Bearing-bypass loading on bolted composite joints

Abstract

The effects of simultaneous bearing and bypass loading on a graphite-epoxy (T300/5208) laminate were investigated. Onset damage and ultimate strengths were determined for each test case. A finite element stress analysis was conducted for each test case. The computed local stresses were used with appropriate failure criteria to analyze the observed failure modes and strengths. An unexpected interaction of the effect of the bypass and bearing loads was found for the onset of compression reacted bearing damage. The interaction was caused by a decrease in the bolt-hole contact arc and a corresponding increase in the severity of the bearing loads. The amount of bolt-hole contact had a significant effect on local stresses and, thus, on the calculated damage-onset and ultimate strengths. An offset-compression failure mode was identified for laminate failure under compression bearing-bypass loading.