FLiBe compatibility of fusion-relevant materials

There is current interest in a 2LiF-BeF2 (FLiBe) molten salt blanket for fusion applications, however, very little compatibility data are available for fusion relevant materials. Initial static capsule testing results for 500 h at 550°-750 °C are presented for V-4Cr-4Ti, Fe-8Cr-2W (alloy F82H) compared to type 316H stainless steel and monolithic SiC as a surrogate for SiC/SiC composites. In addition, sintered Be12Ti specimens with varying additions of Be (0–20%) and a Be2C specimen were exposed with F82H coupons at 650 °C in individual Mo capsules. The V-4Cr-4Ti and SiC specimens exposed at 650 °C had small mass changes. Steel specimens showed increasing mass losses with increasing exposure temperature. However, when Be12Ti-Be specimens were included in a capsule with an F82H coupon, increasing F82H mass gains were observed with increasing Be content due to the formation of a Fe-Be surface layer. No layer and no mass gain were observed for the F82H specimen tested with Be2C.

Pint, Bruce [Oak Ridge National Laboratory (ORNL) ↗

DOE OSTI2026

Impact of nitrogen on lithium-induced corrosion and cracking of RAFM steel

The emergence of private fusion enterprises, combined with advancements in U.S. and EU ITER-TBM as well as EU DEMO liquid breeder blanket concepts, has renewed focus on the materials challenges. This study examines the compatibility of reduced activation ferritic/martensitic (RAFM) steel in liquid Lithium (Li) containing various Nitrogen (N) concentrations, tested at 600 and 700 °C for 500 and 1000 h under static conditions. Microstructural characterization revealed the corrosion-induced dissolution and precipitation in Li containing 0.082 and 0.17 wt.% N at 600 °C, while limited dissolution and precipitation were observed in N-gettered Li using zirconium (Zr) and titanium (Ti) foils at 600 °C. Tensile testing at room temperature after Li exposure revealed a decrease in strength and ductility of the RAFM steel as a function of N content in Li. Severe embrittlement was observed after 500 h in Li containing 0.17 wt.% N at 600 °C and after 500 h in hot-gettered Li at 700 °C. Chromium (Cr) depletion from the steel matrix was observed, leading to the formation of M6C-type carbides on the surface identified by electron microscopy (SEM), X-ray diffraction (XRD), in agreement with thermodynamic calculations. These findings highlight the critical materials challenges posed by liquid Li breeder blanket concepts, emphasizing the need for improved strategies to address Li-induced dissolution, precipitation, and steel embrittlement due to N contamination of the coolant.

Romedenne, Marie [ORNL] (ORCID:0000000317936561)↗