DOE OSTI2024

A Comparison of CdS and Zn(O,S) Buffer Layers in (Ag,Cu)(In,Ga)Se2 Solar Cells

Cu(In,Ga)Se 2 -based solar cells typically use a C dS buffer layer, even though its relatively low bandgap causes parasitic absorption. While alternatives to CdS have been explored in other studies, limited results have been shown for Ag-alloyed CIGS (ACIGS). In this study, ACIGS solar cells with both CdS and Zn(O,S) buffer layers were fabricated and compared for solar cell performance. The Zn(O,S) buffer slightly improved J sc through reduced absorption, although surface optimization is necessary. The Zn(O,S) ACIGS also had improved FF through reduced series resistance and ideality factor, which could be improved further through optimization. However, the Voc in the Zn(O,S) samples was reduced, likely due to increased bulk and front interface recombination. This study shows the promise of Zn(O,S) as a buffer layer in ACIGS solar cells and suggests pathways for further improvement.

absorption↗

DOE OSTI2022

Investigation of Ga 2 O 3 as a new transparent conductive oxide for photovoltaics applications

This small innovation project intended to leverage recent activity and advances in ultrawide-bandgap oxide power electronics toward the investigation of Ga 2 O 3 as a transparent conductive oxide (TCO) for use in photovoltaics (PV). Ga 2 O 3 ’s theoretical advantage over incumbent TCOs is its very large bandgap of 4.8 eV, ensuring optical transparency of photons with λ ≥ 260 nm, effectively the full terrestrial solar spectrum. At the time of proposal writing, literature on Ga 2 O 3 as a TCO/optical material was relatively sparse — what little existed was focused on for UV sensors and/or emitters, with none related to PV. As such, this project was intended to help determine the potential of Ga 2 O 3 as a PV-oriented TCO by investigating its deposition using tools common to the PV and electronics industries — atomic layer deposition (ALD) and RF sputtering (RS), both of which are already used in PV manufacturing — and its resultant optical and electronic properties. Final project goals were to test its application to Si and III-V solar cells. Controllable film thickness and excellent uniformity was established for both methods deposition methods, with ALD providing higher precision for thinner films and RS more effective for growing thicker films. The as-deposited films were found to be amorphous in nature. Spectroscopic ellipsometry (SE) confirmed bandgaps of at least 4.8 eV and non-parasitic absorption across both AM0 and AM1.5G spectra; a refractive index approaching the expected value of 1.8 was also observed, with some degree of tunability based on process parameters. Using this initial optical data, a transfer matrix model, which interfaces with in-house EQE and LIV models, was developed to simulate Ga 2 O 3 optical effects on various solar cells, included potential in antireflection coatings (ARCs). Despite promising optical properties, the resultant resistivity / conductivity metrics did not meet expectations, regardless of deposition process. Although thick RS-deposited films, using both undoped and 1 at% Ge (n-type) doped sintered targets — demonstrated high net carrier concentrations (via C-V), and low specific resistance Ohmic contacts were demonstrated, transmission line measurements (TLM) showed very high resistivity. Further analysis indicated high vertical film conductivity, but very low lateral conductivity. Deeper characterization revealed a relatively high density of nano/microcrystalline inclusions that were ostensibly the source of the vertical conductivity, with the amorphous matrix serving as an effective insulator (likely due to high concentrations of electronic trap states). Despite extensive work to increase film polycrystallinity — demonstrated via high temperature annealing — sufficient lateral conductivity for TCO use was not achieved. The final phase of the project shifted focus toward investigation of ALD-deposited Ga 2 O 3 ’s potential as a passivant and/or passivating contact for both Si and III-V solar cells, with expectation of performance similar to Al 2 O 3 . However, initial rounds of testing using our baseline ALD process yielded minimal (but not quite zero) passivation of both GaInP and Si surfaces. Dielectric passivation is well-known to be highly process sensitive; given the unoptimized nature of the process used, this work was deemed inconclusive. The final outlook with respect to feasibility of Ga 2 O 3 as a PV-oriented TCO is, ultimately, still uncertain. The work performed in this project confirmed the optical properties and deposition methods, but the achieved electrical properties do not meet technological needs; literature reports in recent years are somewhat inconsistent and potentially untrustworthy, but generally appear to be in line with our results. At the very least it is clear that, should Ga 2 O 3 still be under consideration for PV TCO and/or selective contact applications, a significant amount of optimization and study is still needed.

14 SOLAR ENERGY↗

DOE OSTI2021

EBSD of Rough Native CuInGaSe2 Thin-Films

The polycrystalline Cu (In, Ga) Se2, or CIGS, based thin-film materials system has long been studied for use in photovoltaic technologies, where its bandgap tunability, mechanical flexibility, and relatively low production costs are all appealing. Nonetheless, significant defect populations, which serve to reduce efficiency, create performance instabilities, and increase concerns about long-term reliability, have hindered wide-scale adoption. Prior work, including application of a scanning probe based deep level trap spectroscopy (SP-DLTS) defect mapping technique and scanning transmission electron microscope (STEM) based electron energy loss spectroscopy (EELS), has shown that the most detrimental defects, with energy level near mid-gap (thus serving as a carrier recombination center), are most likely caused by CuIn/Ga antisites and tend to cluster at or around certain grain boundaries [1,2]. However, the exact nature of these particular boundaries — their structures, chemistries, or even the relative misorientation of their associated grains — and their relation to this defect clustering and/or its formation is yet unknown. As such, electron backscatter diffraction (EBSD) orientation mapping, directly correlated with defect-sensitive techniques like SP-DLTS and/or STEM-EELS, could prove critical for providing the final missing links toward understanding the mechanisms behind these defects. Indeed, recent studies using correlative electron beam induced current (EBIC) with EBSD have been able to identify boundaries, and their relative misorientations, that possess detrimental electronic properties [3]. However, because EBIC is unable to resolve the defect energy levels, many questions are left unanswered. Furthermore, this study, and others like it, employed focused ion beam (FIB) milling to flatten the natively-rough CIGS [3-5], which may run the risk of changing the nature of any near-surface defect structures.

14 SOLAR ENERGY↗

DOE OSTI2021

23.4% monolithic epitaxial GaAsP/Si tandem solar cells and quantification of losses from threading dislocations

A 2-terminal, dual-junction, epitaxially integrated, GaAsP/Si tandem solar cell with an 3rd party certified efficiency of 23.4 % was fabricated via MOCVD growth on an ex-situ produced Si sub cell. The drastic efficiency improvement over the authors previous peer-reviewed demonstration of such a device architecture is examined. Critical advancements in top cell design to maximize short wavelength response were critical in enabling improved top cell response. An in-depth analysis of this champion tandem cell has identified key loss mechanisms which elucidate the pathway for further efficiency gains. First, voltage dependent collection efficiency in the GaAsP top cell is the primary cause of fill factor losses currently limiting efficiency. Analysis of spectrally resolved I–V measurements and analytical device modeling and indicate poor diffusion length due to elevated dislocation densities as the likely cause for the voltage dependent collection efficiency. Second, modeling for the GaAs 0.75 P 0.25 top cell, using experimental data at multiple dislocation densities, provides quantitative understanding of the current and voltage losses associated with threading dislocations providing a clear efficiency pathway with reduction in dislocation density. Finally, Si subcell modeling identifies the pathway for further Si subcell advances over the present, simplistic design, which has yet to employ the known benefits of rear surface texture or dielectric passivation.

14 SOLAR ENERGY↗

DOE OSTI2021

Metamorphic Tunnel Junctions Grown Via MOCVD Designed for GaAs 0.75 P 0.25 /Si Tandem Solar Cells

A high-performance metamorphic Al 0.2 Ga 0.8 As 0.75 P 0.25 /GaAs 0.75 P 0.25 heterojunction tunnel junction structure was developed for application to monolithic epitaxial GaAs 0.75 P 0.25 /Si 1.7 eV/1.1 eV bandgap tandem solar cells produced via metal-organic chemical vapor deposition. Doping optimization focused on both bulk doping concentrations and mitigating the transient incorporation effects that otherwise causes non-abrupt doping profiles in the Te doped layer. Furthermore, these efforts resulted in a fully-relaxed metamorphic tunnel diode at the target lattice constant having a peak tunneling current density (JP) of 279.1 A·cm –2 and a zero-bias resistance area product (RA) of 3.0×10 –4 Ω·cm 2 . After post-growth annealing to emulate the thermal load of the GaAs 0.75 P 0.25 top cell growth and elimination of the performance enhancing carbon activation anneal, the device achieved JP = 13.1 A·cm –2 and RA = 1.5×10 –3 Ω·cm 2 . These worst-case values are very promising as they enable the operation of GaAs 0.75 P 0.25 /Si tandems under one-sun AM1.5G illumination with negligible series resistance and at AM1.5D concentrations up to 240 suns with only 0.1% absolute efficiency loss.

14 SOLAR ENERGY↗

DOE OSTI2021

Improving GaAsP/Si Tandem Solar Cells Using Silicon Passivated Contacts

The degradation of photocarrier bulk lifetime in Si wafer substrates during the heteroepitaxial growth of III-V materials has been widely reported and is known to limit the efficiency of III-V/Si tandem solar cells. There have been prior strategies to protect Si lifetime in III-V growth chambers, but most require the use of a protective layer that must be removed in subsequent device processing. It would be advantageous for protective layers to remain an active part of the device. In this work, we demonstrate that a polycrystalline silicon (poly-Si) passivated contact can protect the minority carrier lifetime of the Si base wafer during the organometallic vapor phase epitaxy of III-V materials on silicon substrates.

Exascale Computing Project↗

DOE OSTI2021

The Value of Diversity in the Renewable Energy Industry and Research Community

Part of creating a successful solar industry is developing a capable workforce. It has been repeatedly shown that organizations and companies are more productive when they have diverse and inclusive cultures. The solar industry in the U.S. performs well in some aspects (non-white workforce, positive work environment) but drastically under-performs in many others. We discuss these metrics and how this impacts the renewable energy industry and the solar research community. We highlight some initial actions which are necessary to begin to remediate these deficiencies, such as demographic tracking, recruiting strategies, and mentoring. We also present the historical and ongoing efforts to improve the diversity and inclusion of the Photovoltaic Specialists Conference, particularly through the work of this year’s Diversity and Inclusion (D&I) oversight committee. This year’s D&I committee is implementing diversity tracking, a women’s lunch, a diversity lunch, childcare resources, pronouns on badges, gender-neutral restrooms, addressing accessibility issues, and publishing a diversity statement and code of conduct to the PVSC website.

diversity↗

DOE OSTI2020

GaAsP/Si Tandem Solar Cells: Pathway to Low-Cost, High-Efficiency Photovoltaics

Si is the dominant PV technology, now and for the foreseeable future, due to its extensive manufacturing infrastructure, supply chain, feedstock availability, and highly optimized degree of fabrication processes, which altogether has produced an economic scenario where PV electricity generation is often cheaper than conventional fossil based generation. In many places, the overarching goal of grid parity has been achieved, but further improvement in performance-cost metrics are still needed to sustain the continued LCOE reductions needed to not only compete with conventional generation, but displace it on a global scale; a matter of critical importance if we stand any hope of slowing climate change. Nevertheless, single-junction Si PV is already nearing its physical limit, both in performance and cost, and is thus cannot meet these long-term goals alone. To this end, we are working on the development of monolithic III-V/Si tandem solar cells, which improve upon the performance of pure Si by providing enhanced utilization (reduced thermalization) of high-energy photons. This architecture nominally combines the substantial existing knowledge base, manufacturing infrastructure, and low cost of Si PV with the high efficiencies afforded by the well-established multijunction approach — the only proven way to break the single-junction limit. Although the metal-halide perovskite/Si tandem architecture has garnered substantial attention in recent years, serious questions regarding reliability and service lifetime remain, whereas III-V PV has a proven track record, including in the harsh concentrator and space environments. Additionally, there are multiple fabrication approaches to producing III-V/Si tandem cells, but we are focused on monolithic epitaxial integration as it is the most likely to yield the lowest ultimate LCOE in a fully mature, scaled technology. In this work we have produced multiple generations of GaAsP/Si tandem solar cells, demonstrating a more than 10% absolute AM1.5G efficiency improvement within the time frame of the project, including two verified world records. We have done this using industry-standard fabrication methods, showing that this platform can ultimately be manufactured at scale using existing or only slightly upgraded Si and III-V tooling. Our scientific and engineering advances across a range of fundamental and applied areas – III-V/Si heteroepitaxial integration, defect control in metamorphic III-V epitaxy, fundamental materials-oriented solar cell design and modeling methodology, and more – have created clear pathways for continued advances toward the goal of >30% AM1.5G cell efficiency (and >25% module) and will serve to inform the broader research community for well beyond this immediate application. Techno-economic modeling indicates that our approach can indeed meet SunShot/SETO LCOE targets, but as with any “post-Si” technology there are difficult, but not insurmountable barriers, requiring continued focused research and development efforts.

14 SOLAR ENERGY↗

DOE OSTI2020

Reduced Dislocation Introduction in III–V/Si Heterostructures with Glide-Enhancing Compressively Strained Superlattices

The novel use of a GaAs y P 1-y /GaP compressively-strained superlattice (CSS) to provide enhanced control over misfit dislocation (MD) evolution and threading dislocation density (TDD) during GaP/Si metamorphic heteroepitaxy is demonstrated. Here, the insertion of the CSS just after critical thickness, and thus prior to substantial dislocation introduction, is found to yield significantly reduced TDD in relaxed, 500 nm thick, n-type GaP/Si versus comparable control samples. The impact of CSS period count on average TDD and the overall dislocation network morphology was examined, supported by quantitative microstructural characterization, revealing a nearly 20× relative TDD reduction (to 2.4 ± 0.4×10 6 cm -2 ) with a 3-period CSS structure. A similarly low TDD (3.0 ± 0.6×10 6 cm -2 ) is maintained when the resultant n-GaP/Si virtual substrate is used for the growth of a subsequent n-type GaAs 0.75 P 0.25 -terminal GaAs y P 1-y step-graded metamorphic buffer. Although the physical mechanism for TDD reduction provided by these structures is not yet entirely understood, this initial work suggests that enhanced glide dynamics of MDs at or within the CSS placed early in the growth leads to a reduction in the total number of dislocations introduced overall, as opposed to annihilation-based reduction that occurs in conventional strained-layer superlattice dislocation filter approaches.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2020

The Critical Role of AlInP Window Design in III–V Rear-Emitter Solar Cells

This article highlights the critical role of window design on short circuit carrier collection in rear-emitter solar cells, as demonstrated through modeling and experiment using metamorphic GaAs y P 1-y . Ultimately, if the window design is not carefully considered, surface depletion caused by Fermi level pinning at the window/air interface can extend into regions of active collection resulting in a large increase in effective window/base interface recombination velocity. This was experimentally shown here to result in a potential AM1.5G photocurrent loss of 8.1 mA/cm 2 , or nearly 50%, based on integrated internal quantum efficiency (IQE). Associated IQE modeling and curve fitting indicate that the effective IRV at the GaAs 0.75 P 0.25 /Al 0.64 In 0.36 P interface is increased by multiple orders of magnitude when the window is not sufficiently thick or doped to fully contain the surface depletion to within the window layer. Calculations of the surface depletion depth as a function of doping and the surface Fermi pinning energy level provides insight into the fundamental limits of window thickness. As a result, this allows the estimation of the Al 0.64 In 0.36 P surface pinning level to be at least 1.25 eV below the conduction band edge, or in the bottom half of the bandgap.

14 SOLAR ENERGY↗