Pt Catalysts Modified with Manganese Oxide through Atomic Layer Deposition for CO Oxidation: Establishing a Coating Layer above or below Pt
The effect of atomic layer deposition (ALD) of manganese oxide on CO oxidation over Pt/Al2O3 is investigated. Two types of catalysts with a thin MnOx layer coated on or under the Pt nanoparticles (NPs) are prepared, and a pristine Pt/Al2O3 catalyst is used as a reference sample. The addition of the ALD layers improves the catalyst durability and both catalysts with MnOx exhibit greater stability after thermal aging at 1073-K. Besides, MnOx promotes CO oxidation through active Pt-MnOx interfacial sites, showing a reaction rate up to 35-fold faster than that of unmodified Pt. Interestingly, the CO adsorption ability of the Pt catalysts with MnOx overcoats is greatly suppressed after the high-temperature calcination; however, the reaction rate of CO oxidation is still excellent. This phenomenon is because the uniformly covered MnOx with two atomic layers diminishes the exposed Pt surface, but the reaction near the Pt-MnOx interfacial site still occurs. Our results guide the effective use of ALD, which is actively applied to heterogeneous catalysis, and provide a novel direction to control metal-assisted interactions.
36 MATERIALS SCIENCE↗
A Perspective on Thin-Film Perovskites as Supports for Metal Catalysts
Perovskite-supported metals have sometimes been referred to as “intelligent catalysts” because of the potential to regenerate sintered particles by driving the metal into the oxide lattice by high-temperature oxidation and releasing the metal by reduction. However, low surface areas and incomplete release of metal from the lattice have prevented the widespread application of these materials. Furthermore, we describe the preparation of thin perovskite films on stable supports by Atomic Layer Deposition (ALD) as a means for avoiding the limitations associated with bulk perovskites. Examples will be given that demonstrate many of the favorable properties of perovskite supports can be retained, while avoiding some of the shortcomings. Potential opportunities for using these materials are discussed.
36 MATERIALS SCIENCE↗
Epitaxial and Strong Support Interactions between Pt and LaFeO 3 Films Stabilize Pt Dispersion
The ability to stabilize very small Pt crystallites in supported-metal catalysts following harsh treatments is an important industrial problem. Herein, we demonstrate that Pt particles can be maintained in the 1- to 2-nm range following multiple oxidation and reduction cycles at 1073 K when the particles are supported on 0.5-nm LaFeO 3 films that have been deposited onto MgAl 2 O 4 using atomic layer deposition (ALD). Characterization by Scanning Transmission Electron Microscopy (STEM) suggest that, when the catalyst is oxidized at 1073 K, the Pt crystallites are oriented with respect to the underlying LaFeO 3 . X-Ray Absorption Spectroscopy (XAS) also shows evidence for changes in the Pt environment. CO-oxidation rates for the reduced catalyst remain unchanged after five redox cycles at 1073 K. Epitaxial growth of Pt clusters and the consequent strong metal-support interaction between Pt and LaFeO 3 are indicated to be prime reasons for the enhanced catalytic performances.