FLiBe compatibility of fusion-relevant materials

Abstract

There is current interest in a 2LiF-BeF2 (FLiBe) molten salt blanket for fusion applications, however, very little compatibility data are available for fusion relevant materials. Initial static capsule testing results for 500 h at 550°-750 °C are presented for V-4Cr-4Ti, Fe-8Cr-2W (alloy F82H) compared to type 316H stainless steel and monolithic SiC as a surrogate for SiC/SiC composites. In addition, sintered Be12Ti specimens with varying additions of Be (0–20%) and a Be2C specimen were exposed with F82H coupons at 650 °C in individual Mo capsules. The V-4Cr-4Ti and SiC specimens exposed at 650 °C had small mass changes. Steel specimens showed increasing mass losses with increasing exposure temperature. However, when Be12Ti-Be specimens were included in a capsule with an F82H coupon, increasing F82H mass gains were observed with increasing Be content due to the formation of a Fe-Be surface layer. No layer and no mass gain were observed for the F82H specimen tested with Be2C.