DOE OSTI2025

An Additively Manufactured Fe-3Si Stator for a High-Performance Electrical Motor

Additive manufacturing (AM) has the potential to produce novel high-performance electrical machines, enabling the direct printing of complex shapes and the simultaneous processing of multiple feedstocks in a single build. We examined the properties and functional performance of Fe-3 wt.% Si materials that were printed via selective laser melting, machined down to thin laminates, and stacked to form a stator core of a prototype brushless permanent-magnet electrical motor. Big Area Additive Manufacturing of Nd2Fe14B (NdFeB)–polyphenylene sulfide (PPS) bonded magnets was performed, with them then being magnetized and used for the rotor. The magnetic, mechanical, and electrical properties of the as-printed and various heat-treated thin laminates and the back electromotive force (EMF) of the electrical motors at different rotational speeds were measured. The thin laminates exhibit a maximum relative permeability of 7494 at an applied field of 0.8 Oe and a core loss of about 20 W/lb at 60 Hz with the maximum induction of 15 kg. In addition to the demonstration of AM printing, motor assembly, and complete characterization of printed Fe-3 wt.% Si, this report highlights the areas of improvement needed in printing technologies to achieve AM built electrical motors and the need for isotropic microstructure refinements to make the laminates appropriate for high-mechanical-strength and low-loss rotational electrical devices.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Integrated top-down process and voxel-based microstructure modeling for Ti-6Al-4V in laser wire direct energy deposition process

Laser-wire metal additive manufacturing (AM) is one of the ideal direct energy deposition (DED) processes for creating large-scale parts with a medium level of complexity. However, the DED process involves complex thermal signatures and wide length scales making the fabrication of realistic AM components and part qualification often reliant on experimental trial-and-error optimization. While experimental measurements over the full volume of a part are valuable and necessary, measuring the entire area of a part is significantly laborious and practically infeasible, particularly for large parts in terms of cost and rapid qualification. Therefore, in this work, we developed an effective thermal and microstructure modeling framework based on the Johnson–Mehl-Avrami-Kolmogorov (JMAK) and Koistinen & Marburger (KM) models through a top-down approach that considers plate distortion-affected thermal profiles. A voxel-by-voxel simulation method is used to predict individual phase fractions of Ti-6Al-4 V. The predicted results were validated through detailed metallurgical measurements. A combined voxel-by-voxel approach with a sparse data reconstruction technique produced a near-perfect reconstruction of the original data. This approach anticipates a significant reduction in data points and computation time and resources. Lastly, we conclude with potential extensions of this work to other modeling efforts.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Denoising diffusion probabilistic models for generative alloy design

Inverse material design is an extremely challenging optimization task made difficult by, in part, the highly nonlinear relationship linking performance with composition. Quantitative approaches have improved significantly owing to advances in high throughput experimentation and computational thermodynamics. However, existing physics-based tools are mostly forward models; input a chemistry and obtain a prediction. More recently the materials community has leveraged advances in the machine learning community to establish novel inverse design frameworks. Very recently denoising diffusion probabilistic models have been shown to be extremely powerful generators producing synthetic data of various modalities e.g. images, text, audio, tables, etc.. In this work a novel framework for alloy design and optimization is proposed leveraging these class of models. Five key generative tasks are demonstrated (1) unconditional generation (2) composition conditioned generation (3) property conditioned generation (4) multi-feedstock conditioned generation and (5) generative optimization. These methods were tested on three case studies: high entropy alloy design, superalloy binder jet additive manufacturing, and in-situ dual-feedstock wire-arc additive manufacturing. Results indicate that the established models are extremely flexible, expressive, and robust. The architecture’s flexibility and training procedure empower the model to learn complex intra-compositional and composition-property relationships. Furthermore, the probabilistic nature of these models makes them well suited for addressing solution non-uniqueness and tackling uncertainty quantification tasks. While the fidelity and quantity of the underlying training data is paramount, we envision that future alloy design frameworks will make extensive use of these kinds of machine learning models as “search” tools bolstering the utility of experimental and computational approaches.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Controlling microstructure and B2 ordering kinetics in Fe–Al system through additive manufacturing

Multi-material fabrication between steel and aluminum is challenging because of the formation of several intermetallic phases. Embrittling B2 ordered intermetallics form in the steel rich side and are stable till about 60% of Al dilution in steel. In this work by using multi-length scale characterization coupled with integrated computational process and thermokinetic modeling, we show that the ordered B2 intermetallics in the steel rich side of the Fe–Al system forms via a nucleation and growth mechanism. The extent of B2 ordered intermetallics can be controlled by modifying the directed energy deposition-additive manufacturing (DED-AM) process parameters. Our findings lay the foundation for enabling fabrication of crack-free functionally graded compositions between the two alloys.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Process parameter translation strategies for variable directed energy deposition spot size using 316L, copper, and Inconel 625

Directed energy deposition (DED) is a form of additive manufacturing available across a variety of laser spot diameter values, often referred to as spot sizes. However, there is no method to easily transfer process parameters across discrete spot sizes, leading to DED process parameters that are equipment specific and not widely applicable. In this study, a strategy is proposed and investigated for five spot sizes that keep the areal energy density constant while varying power, feed rate, and powder flow during the deposition of 316L stainless steel. An assessment of trends in hardness and microstructure is possible due to the novel production of components of a single material across several spot sizes using a single nozzle on a single DED system. The proposed strategy was used to nullify the hardness drop during functional grading of Inconel 625 and pure copper, enabling fabrication of multi-material sample that does not compromise desirable properties. This application shows the value in establishing more efficient process parameter development and understanding spot size influences on geometric and material property flexibility, to enable a more diverse powder-based DED design space and to increase the industry adoption of DED systems.

316L↗
DOE OSTI2024

Process–Property–Performance Mapping of Additively Manufactured 316H Stainless Steel Components

The Advanced Materials and Manufacturing Technologies Program is focused on accelerating the development of advanced materials and components fabricated via additive manufacturing, and is using laser powder bed fusion (LPBF) of 316H stainless steel as an initial case study. In the previous fiscal year, miniature high-throughput specimens were printed on multiple LPBF systems to provide initial processing windows to minimize porosity and limit epitaxial grain growth during prints. This fiscal year, scaled builds were completed on three different LPBF systems at ORNL: a GE Concept Laser M2, a Renishaw AM400, and an EOS M290. Builds on the Concept Laser were conducted on multiple powder lots and processing parameter ranges to provide microstructure effects on time-independent and time-dependent mechanical properties. Builds on the Renishaw were produced using Oak Ridge National Laboratory (ORNL)-optimized printing parameters and Argonne National Laboratory (ANL)-optimized printing parameters to compare outcomes of parallel process optimization efforts at different national laboratories on the same LPBF system. Similarly, the build completed on the EOS M290 replicated the processing parameters of builds completed at Los Alamos National Laboratory (LANL). Optical microscopy and electron backscatter diffraction characterization was completed on all builds. In addition to the general round robin characterization, this work-package generated time-independent data, including tensile and fracture toughness test data on scaled Concept Laser builds as a function of processing parameters and post-build heat treatment. This analysis is complimentary to work in parallel work packages aiming to establish heat treatment and processing effects on time-dependent properties. It was found that although the stress-relief heat treatment provides the highest strength at lower-temperatures, tensile strength begins to converge at higher temperatures regardless of heat treatment condition. In addition, the more rigorous solution annealing and hot-isostatic pressing post-build heat treatments result in higher fracture toughness than the stress-relieved condition. The root-causes of the lower fracture toughness of the stress-relieved LPBF 316H material was informed via a stress-relief optimization study on a scaled concept laser print, where it was found that although dislocation recovery was largely complete after only a couple hours at 650°C, the extended hold of the current 24h heat treatment employed on scaled builds likely caused increased carbide volume fractions along the LPBF 316H grain boundaries, thereby deteriorating crack propagation resistance. This trend was seen to become more deleterious with additional increases of stress-relief temperature to 750°C or 850°C. These results have helped inform a new optimal stress-relief annealing condition for LPBF 316H for future campaign testing (650°C for 2h).

36 MATERIALS SCIENCE↗
DOE OSTI2024

Process–Property–Performance Mapping of Additively Manufactured 316H Stainless Steel Components

The Advanced Materials and Manufacturing Technologies Program is focused on accelerating the development of advanced materials and components fabricated via additive manufacturing, and is using laser powder bed fusion (LPBF) of 316H stainless steel as an initial case study. In the previous fiscal year, miniature high-throughput specimens were printed on multiple LPBF systems to provide initial processing windows to minimize porosity and limit epitaxial grain growth during prints. This fiscal year, scaled builds were completed on three different LPBF systems at ORNL: a GE Concept Laser M2, a Renishaw AM400, and an EOS M290. Builds on the Concept Laser were conducted on multiple powder lots and processing parameter ranges to provide microstructure effects on time-independent and time-dependent mechanical properties. Builds on the Renishaw were produced using Oak Ridge National Laboratory (ORNL)-optimized printing parameters and Argonne National Laboratory (ANL)-optimized printing parameters to compare outcomes of parallel process optimization efforts at different national laboratories on the same LPBF system. Similarly, the build completed on the EOS M290 replicated the processing parameters of builds completed at Los Alamos National Laboratory (LANL). Optical microscopy and electron backscatter diffraction characterization was completed on all builds. In addition to the general round robin characterization, this work-package generated time-independent data, including tensile and fracture toughness test data on scaled Concept Laser builds as a function of processing parameters and post-build heat treatment. This analysis is complimentary to work in parallel work packages aiming to establish heat treatment and processing effects on time-dependent properties. It was found that although the stress-relief heat treatment provides the highest strength at lower-temperatures, tensile strength begins to converge at higher temperatures regardless of heat treatment condition. In addition, the more rigorous solution annealing and hot-isostatic pressing post-build heat treatments result in higher fracture toughness than the stress-relieved condition. The root-causes of the lower fracture toughness of the stress-relieved LPBF 316H material was informed via a stress-relief optimization study on a scaled concept laser print, where it was found that although dislocation recovery was largely complete after only a couple hours at 650°C, the extended hold of the current 24h heat treatment employed on scaled builds likely caused increased carbide volume fractions along the LPBF 316H grain boundaries, thereby deteriorating crack propagation resistance. This trend was seen to become more deleterious with additional increases of stress-relief temperature to 750°C or 850°C. These results have helped inform a new optimal stress-relief annealing condition for LPBF 316H for future campaign testing (650°C for 2h).

36 MATERIALS SCIENCE↗
DOE OSTI2024

Design optimization of lightweight automotive seatback through additive manufacturing compression overmolding of metal polymer composites

With the growing demand for enhanced automotive fuel efficiency and environmental sustainability, there is a need for lightweighting automotive components through innovative design and manufacturing processes. Here, this study leverages a combination of numerical iterative design optimization and hybrid additive manufacturing–compression molding (AM-CM) technique for metal polymer composites to lightweight an automotive seatback. The AM-CM process enables robust mechanical interlocking between metals and composites, boasting high stiffness and strength with low overall density. Replacing metallic components with such metal polymer composites allows for comparable mechanical performance while significantly reducing the overall weight. First, the automotive seatback design space is reduced to critical load carrying regions using topology optimization and high stress concentration areas are identified using finite element analysis. Next, a lightweight metal polymer subcomponent is designed for a high stress concentration region. The full seatback frame with spatially heterogeneous material-specific design is then iteratively optimized to enable enhanced stiffness with minimal weight. Overall, the automotive seatback frame designed with location-specific metal, polymer, and metal polymer composite materials weighs 20% less than the metal-only design while exhibiting similar stiffness.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Red Mud: From Industrial Waste to a Flux for Manufacturing Sustainable Iron/Steel

Here, this study highlights the potential of red mud/bauxite residue, an industrial waste product generated during alumina extraction as a flux for iron and steelmaking. The thermodynamic feasibility of using red mud as a flux in the presence of different reducing agents is evaluated. Potential approaches to decarbonize iron and steel production while utilizing red mud as a flux, as well as the benefits of red mud remnant after iron extraction, are discussed.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Indirect additive manufacturing process for fabricating bonded soft magnets

A bonded soft magnet object comprising bonded soft magnetic particles of an iron-containing alloy having a soft magnet characteristic, wherein the bonded soft magnetic particles have a particle size of at least 200 nm and up to 100 microns. Also described herein is a method for producing the bonded soft magnet by indirect additive manufacturing (IAM), such as by: (i) producing a soft magnet preform by bonding soft magnetic particles with an organic binder, wherein the magnetic particles have an iron-containing alloy composition with a soft magnet characteristic, and wherein the particles of the soft magnet material have a particle size of at least 200 nm and up to 100 microns; (ii) subjecting the preform to an elevated temperature sufficient to remove the organic binder to produce a binder-free preform; and (iii) sintering the binder-free preform at a further elevated temperature to produce the bonded soft magnet.

Paranthaman, Mariappan Parans↗
DOE OSTI2024

PredSiD

This tool can be deployed to an end user and they do not need to have access to the thermodynamic database to use the tool. The tool will enable the end user to plug in the composition and sintering process variables and estimate delta phase fraction.

Kannan, Rangasayee↗
DOE OSTI2024

Microstructure manipulation via machining and heat treatments in hybrid manufacturing of 316L stainless steel

Hybrid manufacturing combines additive and subtractive (machining) processes in a single platform to reduce the total time to fabricate a component in its final form. Here we show that if sufficient plastic deformation can be imparted to the material during machining, recrystallization can be triggered during post-fabrication heat treatment. This can enable highly localized microstructure control. Additionally, we show that stainless steel 316L, when machined without coolant accumulates significant plastic strain compared to when machined with coolant that results in faster recrystallization kinetics during heat treatment. These effects are limited to the surface while the bulk microstructure remains unaffected.

316L stainless steel↗
DOE OSTI2024

Reduction kinetics of hematite powder using argon/hydrogen plasma with prospects for near net shaping of sustainable iron

Direct reduction of iron ore using hydrogen plasma is being explored as a potential solution to decarbonize the iron and steel sector. The current state-of-the-art demonstrated reduction of hematite pellets via hydrogen plasma using Ar + 10% H 2 but had slow reduction kinetics, requiring 30 minutes of plasma exposure for complete reduction. Here we show that using hematite in a powder form, easily obtainable from beneficiated ore, results in 10× faster kinetics using plasma generated from Ar + 2% H 2 shielding gas compared to the current state-of-the art. Additionally, the increased kinetics using powders and a dilute hydrogen concentration can enable the use of advanced manufacturing techniques like blown powder directed energy deposition using a plasma tungsten arc welding torch to manufacture near net shape components directly from the ore concentrates. This ore to part approach will also reduce the emissions associated with downstream processes like rolling, forging, and machining, thereby further aiding in the sectorial decarbonization efforts.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Wire directed energy deposition of steel-aluminum structures using cold metal transfer process

In this study, a sharp transition from 316L stainless steel to 4043 aluminum alloy was fabricated using wire directed energy deposition (DED) via the cold metal transfer (CMT) process. The CMT process with its inherently low heat input, led to a significant reduction in intermetallic thickness at the bi-metallic interface compared to blown powder DED technique reported in the literature resulting in superior properties when compared to those of dissimilar steel-aluminum welds. Thermo-kinetic modeling confirmed that the intermetallic formation is through a classical nucleation and growth mechanism, and the fraction and thickness can be controlled by adjusting CMT process parameters to kinetically arrest or minimize the intermetallic formation. These findings underscore the efficacy of CMT-based wire DED for fabrication of steel-aluminum bi-metallic structures.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Investigating stainless steel/aluminum bimetallic structures fabricated by cold metal transfer (CMT)-based wire-arc directed energy deposition

Here, this study investigated the process of fabricating a bimetallic structure of 316L stainless steel (SS) and 4043 aluminum (Al) using wire-arc directed energy deposition (DED) based on the cold metal transfer (CMT) process. The impact of heat input on the fabricated structure’s geometry, porosity, and microstructures at the interface, with a specific emphasis on the intermetallic compound (IMC) formation, and the subsequent impact on the joint strength of the structure, were studied. The IMC layer at the interface was predominantly comprised of FeAl 2 Si. For the various heat input conditions studied, the IMC layer's thickness varied from 5 µm to 18 µm. The tensile strength reached up to approximately 130 MPa, which is among the highest reported in the literature for steel/Al bimetallic structures. The specimens fabricated with high heat input conditions had a thicker IMC layer at the steel/Al interface, resulting in a more brittle interface and degradation of the mechanical properties.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Exploration of Binder Jet Additive Manufacturing for Automotive Heat Sink Component Fabrication

ORNL (Contractor) and Magna Services of America Inc. (Participant) collaborated to determine the feasibility of binder jet additive manufacturing (BJAM) for the fabrication of copper components for automotive heat sink applications. This Phase 1 collaboration focused on printing copper heat sinks that rely on capillary effect to move fluids rather than mechanical pumps in electric vehicles to extend the battery range and life. Partial sintering of copper powders deposited via BJAM was hypothesized to aid capillary effect to improve the heat transfer. Further, BJAM offers the potential for scalability at a production level.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Predictive binder jet additive manufacturing enabled by clean burn-off binder design

Binder jet additive manufacturing (BJAM) presents an avenue for advanced manufacturing of various high-value materials due to high deposition rates, scalability, and geometric flexibility. However, conventional organic binders in BJAM introduce residual carbon upon pyrolysis, often leading to imprecise alloy composition in the final sintered part. The undesirable residual carbon from binder burn-off limits the application of BJAM for high-performance alloys due to their high sensitivity to carbon addition. In this study, we have designed poly(vinylpyrrolidone-co-vinyl acetate) (PVP-VAc) as a clean burn-off binder for BJAM, where excess oxygen groups in VAc enable cleaner burn-off and reduce residual carbon retention. Compared to a widely used commercial binder, the optimized PVP-VAc binder reduced residual carbon retention by over 90% in H13 tool steel. The significant reduction in residual carbon enables predictable printing and subsequent sintering of complex H13 tool steel geometries, an alloy known to have substantial challenges around distortion due to the sintering window shifting from carbon addition. The design of a clean burnout binder provides a major path forward for BJAM by enabling new AM designs and applications for composition-sensitive high-performance alloys, such as nickel-based superalloys, titanium alloys, and high alloyed steels.

36 MATERIALS SCIENCE↗