Mechanical and thermal behavior of additively manufactured Invar 36 using a laser hot wire hybrid DED process

Invar 36 alloy is a material of high interest in the composite tooling sector due to its low coefficient of thermal expansion. Current production of Invar 36 tooling using traditional manufacturing such as casting and forging is associated with long lead times due to a multitude of factors such as labor and component shortages, high material costs, foreign competition, and supply chain issues. An attractive alternate process is the use of an integrated 5-axis CNC hybrid Laser Hot Wire Deposition System (LHWD) for manufacturing invar molds. Here, the hybrid process provides a combination of the additive and subtractive technologies resulting in a synergistic platform for producing and repairing structures and molds. The main novelty and goal of this work is to study the properties of Invar deposited by a LHWD and to provide guidelines for the manufacture of parts using this process. In this study, the thermal expansion behavior of the manufactured specimens has been analyzed and related to its printing parameters and direction. Multiple specimens were extracted for mechanical, dilatometry and metallographic testing. A thermal IR recording of the printing process was also carried out to observe the thermal history of the produced parts to establish thermal influence on performance-property-processing relationship. The results of these tests show the advantage of LHWD technology for the manufacture of Invar alloy parts, as it presents similar thermal expansion behavior as those commercially available with minimal presence of precipitates and no macrostructural failures such as pores, cracks and lacks of fusion.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Phase Selection During Solidification and Solid-State Phase Transformations in an Al-10Ce-8Mn (wt pct) Alloy

In multicomponent Al-Ce alloys, and especially after additive manufacturing (AM), complex and metastable solidification microstructures are frequently observed. Here, in this research, the relationship between solidification conditions and phase selection are explored for an Al-10Ce-8Mn (wt pct) alloy using a systematic study of laser melting conditions. Three solidification modes were observed: primary Al 10 Mn 2 Ce; primary Al 20 Mn 2 Ce; and eutectic FCC Al + Al 20 Mn 2 Ce. These solidification modes were correlated to specific liquid-solid interface velocities using a simple thermal model, showing the change in primary solidification phase for low (< 6.8 × 10 −4 m/s), moderate (between 8.2 × 10 −4 and 5.9 × 10 −2 m/s) and high solidification velocities (> 6.2 x 10 −2 m/s) for the above three solidification microstructures, respectively. These results were rationalized by using interface response function (IRF) theory to describe the solidification undercooling for the possible primary intermetallic phases. The implication of the local phase selection from differing solidification conditions is summarized by a comparison of hardness which demonstrates the potential variance of Vickers hardness from 101 to 242 (VHV) by changing the laser velocity from 1 to 83 mm/s. Interestingly, on heat treatment at 400°C, the decomposition pathways of the solidification microstructure and hardness were also found to be different, thereby opening multiple pathways for spatial microstructure and property control within AM components.

Sisco, Kevin↗
DOE OSTI2024

Process parameter translation strategies for variable directed energy deposition spot size using 316L, copper, and Inconel 625

Directed energy deposition (DED) is a form of additive manufacturing available across a variety of laser spot diameter values, often referred to as spot sizes. However, there is no method to easily transfer process parameters across discrete spot sizes, leading to DED process parameters that are equipment specific and not widely applicable. In this study, a strategy is proposed and investigated for five spot sizes that keep the areal energy density constant while varying power, feed rate, and powder flow during the deposition of 316L stainless steel. An assessment of trends in hardness and microstructure is possible due to the novel production of components of a single material across several spot sizes using a single nozzle on a single DED system. The proposed strategy was used to nullify the hardness drop during functional grading of Inconel 625 and pure copper, enabling fabrication of multi-material sample that does not compromise desirable properties. This application shows the value in establishing more efficient process parameter development and understanding spot size influences on geometric and material property flexibility, to enable a more diverse powder-based DED design space and to increase the industry adoption of DED systems.

316L↗
DOE OSTI2024

Influence of printing parameters on the mechanical behavior of 3D-printed SS316L parts manufactured using laser hot wire directed energy deposition

Hybrid manufacturing combines the simultaneous benefits of additive manufacturing (complex geometries, part consolidation, and mass customization) with the advantages of subtractive manufacturing (superior surface finish and enhanced dimensional accuracies) by integrating a suite of complementary traditional processes into a base platform of additive manufacturing. The use of hybrid technology has grown in recent years given its capabilities on repairing metallic structures, producing parts with conformal cooling features, and manufacturing functionally graded products. These kinds of capabilities are of great interest to the medical implant, energy, automotive, maritime, and aerospace industry sectors, among many other fields. This work investigated the mechanical properties of stainless steel (SS) 316L as a function of different tool paths strategies using an integrated 5-axis CNC hybrid Mazak system with a laser hot wire deposition system (LHWDS). This study includes the evaluation of different printing parameters and their impact on the quality of the printed bead as well as the incorporation of a structure–property material relationship based on the mechanical performance of the manufactured coupons.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Hybrid additive manufacturing of AISI 316L via asynchronous powder and hot-wire laser directed energy deposition

Hybrid Additive Manufacturing (AM) offers a way to leverage the advantages of different AM technologies, enabling the efficient production of sizeable parts without compromising material properties or geometric complexity capabilities. This study presents an asynchronous hybrid Directed Energy Deposition (DED) strategy employing laser powder DED and laser hot-wire DED. AISI 316L parts comprising multiple powder and wire segments were fabricated with optional machining on AISI 316L substrates to investigate how quality is impacted by (i) alternative process sequences (laser powder DED followed by laser hot-wire DED and vice versa), (ii) machined vs. as-printed interfacial conditions, and (iii) material deposition on top vs. alongside previously built segments. Optical microscopy, X-ray computed tomography, and Vickers hardness were used to characterize the morphology and microstructure of the parts, localized porosity and lack of fusion defects, bulk density, and mechanical properties. Interfacial machining was necessary for dimensional control but promoted lack of fusion voids, resulting in a 99.71 ± 0.01% dense part. As-printed interfaces resulted in a denser part (99.82 ± 0.02%) at the expense of dimensional accuracy. The hardness of the parts with as-printed and machined interfaces was 196 ± 0.37 HV and 192 ± 0.40 HV, respectively, compared to 156 ± 1.4 HV for the substrate. Depositing powder alongside or on top of wire sections resulted in interfaces with a hardness of 217 ± 2.2 HV, compared to 185 ± 3.4 HV for the wire-powder interfaces.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Hybrid metal additive/subtractive machine tools and applications

Additive manufacturing creates parts by depositing a preform, typically layer by layer. Subtractive manufacturing involves removing material from a preform to create parts. Hybrid machine tools combine both additive and subtractive processes in the same workspace. They can be used to create parts that meet functional tolerance and surface finish requirements, or to create features that are difficult to produce using additive or subtractive processes alone. Here, this paper describes hybrid metal additive/subtractive machine tools. It covers design considerations, sensors and controls, process management, programming and software, and the impact on the design space. It also identifies future research challenges.

42 ENGINEERING↗