Hanford Double Shell Waste Tank Corrosion Studies (Final Report)

Abstract

For fiscal year (FY) 2022, the Savannah River National Laboratory (SRNL) focused on two experimental tasks related to Hanford Double Shell Tank (DST) chemistry and integrity. The first task focused on understanding risk of corrosion due to formation of either continuous layers or discrete patches of solids on the tanks' inner sidewalls and bottoms. The tank bottom solids contact corrosion testing focused on studying the effects of forming a dry adherent solids layer on a carbon steel substrate. Long-term exposure tests and electrochemical tests were performed to investigate the effect of drying (i.e., removing water) from the solids phase. The second task focused on corrosion of the exterior of the secondary liner. In previous years, vapor corrosion inhibitors (VCIs) were investigated as a means of mitigating corrosion of the exterior of the secondary liner. During FY22 the utilization of nitrogen was explored as a means of corrosion mitigation. The corrosion test results with nitrogen were compared with the corrosion mitigation performance of the VCIs.