Engineering topics
Gorte, Raymond
Publications and source records attributed to Gorte, Raymond.
Enhancing Coking Tolerance and Stability of SOFC Anodes Using Atomic Layer Deposition (ALD) of Oxide Thin Films
The overall objective of this project was to use atomic layer deposition (ALD) to add modifiers to the surfaces of conventional Ni-YSZ cermet, solid oxide fuel cell (SOFC) anodes to enhance both their tolerance to hydrocarbon fuels by decreasing their propensity to form coke deposits, and to increase redox stability. Studies of the use of ALD to modify analogous supported metal powder catalysts were also added to the scope of the project in response to our industrial partner, Atrex going out of business. The initial portion of the program focused on designing and building the ALD reactor required for deposition of the oxide modifier films. Studies of the oxide modifier films on the coking tolerance and of redox properties of Ni-cermet anodes were then carried out. These studies demonstrated that while surface oxide modifiers were able to impart some coking resistance this only occurred for a relatively small range of operating conditions (e.g., temperature, steam-to-fuel ratio, etc.) and not at the level that would be required for operating in methane fuel at low steam-to-methane ratios. In light of this observation, we focused on assessing another approach to enhance anode coking resistance which eliminated bulk Ni from the anode. This approach made use of electronically conducting perovskite films to provide electrical conductivity in the anode, while using small amounts of Ni or other metals, such as Pt, deposited using ALD as the anode oxidation catalyst. This approach proved to be quite promising at both imparting coking resistance and redox stability.
Pt Catalysts Modified with Manganese Oxide through Atomic Layer Deposition for CO Oxidation: Establishing a Coating Layer above or below Pt
The effect of atomic layer deposition (ALD) of manganese oxide on CO oxidation over Pt/Al2O3 is investigated. Two types of catalysts with a thin MnOx layer coated on or under the Pt nanoparticles (NPs) are prepared, and a pristine Pt/Al2O3 catalyst is used as a reference sample. The addition of the ALD layers improves the catalyst durability and both catalysts with MnOx exhibit greater stability after thermal aging at 1073-K. Besides, MnOx promotes CO oxidation through active Pt-MnOx interfacial sites, showing a reaction rate up to 35-fold faster than that of unmodified Pt. Interestingly, the CO adsorption ability of the Pt catalysts with MnOx overcoats is greatly suppressed after the high-temperature calcination; however, the reaction rate of CO oxidation is still excellent. This phenomenon is because the uniformly covered MnOx with two atomic layers diminishes the exposed Pt surface, but the reaction near the Pt-MnOx interfacial site still occurs. Our results guide the effective use of ALD, which is actively applied to heterogeneous catalysis, and provide a novel direction to control metal-assisted interactions.
Epitaxial and Strong Support Interactions between Pt and LaFeO 3 Films Stabilize Pt Dispersion
The ability to stabilize very small Pt crystallites in supported-metal catalysts following harsh treatments is an important industrial problem. Herein, we demonstrate that Pt particles can be maintained in the 1- to 2-nm range following multiple oxidation and reduction cycles at 1073 K when the particles are supported on 0.5-nm LaFeO 3 films that have been deposited onto MgAl 2 O 4 using atomic layer deposition (ALD). Characterization by Scanning Transmission Electron Microscopy (STEM) suggest that, when the catalyst is oxidized at 1073 K, the Pt crystallites are oriented with respect to the underlying LaFeO 3 . X-Ray Absorption Spectroscopy (XAS) also shows evidence for changes in the Pt environment. CO-oxidation rates for the reduced catalyst remain unchanged after five redox cycles at 1073 K. Epitaxial growth of Pt clusters and the consequent strong metal-support interaction between Pt and LaFeO 3 are indicated to be prime reasons for the enhanced catalytic performances.