DOE OSTI2024

FY24 Progress Report: Disposition of Cracks & Features Observed in the Inner Can Closure Weld Region (ICCWR) of the 3013 Package

The long-term integrity of the 3013 containers is of interest for the safe storage of Pu materials. Although the 3013 standard embodies multiple barrier concept, the integrity of the inner container is considered to be crucial since it protects the Safety Class outer container from its contents. The container is designed to withstand high pressures that could result from the complete radiolysis of the maximum water content permissible by the 3013 standard. Shelf-life studies and destructive examination have not found high gas pressures but have found that corrosive gases are generated. Pitting and stress corrosion cracking (SCC) are considered to be critical corrosion modes for the performance of the inner container and have been observed during destructive examinations. Considerable research has been conducted on the possibility of aqueous electrolytes condensing on the inner container that can promote SCC. These studies indicate the uncertainties surrounding the formation of corrosive environments and the corrosion behavior of container materials. In this initial report, a Bayesian network (BN) model is described that can consider the uncertainties and the causal connections between various factors influencing the corrosion modes of the inner container. The BN model is preliminary and provides an initial framework to identify the necessary information. The report also provides initial experimental results on the electrochemical behavior of stainless steels in anticipated condensed environments from gas phase migration of acidic gases. The experimental results are consistent with the corrosion model. Recommendation for further work on the BN model include assembling an expert group to provide input to the BN structure and quantification of the conditional probability matrix, experimental studies to characterize the microstructure of the container, electrochemical studies to identify critical potentials for localized corrosion and SCC, and crack growth rate studies

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗

DOE OSTI2024

Characterization of Stress-Corrosion-Cracking in Plutonium-Bearing Storage Containers

Introduction • The Integrated Surveillance Program, under the Department of Energy, is responsible for the periodic surveillance of storage containers containing plutonium-bearing materials. • The container-packages are designed to isolate the materials for 50 to 100 years with minimal surveillance. • During monitoring, corrosion-pitting and stress-corrosion-cracking (SCC) has been identified in some of the inner-cans near the weld regions. • SCC through wall penetration would result in an undesired increased risk of leakage. • An investigation is in progress to identify and characterize corrosion events to determine the prevalence of corrosion features and the likelihood of a throughwall breach. • Here, we discuss the characterization efforts carried out by Scanning Electron Microscopy (SEM), including 3D-tomography by Focused Ion Beam (FIB) methods.

Perez, Emmanuel E.↗

DOE OSTI2024

Bench-Scale Electrolytic Dissolution of Quarter-Scale FCA Cans

In 2016, the Savannah River National Laboratory (SRNL) led, in support of and under sponsorship of the Department of Energy’s National Nuclear Security Administration (DOE/NNSA) Office of Material Management and Minimization (M3), the removal and transfer of the plutonium based Fast Critical Assembly (FCA) fuel from the Japan Atomic Energy Agency (JAEA) Tokai facility to the Savannah River Site (SRS). The team also included JAEA, multiple organizations in Savannah River Nuclear Solutions (SRNS), International Nuclear Services, and many other entities. The FCA fuel removal project completion was a key deliverable for M3 to the 2016 Nuclear Security Summit and constituted the largest inventory of weapons-usable plutonium removed under the nonproliferation program. The FCA materials consist of thousands of stainless steel (SS) clad plates and hundreds of SS clad rods. The FCA fuel elements were packaged in a carrier can and stored at SRS pending disposition of the fuel. Following an assessment of candidate disposition options, SRNS identified electrolytic dissolution (ED) as the most promising disposition option for the FCA plates and their preferred option was endorsed by DOE. This option entails electrochemically dissolving the entire FCA carrier can with fuel elements and was based on bench-scale laboratory testing and historical work on processing SS-clad and zirconium-clad uranium-based fuel in the H-Canyon electrolytic dissolver (last operated in 1980). The FCA plate consists of a plutonium-aluminum metal alloy core hermitically sealed in SS cladding.

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗

DOE OSTI2024

Destructive Examination Protocol for 3013-Container-Package Storing Plutonium-Bearing Materials

The 3013-container-package consists of a convenience, inner and outer container and is used for long-term storage of plutonium-bearing materials. A destructive examination (DE) protocol has been developed to examine the container package visually and with microscopic aid to find any corrosion conditions that could result in the loss of the integrity of the container package over its lifetime. The DE protocol contains three main steps: initial container examination, helium (He) leak testing, and detailed imaging and analysis of the inner container closure weld region (ICCWR). The ICCWR has been determined to be bounding, defined as exhibiting worst case conditions for stress corrosion cracking (SCC) of the inner container. To assess SCC in the ICCWR, the inner container lid is cut into quarters and the weld and He-leak testing gasket are removed. Then a citric acid wash is performed to remove adherent chlorides from the ICCWR. The wash is then sent for analysis to determine the concentration of chlorides in the ICCWR. While the analysis for chloride concentration is being performed, the quarter sections are further sectioned into 1/8th subsections by cutting each section in half. These subsections are washed using nitric acid to remove corrosion products. Then each subsection is imaged using a Wide Angle 3-D Measurement System (WAMS). After analysis of microscope images for potential SCC, additional imaging can be performed, including subsurface imaging. After review, a determination is made of whether the container integrity may potentially affect the safe storage of the material.

container↗

DOE OSTI2024

He Leak Testing of 3013 Inner Container Lids

The 3013-container package is used for the long-term storage of plutonium bearing materials at Department of Energy (DOE) sites. The package consists of three nested stainless-steel containers: outer, inner and convenience, which are made of stainless steel. The requirements of the DOE 3013 Standarda, also entail the development of a surveillance program, tasked to ensure structural integrity of the outer container for at least 50 years. The Materials Identification and Surveillance Working Group (MIS-WG) is specified to be responsible for selecting the containers for the surveillance as well as analyzing results. The MIS-WG determined that corrosion is a potential mechanism for container degradation with the most credible type of failure to be stress corrosion cracking (SCC) through wall breach of the inner container closure weld region (ICCWR). A breach of the inner container has the potential of allowing corrosive gases to be released into the safety class outer container.

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗

DOE OSTI2024

Effect of Drying on Corrosion Mitigation of Hanford Transfer Lines

Radioactive waste is stored in underground, carbon-steel double-shell tanks at the Department of Energy Hanford site. The waste is transferred between the tanks and other assets using the transfer lines spanning throughout the various tank farms at Hanford. The transfer lines consist of a pipe-in-pipe design, small diameter pipes, and are not piggable. Recent inspection data of the transfer lines have shown areas with corrosion on both interior of the encasements and exterior of the primary pipes, with nearly 50 percent wall loss on the primary pipes and nearly 25% wall loss on the encasement pipes due to pitting corrosion. The visual inspections of the transfer lines have shown presence of corrosion products near the pipeline risers and beyond. It has been hypothesized that the corrosion is predominantly due to the high humidity conditions and in some cases is driven by the presence of residual hydrotest water in the encasement and the associated contact with the safety significant primary pipe. Therefore, drying of the transfer lines could lead to corrosion mitigation. Experimental studies are being conducted to understand the effect of environmental conditions, especially, relative humidity and temperature, on transfer line grade carbon steel corrosion and on mitigating corrosion. The experimental conditions are selected based on the seasonal temperature changes, and relative humidity conditions ranging from 30 to 100 percent. The experimental data will be used as guidance for maintaining a dry environment that will help mitigate the transfer-line corrosion caused by the high humidity conditions.

Shukla, Pavan K.↗

DOE OSTI2024

Effectiveness of Vapor Corrosion Inhibitors Under Elevated Chloride Conditions for Aboveground Storage Tank Application

The sand quality used to construct the tank pad is an important contributing factor to the rate of corrosion that occurs on the soil-side of the aboveground storage tanks (ASTs) floor plates. Clean sand that meets specific criteria provides the first line of defense for mitigation of tank floor corrosion. However, it has been observed that the sand quality used for some existing tanks differ greatly from the specifications provided in the API 651 standard; this could be partially due to initial sand quality not meeting the specification, and partially due to the environmental effects over time. For example, rain-water intrusion could lead to higher than the specified contents of corrosive species such as chloride. Tank operators are increasingly using vapor corrosion inhibitors (VCIs) either as a stand alone or in combination with cathodic protection (CP) for ASTs to mitigate soil-side corrosion. VCIs are delivered either through-thefloor or injected through the ports in the ring wall. Experimental studies were conducted to evaluate VCIs’ performance at elevated chloride concentrations and to study the effectiveness of the delivery methods under extreme chloride conditions. The experimental work found that VCI performance is robust and not compromised due to high chloride levels, such as 300 ppm or more. The work also showed that the through-the-floor VCI delivery method is more beneficial compared to the through-the-sand-pad method when tank pad corrosivity is elevated.

Shukla, Pavan K.↗

DOE OSTI2024

Effectiveness of Vapor Corrosion Inhibitors Under Bacterial Activity for Aboveground Storage Tank Application

Bacterial activity is known to influence corrosion and can result in increasing soil-side corrosion of the aboveground storage tanks (ASTs) floor plates. Association for Materials Protection and Performance (AMPP) defines this phenomenon as Microbiologically Influenced Corrosion (MIC). It has been hypothesized that vapor corrosion inhibitors (VCIs) can not only function in presence of bacterial activity but can also function as biocides. Experiments were conducted to study the effect of bacterial activity on corrosion in the sand pad conditions and effect of VCIs in mitigating MIC. Various bacteria cultures were grown using commercially available culture media, and coupon exposure tests were performed with field sand mixed with the culture media. To this end, control and VCI-dosed electrolytes were prepared using the field sand plus bacteria cultures. Pre- and post-test bacteria concentration estimation and measurements, respectively, in the VCI-dosed electrolytes indicated that VCIs do not function as biocides, however, VCIs are highly effective for mitigating corrosion in presence of bacterial activity.

Shukla, Pavan K.↗

DOE OSTI2023

Hanford Double Shell Waste Tank Corrosion Studies (Final Report)

For fiscal year (FY) 2022, the Savannah River National Laboratory (SRNL) focused on two experimental tasks related to Hanford Double Shell Tank (DST) chemistry and integrity. The first task focused on understanding risk of corrosion due to formation of either continuous layers or discrete patches of solids on the tanks' inner sidewalls and bottoms. The tank bottom solids contact corrosion testing focused on studying the effects of forming a dry adherent solids layer on a carbon steel substrate. Long-term exposure tests and electrochemical tests were performed to investigate the effect of drying (i.e., removing water) from the solids phase. The second task focused on corrosion of the exterior of the secondary liner. In previous years, vapor corrosion inhibitors (VCIs) were investigated as a means of mitigating corrosion of the exterior of the secondary liner. During FY22 the utilization of nitrogen was explored as a means of corrosion mitigation. The corrosion test results with nitrogen were compared with the corrosion mitigation performance of the VCIs.

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗

DOE OSTI2021

FY21 Progress Report: SRNL Analysis of ICCWR LCM and WAMS data for Corrosion and Cracking

The development of algorithms for machine learning and data analysis for the 3013 Surveillance Program is a collaborative effort by the Savannah River National Laboratory (SRNL) and the University of South Carolina (USC). For corrosion detection, Laser Confocal Microscope (LCM) or Wide Area 3D Measurement System (WAMS) data is extracted from large binary files, with software written to convert the data to physical attributes (e.g., height, color and grayscale values; all as functions of a location in a plane projection). A user-friendly Matlab Graphical User Interface (GUI) that reads data from either LCM or WAMS files was developed to integrate input data with software developed for processing and evaluation. The GUI can selectively download binary data, interrogate data attributes, label data, flag significant features, execute Machine Learning (ML) algorithms, output parameters for trained ML algorithms, report ML model accuracy with respect to labeled data, and generate graphical representations for various analyses. Features can be called out by user-specified thresholds, manual labeling or machine learning algorithms when they have been completed. The ability to rapidly label data is important because of the volume of data required for training machine learning algorithms. The GUI has the flexibility to allow addition of improved ML algorithms, methods for data visualization, and statistical computations. Statistical analyses via the GUI include areas of pits within a defined range of pit depths, correlations between Red-Green-Blue (RGB) or grayscale intensity and relative surface height, covariances between values associated with features, and feature histograms. The development of supervised machine learning algorithms, however, has been hindered by a lack of training data. The machine learning algorithms for crack identification are being refined but require improvements to the true positive rate for crack detection. This shortcoming is an artifact of the limited training data currently available, perhaps more so than the structure of the neural networks. At present, the best results are had from a consensus over an ensemble of randomly generated Deep Neural Network (DNN) or Convolutional Neural Network (CNN) algorithms. Although the consensus accuracy method has yielded optimum true positive and true negative rates in excess of 80%, additional validation testing is necessary. In addition to the suite of LCM data that was initially used, and which represents the majority of the work presented in this report, WAMS image data was also reviewed at a preliminary level. The review included a comparison between image resolution and dynamic range for each method. WAMS (ZON file) image data was found to have a pixel pitch of 3.69μm compared to 1 μm for the LCM (vk4 file) data, which implies a lower resolution for the WAMS images. Conversely, the ratio of dynamic range of the WAMS data to the LCM data was approximately 41:20 for height data, suggesting that information from WAMS should more accurately determine the depth of pits. At present, the significance of the greater dynamic range of the WAMS data relative to the LCM data has not yet been evaluated.

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗

DOE OSTI2021

Hanford Double Shell Waste Tank Corrosion Studies FY2020 (Final Report)

For fiscal year (FY) 2020, the Savannah River National Laboratory (SRNL) focused on three experimental tasks related to Hanford Double Shell Tank (DST) chemistry and integrity. The first task focused on understanding risk of corrosion due to formation of either continuous layers or discrete patches of deposits on the tanks’ inner sidewalls and bottoms. The second task studied vapor space corrosion (VSC) of the secondary liner using two commercially available vapor corrosion inhibitors (VCIs) at manufacturer recommended dosages. Finally, the third task investigated the long-term open circuit potential (OCP) drift for mill-scale coupons, coupons with polished surfaces, and partial mill-scale coupons that were exposed to tank waste simulants. Additional tests were performed to evaluate the OCP drift as a function of the quantity and composition of organic compounds added to the simulant. A test that was included in the matrix that established the new chemistry limits for tank corrosion, but was previously unreported, was presented and reviewed as well.

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗

DOE OSTI2020

Hanford Double Shell Waste Tank Corrosion Studies (Final Report FY2019)

During fiscal year (FY) 2019, the Savannah River National Laboratory (SRNL) focused on four primary tasks for Hanford Double Shell Tanks (DSTs) corrosion studies. The first task, New Limits, was a continuation from the electrochemical work started in FY16, to expand electrochemical testing to elevated temperatures and elevated hydroxide concentrations and evaluate how these factors will influence pitting corrosion. Using the pitting factor (PF) equation, these new conditions were validated to provide a conservative estimate for the susceptibility of pitting corrosion on legacy carbon steel. The second task, Secondary Liner Corrosion, focused on Vapor Space Corrosion (VSC) and immersion testing studies using two commercially available vapor corrosion inhibitors (VCIs). For this FY, the VCI strategy was applied mid-experiment to determine performance on weathered coupons. The third task, Long-Term Open Circuit Potential (OCP) Drift, was performed using simplified simulated chemistries to evaluate change in pitting corrosion risk due to evolution of corrosion potential for mill-scale and freshly polished 600-grit surfaces. Finally, the fourth task, Microbiologically-Influenced Corrosion (MIC) studies, was focused on the study of leak detection pit (LDP) water sent from the Hanford tank farm for determination of bacteria that can be conducive to corrosion using commercially available kits: BART TM and MICkit® 5. In addition, this FY, a secondary task was added which was a continuation of the study of the Quartz-enhanced Photoacoustic Spectroscopy (QEPAS) system. Work was started but was ultimately not pursued. A summary of each task performed is presented below.

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗

DOE OSTI2020

Thermal Dehydration of Aluminum (Oxy)hydroxides on Fuel Cladding Material - 20200

The aluminum cladding of research-reactor fuel undergoes general corrosion with resulting formation of adherent aluminum (oxy)hydroxide films during in-reactor and post-discharge exposure to water under various conditions and temperatures. These (oxy)hydroxides contain chemically-bound water that poses challenges for extended dry storage due to the risk of thermal or radiolytic decomposition releasing free water and/or hydrogen and oxygen gases. This study comprised laboratory experiments of thermal drying behavior of aluminum (oxy)hydroxides to identify approaches for reducing bound water on fuel cladding prior to sealed dry storage. Effective drying strategies for adherent (oxy)hydroxides on fuel cladding will improve the safety of dry storage by mitigating potential avenues for additional corrosion and/or generation of flammable gases inside the storage canister. This work is part of a broader investigation to address knowledge gaps and technical data needs for dry storage of aluminum-clad spent nuclear fuel (ASNF), which included investigation of (oxy)hydroxide formation on aluminum alloy substrates immersed in water, characterization of service-grown films from ASNF, and radiolytic yield of hydrogen from (oxy)hydroxide powders and films. The current work comprises experimental thermal dehydration of aluminum trihydroxides (bayerite and gibbsite) characteristic of low-temperature (<80 deg. C) corrosion in water and aluminum oxyhydroxide (boehmite) characteristic of high temperature (>80 deg. C) corrosion in water. First, commercially produced (oxy)hydroxide powders (boehmite and gibbsite) were tested via thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC). The effort aimed to identify or confirm key temperature ranges/thresholds for the thermal decomposition reactions, as well as impacts of ramp rate and hold times, for drying of isolated, high-surface-area (oxy)hydroxides. The information gleaned from powder tests was used to guide subsequent drying tests on adherent (oxy)hydroxide films grown on aluminum alloy substrates. TGA was used to analyze small samples of the aluminum coupons with adherent (oxy)hydroxide films. Specimens were characterized both pre- and post-drying using X-ray diffraction (XRD) to determine the film composition and scanning electron microscopy (SEM) to determine its morphology. Drying of adherent (oxy)hydroxide films was anticipated to pose additional complications relative to drying of (oxy)hydroxide powders. Anticipated challenges include achieving sufficient drying of the (oxy)hydroxide at low-enough temperature to avoid melting or other undesirable phase changes in the aluminum substrate and overcoming transport limitations of water through the thickness of a dense film or through a tortuous pore structure to reach the outer surface of the film. Inn addition, dehydration of (oxy)hydroxides significantly changes the film density, which may lead to substantial alterations in the morphology, including potential cracking and spalling of the film. TGA/DSC tests of gibbsite powders resulted in successful conversion to boehmite or alumina, depending on the maximum temperature reached. At low ramp rates (≤5 deg. C/min), the conversion to boehmite occurred around 300 deg. C (210-340 deg. C). XRD confirmed that boehmite was the only phase detected after tests reaching 450 deg. C. The transition to alumina occurred around 510 deg. C (470-550 deg. C), with XRD detecting only alumina after tests reaching at least 600 deg. C. Boehmite powders dehydrated to alumina at about 400 deg. C (330-460 deg. C) for coarse (77-μm particle diameter) powder and about 490 deg. C (420-520 deg. C) for fine (0.7-μm particle diameter) powder. For all powders tested, the maximum percent mass loss after drying to high temperature slightly exceeded the theoretical mass loss for complete dehydration of the stoichiometric (oxy)hydroxide to alumina, which is likely attributable to physisorbed water in the powder. Drying of a thick (∼8.6 μm), predominantly bayerite adherent film displayed a dramatic change in film morphology, with the initially continuous trihydroxide film cracking into sections on the order of 50 μm square and partially delaminating. The outermost layer of the film completely faked of in some regions. The layer exposed under the spalled oxide also displayed prominent cracking, with spacing on the order of 10 μm, but this surface layer appeared to remain completely adhered to the aluminum substrate. TGA showed mass losses per unit surface area up to ∼1.0 mg/cm{sup 2}. XRD characterization of the remaining oxide was inconclusive, with no crystalline phases detected. (authors)

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2020

(Oxy)hydroxides Formed on Aluminum Fuel Materials After Irradiation and Long-Term Wet Storage - 20354

The aluminum cladding of research-reactor fuel experiences general corrosion when in contact with water during in-reactor service and post-discharge wet storage, resulting in the formation of adherent aluminum (oxy)hydroxide films. These (oxy)hydroxides contain chemically-bound water that poses challenges for extended dry storage due to the risk of thermal or radiolytic decomposition releasing free water and/or hydrogen and oxygen gases. This study describes characterization of the (oxy)hydroxides present on several aluminum materials used in reactor operation and subsequently stored wet in the L-Basin storage facility at the Savannah River Site (SRS) for an extended period. Characterization data providing insight into the loading, composition, and morphology of (oxy)hydroxides to be expected on service-exposed aluminum cladding provides valuable benchmarks for designing adequate drying and dry-storage approaches. This work is part of a broader investigation to address knowledge gaps and technical data needs for dry storage of aluminum-clad spent nuclear fuel (ASNF), which included in-lab growth of (oxy)hydroxide films on aluminum alloy substrates to investigate formation behavior, investigation of drying methods to remove existing (oxy)hydroxides from ASNF cladding, and measurement of radiolytic yield of hydrogen from (oxy)hydroxide powders and films. In this study, (oxy)hydroxide films were characterized for three aluminum-alloy materials used in reactors and subsequently stored wet for up to approximately 40 years in L-Basin at SRS: one cropping from a Missouri University Research Reactor (MURR) fuel element (Al-6061 alloy), one cropping from a Universal Sleeve Housing (USH) (Al-6063 alloy), and one Mark-16B fuel assembly (either Al-6061 or Al- 6063). The USH and Mark-16B were used in SRS production reactors. Characterization of the as-received (oxy)hydroxides included scanning electron microscopy (SEM) in both plan-view and cross-section to characterize the (oxy)hydroxide layer's morphology, thickness, and structure. X-ray diffraction (XRD) was used to identify the chemical composition and distinguish between the various aluminum (oxy)hydroxides known to form under reactor and storage conditions. XRD analysis revealed both bayerite (Al(OH)3) and boehmite (AlOOH) on the surface of the MURR and USH samples, as well as bayerite, boehmite, and gibbsite (another Al(OH)3 polymorph) on the surface of the Mark-16B sample. The aluminum trihydroxides, bayerite and gibbsite, are typically associated with corrosion in low-temperature (<80 deg. C) water, while boehmite is expected to form at higher water temperature (>80 deg. C). The presence of bayerite on the USH, which is believed to have operated close to 90 deg. C, suggests that boehmite formed during in-reactor exposure was not protective against further hydroxide growth in low-temperature wet storage. Cross-section scanning electron microscopy (SEM) showed total (oxy)hydroxide layer thicknesses of ∼5- 10 μm for the MURR and ∼5-15 μm for the Mark-16B. The thickness of the USH's (oxy)hydroxide layer was indiscernible by the current mounting and imaging method, despite plan-view SEM and XRD confirming the presence of an (oxy)hydroxide layer. (authors)

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗

DOE OSTI2020

Impact of Permanganate Oxidation of Glycolate on Corrosion of the Defense Waste Processing Facility (DWPF) Recycle Collection Tank (RCT), Transfer-line and Waste Tank Materials of Construction (MoC)

Savannah River Remediation (SRR) is evaluating the use of glycolic acid to replace formic acid as an alternate reductant for the Defense Waste Processing Facility (DWPF) at Savannah River Site (SRS). The replacement is aimed at reducing facility hazards, improving pH stability and rheological control, and lowering off gas production. Glycolate, which is the product that may remain, can also be carried downstream to High-Level Waste and Low-Level Waste facilities. Complete oxidation of glycolate and other organic species from the Sludge Receipt and Adjustment Tank (SRAT) may be necessary to minimize thermolytic hydrogen generation that can cause flammability issues. The glycolate oxidation may be performed in the Recycle Collection Tank (RCT). The RCT heel would be adjusted with sodium hydroxide to maintain the solution caustic and sodium nitrite as corrosion inhibitor prior to the addition of condensate that can be from the contents of the Slurry Mix Evaporator Condensate Tank (SMECT) or Offgas Condensate Tank (OGCT). The RCT tank collects the waste to be transferred via the Low Point Pump Pit – Recycle Pump Tank (LPPP-RPT) through a jacketed transfer-line to the Tank Farm facility. Scoping studies were performed to evaluate an oxidizing agent and sodium permanganate was selected as the best option for glycolate destruction. Testing was recommended to determine the impact on the Materials of Construction (MoC) due to the addition of sodium permanganate. The targeted concentration of sodium permanganate used equated to a 7:1 molar permanganate to glycolate ratio (nominally 0.002 M permanganate). However, to conservatively maximize the permanganate corrosivity, in some cases no glycolate was added.

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗