Pt Catalysts Modified with Manganese Oxide through Atomic Layer Deposition for CO Oxidation: Establishing a Coating Layer above or below Pt

Abstract

The effect of atomic layer deposition (ALD) of manganese oxide on CO oxidation over Pt/Al2O3 is investigated. Two types of catalysts with a thin MnOx layer coated on or under the Pt nanoparticles (NPs) are prepared, and a pristine Pt/Al2O3 catalyst is used as a reference sample. The addition of the ALD layers improves the catalyst durability and both catalysts with MnOx exhibit greater stability after thermal aging at 1073-K. Besides, MnOx promotes CO oxidation through active Pt-MnOx interfacial sites, showing a reaction rate up to 35-fold faster than that of unmodified Pt. Interestingly, the CO adsorption ability of the Pt catalysts with MnOx overcoats is greatly suppressed after the high-temperature calcination; however, the reaction rate of CO oxidation is still excellent. This phenomenon is because the uniformly covered MnOx with two atomic layers diminishes the exposed Pt surface, but the reaction near the Pt-MnOx interfacial site still occurs. Our results guide the effective use of ALD, which is actively applied to heterogeneous catalysis, and provide a novel direction to control metal-assisted interactions.