass loads, the hole tended to close on the fastener leading to dual contact. It was shown that dual contact reduces the stress concentration at the fastener and would, therefore, increase joint strength in compression. The results illustrate the general importance of accounting for bolt-hole clearance and contact to accurately compute local bolt-hole stresses for combined bearings and bypass loading.

Naik, R. A.↗

NASA NTRS1989

Stress analysis method for clearance-fit joints with bearing-bypass loads

A simple direct stress analysis method is proposed for a laminate with a clearance-fit fastener subjected to combined bearing and bypass loads in tension or compression, including bearing and bypass loads on bolt-hole contact and local stresses. The approach uses a linear-elastic finite element analysis with an inverse formulation; conditions along the bolt-hole interface are specified by constraint equations that limit nodal displacements to a circular arc corresponding to the bolt diameter. The application of the method to the analysis of the effects of bearing-bypass loading on bolt-hole contact angles and local stresses, with the plate material properties representing a quasi-isotropic T300/5208 graphite/epoxy laminate, is discussed.

Naik, R. A.↗

NASA NTRS1988

Three-dimensional elastic analysis of a composite double cantilever beam specimen

Attention is given to the stresses and the strain energy release rate along the delamination front in the present three-dimensional elastic analysis of a 24-ply, cocured double-cantilever beam specimen by means of 20-noded parabolic-isoparametric finite elements. At the free surface, the strain energy release rate was found to be substantially smaller than the plane strain value; this is suggested to be due to the free-surface effect that exists where the delamination meets the surface edge.

Raju, I. S.↗

NASA NTRS1988

Ply-level failure analysis of a graphite/epoxy laminate under bearing-bypass loading

A combined experimental and analytical study was conducted to investigate and predict the failure modes of a graphite/epoxy laminate subjected to combined bearing and bypass loading. Tests were conducted in a test machine that allowed the bearing-bypass load ratio to be controlled while a single-fastener coupon was loaded to failure in either tension or compression. Onset and ultimate failure modes and strengths were determined for each test case. The damage-onset modes were studied in detail by sectioning and micrographing the damaged specimens. A two-dimensional, finite-element analysis was conducted to determine lamina strains around the bolt hole. Damage onset consisted of matrix cracks, delamination, and fiber failures. Stiffness loss appeared to be caused by fiber failures rather than by matrix cracking and delamination. An unusual offset-compression mode was observed for compressive bearing-bypass laoding in which the specimen failed across its width along a line offset from the hole. The computed lamina strains in the fiber direction were used in a combined analytical and experimental approach to predict bearing-bypass diagrams for damage onset from a few simple tests.

Naik, R. A.↗

NASA NTRS1988

Convergence of strain energy release rate components for edge-delaminated composite laminates

Strain energy release rates for edge delaminated composite laminates were obtained using quasi 3 dimensional finite element analysis. The problem of edge delamination at the -35/90 interfaces of an 8-ply composite laminate subjected to uniform axial strain was studied. The individual components of the strain energy release rates did not show convergence as the delamination tip elements were made smaller. In contrast, the total strain energy release rate converged and remained unchanged as the delamination tip elements were made smaller and agreed with that calculated using a classical laminated plate theory. The studies of the near field solutions for a delamination at an interface between two dissimilar isotropic or orthotropic plates showed that the imaginary part of the singularity is the cause of the nonconvergent behavior of the individual components. To evaluate the accuracy of the results, an 8-ply laminate with the delamination modeled in a thin resin layer, that exists between the -35 and 90 plies, was analyzed. Because the delamination exists in a homogeneous isotropic material, the oscillatory component of the singularity vanishes.

Raju, I. S.↗

NASA NTRS1988

Factors influencing elastic stresses in double cantilever beam specimens

An elastic stress analysis was conducted for a double cantilever beam (DCB) specimen using finite-element methods. The purpose of this study was to identify the important parameters that influence stresses ahead of the delamination front. The study focused on an aluminum DCB specimen, typical of adhesively-bonded joints, and on a graphite/epoxy specimen representing a cocured composite. Opening mode sigma sub y stresses ahead of the crack tip were calculated and compared with those for a monolithic reference specimen. Beyond the singularity-dominated region very near the crack tip, the sigma sub y distribution was elevated compared to the monolithic case. Both the adhesive thickness and the adherend transverse (thickness-direction) stiffness were found to influence the elevation of sigma sub y. In contrast, adherend thickness and longitudinal stiffness has very little effect on this stress distribution. Estimates for adhesive yielding beyond the aluminum DCB crack tip showed that both the area and height of the plastic zone increased to a peak value for increasing adhesive thicknesses. Results from this study would provide insight for comparing data from different DCB specimens and for designing new DCB specimens.

Crews, J. H., Jr.↗

NASA NTRS1987

Bearing-bypass loading on bolted composite joints

The effects of simultaneous bearing and bypass loading on a graphite-epoxy (T300/5208) laminate were investigated. Onset damage and ultimate strengths were determined for each test case. A finite element stress analysis was conducted for each test case. The computed local stresses were used with appropriate failure criteria to analyze the observed failure modes and strengths. An unexpected interaction of the effect of the bypass and bearing loads was found for the onset of compression reacted bearing damage. The interaction was caused by a decrease in the bolt-hole contact arc and a corresponding increase in the severity of the bearing loads. The amount of bolt-hole contact had a significant effect on local stresses and, thus, on the calculated damage-onset and ultimate strengths. An offset-compression failure mode was identified for laminate failure under compression bearing-bypass loading.

Crews, J. H., Jr.↗

NASA NTRS1987

Convergence of strain energy release rate components for edge-delaminated composite laminates

Raju, I. S.↗

NASA NTRS1987

Energy dissipation associated with crack extension in an elastic-plastic material

Crack extension in elastic-plastic material involves energy dissipation through the creation of new crack surfaces and additional yielding around the crack front. An analytical procedure, using a two-dimensional elastic-plastic finite element method, was developed to calculate the energy dissipation components during a quasi-static crack extension. The fracture of an isotropic compact specimen was numerically simulated using the critical crack-tip-opening-displacement (CTOD) growth criterion. Two specimen sizes were analyzed for three values of critical CTOD. Results from the analyses showed that the total energy dissipation rate consisted of three components: the crack separation energy rate, the plastic energy dissipation rate, and the residual strain energy rate. All three energy dissipation components and the total energy dissipation rate initially increased with crack extension and finally reached constant values.

Shivakumar, K. N.↗