Process parameter translation strategies for variable directed energy deposition spot size using 316L, copper, and Inconel 625

Fillingim, Kenton B.; Kannan, Rangasayee; Heinrich, Lauren; Saleeby, Kyle; Nandwana, Peeyush; Feldhausen, Thomas

doi:10.1016/j.heliyon.2024.e37658

Home/Archive/DOE OSTI

DOE OSTI · 2448200

Process parameter translation strategies for variable directed energy deposition spot size using 316L, copper, and Inconel 625

Fillingim, Kenton B.·Kannan, Rangasayee·Heinrich, Lauren·Saleeby, Kyle·Nandwana, Peeyush·Feldhausen, Thomas

View original source ↗Read source document ↗Export metadata ↓

Abstract

Directed energy deposition (DED) is a form of additive manufacturing available across a variety of laser spot diameter values, often referred to as spot sizes. However, there is no method to easily transfer process parameters across discrete spot sizes, leading to DED process parameters that are equipment specific and not widely applicable. In this study, a strategy is proposed and investigated for five spot sizes that keep the areal energy density constant while varying power, feed rate, and powder flow during the deposition of 316L stainless steel. An assessment of trends in hardness and microstructure is possible due to the novel production of components of a single material across several spot sizes using a single nozzle on a single DED system. The proposed strategy was used to nullify the hardness drop during functional grading of Inconel 625 and pure copper, enabling fabrication of multi-material sample that does not compromise desirable properties. This application shows the value in establishing more efficient process parameter development and understanding spot size influences on geometric and material property flexibility, to enable a more diverse powder-based DED design space and to increase the industry adoption of DED systems.

Explore related subjects

316L 36 MATERIALS SCIENCE Copper Directed energy deposition Inconel 625 Laser spot size

Keep this discovery

Explore connections, maps & timelines

BibTeX RIS

Fillingim, Kenton B., Kannan, Rangasayee, Heinrich, Lauren, Saleeby, Kyle, Nandwana, Peeyush, Feldhausen, Thomas. 2024-09-07. Process parameter translation strategies for variable directed energy deposition spot size using 316L, copper, and Inconel 625. https://doi.org/10.1016/j.heliyon.2024.e37658

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

DOE OSTI2023

Evaluation of printability methodologies and feasibility to down select LBPF steel and other materials for nuclear applications

In this work, new research is underway to produce alloys beyond well-known alloys with modified compositions that are better suited to be produced with additive manufacturing. These alloys can only possess improved radiation tolerance but also improved high temperature strength, creep resistance while also using elements that reduce the amount of activation after irradiation. This work package supports the vision and goals of the Advanced Materials and Manufacturing Technology (AMMT) program relevant to accelerate the development and deployment of advanced manufacturing processes. This work focuses on evaluating the methodology for designing alloys best suited for AM processes based on “printability”, literature research to evaluate and down select steel alloy systems. In this work, microstructural characterization and testing activities have been performed on certain steel alloys to support the efforts from collaborating laboratories during the evaluation and printing of the test articles. The final recommendation will be performed by all four participating laboratories.

316L↗

DOE OSTI2023

On the melt pool dynamic of voxel-controlled metal matrix composites via hybrid additive manufacturing: Laser powder bed fusion and ink-jetting

In this study, the effect of the addition of reinforcement nanoparticles to the 316L matrix by adopting ex-situ and in-situ method (drop on demand jetting) to produce 316L/Al 2 O 3 nanocomposite was investigated. In the ex-situ method, the Al 2 O 3 nanoparticles (NPs) were lightly mixed with 316L powder and processed by laser powder bed fusion. In the in-situ method, an ethanol-based ink containing Al 13 nanoclusters (NCs) was added to 316L powder and then processed by laser. Both ex-situ and in-situ method produced nanocomposites with Al-Si-Mn-O-enriched precipitations within the 316L matrix. The addition of NPs/NCs to the 316L matrix, altered the geometrical characteristic of the single-track melt pools. At the same laser power, with increasing the amount of Al 2 O 3 NPs and Al 13 NCs the melt pool deepened due to reduced thermal conductivity and prolonged liquid presence. Further, as a result, 316L/1 wt% Al 13 NCs deposited single track showed larger grains in comparison to 316L single track. At a high laser power of 150W, the Marangoni flow and the buoyancy force caused the nanoparticles to agglomerate and float to the top surface of tracks; therefore, the wt% fraction of precipitation was drastically reduced due to the loss of Al. The 316L/Al 2 O 3 NPs and 316L/Al 13 NCs exhibited the microhardness of 285 ± 13 HV and 293 ± 7 HV, respectively, higher than the deposited 316L single track, 265 ± 15 HV. Lastly, a hybrid LPBF+ink-jet printer was adopted to selectively change the composition of different zones by adding Al 13 NCs ink to 316L and producing a voxel-controlled metal matrix composite.

316L↗