Floating substrate process: Large-area silicon sheet task low-cost solar array project

Supercooling of silicon-tin alloy melts was studied. Values as high as 78 C at 1100 C and 39 C at 1200 C were observed, corresponding to supersaturation parameter values 0.025 and 0.053 at 1050 C and 1150 C, respectively. The interaction of tin with silane gas streams was investigated over the temperature range 1000 to 1200 C. Single-pass conversion efficiencies exceeding 30% were obtained. The growth habit of spontaneously-nucleated surface growth was determined to be consistent with dendritic and web growth from singly-twinned triangular nucleii. Surface growth of interlocking silicon crystals, thin enough to follow the surface of the liquid and with growth velocity as high as 5 mm/min, was obtained. Large area single-crystal growth along the melt surface was not achieved. Small single-crystal surface growth was obtained which did not propagate beyond a few millimeters.

Garfinkel, M.↗

NASA NTRS1977

New process produces high-power Schottky diodes

Processing procedure using low-temperature platinum silicide, results in successful high-yield fabrication of large-area mesa-geometry Schottky diodes, with reverse breakdown voltages as high as 150 volts and leak currents less than 5 milliamps at 212 F.

Cordes, L. F.↗

NASA NTRS1975

Development and fabrication of improved Schottky power diodes

Reproducible methods for the fabrication of silicon Schottky diodes have been developed for tungsten, aluminum, conventional platinum silicide, and low temperature platinum silicide. Barrier heights and barrier lowering under reverse bias have been measured, permitting the accurate prediction of forward and reverse diode characteristics. Processing procedures have been developed that permit the fabrication of large area (about 1 sq cm) mesageometry power Schottky diodes with forward and reverse characteristics that approach theoretical values. A theoretical analysis of the operation of bridge rectifier circuits has been performed, which indicates the ranges of frequency and voltage for which Schottky rectifiers are preferred to p-n junctions. Power Schottky rectifiers have been fabricated and tested for voltage ratings up to 140 volts.

Cordes, L. F.↗

NASA NTRS1974

High voltage power Schottky diodes

Calculations of the low frequency rectification efficiency of power Schottky diodes show that silicon Schottky rectifiers have lower losses than silicon p-n junctions for all voltage applications up to approximately 150 volts. These calculations are presented. Large area Schottky diodes have been fabricated which exhibit near ideal reverse leakage at 100 C out to approximately 100 volts and which have current capability of 100 A. Fabrication details and performance data are presented.