Evaluation of interfacial photophysical processes by time-resolved optical spectroscopy in perovskite solar cells
Not provided.
Engineering topics
Publications and source records attributed to Grater, Luke.
Not provided.
Perovskite solar cells have seen impressive progress in performance and stability, yet maintaining efficiency while scaling area remains a challenge. Here we find that additives commonly used to passivate large-area perovskite films often co-precipitate during perovskite crystallization and aggregate at interfaces, contributing to defects and to spatial inhomogeneity. Here we develop design criteria for additives to prevent their evaporative precipitation and enable uniform passivation of defects. We explored liquid crystals with melting point below the perovskite processing temperature, functionalization for defect passivation and hydrophobicity to improve device stability. We find that thermotropic liquid crystals such as 3,4,5-trifluoro-4'-(trans-4-propylcyclohexyl)biphenyl enable large-area perovskite films that are uniform, low in defects and stable against environmental stress factors. We demonstrate modules with a certified stabilized efficiency of 21.1% at an aperture area of 31 cm 2 and enhanced stability under damp-heat conditions (ISOS-D-3, 85% relative humidity, 85 °C) with T 86 (the duration for the efficiency to decay to 86% of the initial value) of 1,200 h, and reverse bias with (ISOS-V-1, negative maximum-power-point voltage) and without bypass diodes.
Perovskite solar cells (PSCs) consisting of interfacial two- and three-dimensional heterostructures that incorporate ammonium ligand intercalation have enabled rapid progress toward the goal of uniting performance with stability. However, as the field continues to seek ever-higher durability, additional tools that avoid progressive ligand intercalation are needed to minimize degradation at high temperatures. We used ammonium ligands that are nonreactive with the bulk of perovskites and investigated a library that varies ligand molecular structure systematically. Here, we found that fluorinated aniliniums offer interfacial passivation and simultaneously minimize reactivity with perovskites. Using this approach, we report a certified quasi–steady-state power-conversion efficiency of 24.09% for inverted-structure PSCs. In an encapsulated device operating at 85°C and 50% relative humidity, we document a 1560-hour T85 at maximum power point under 1-sun illumination.
The tunable band gaps and facile fabrication of perovskites make them attractive for multi-junction photovoltaics. However, light-induced phase segregation limits their efficiency and stability: this occurs in wide band gap (> 1.65 eV) I/Br mixed perovskite absorbers, and becomes even more acute in the top cells of triple-junction solar photovoltaics that requires a fully 2.0 eV band gap absorber. We report herein that lattice distortion in I/Br mixed perovskites is correlated with the suppression of phase segregation, generating an increased ion migration energy barrier arising from the decreased average interatomic distance between A-site cation and iodide. Using a ~2.0 eV Rb/Cs mixed-cation inorganic perovskite with large lattice distortion in the top subcell, we fabricated all-perovskite triple-junction solar cells and achieved an efficiency of 24.3% (23.3% certified quasi-steady-state efficiency) with an open-circuit voltage of 3.21 V. This is, to our knowledge, the first reported certified efficiency for perovskite-based triple-junction solar cells. The triple-junction devices retain 80% of their initial efficiency following 420 hours of operation at the maximum power point.
The open circuit voltage (V OC ) deficit in perovskite solar cells (PSCs) is greater in wide bandgap (>1.7 eV) cells than in ~1.5 eV perovskites. Quasi-Fermi level splitting (QFLS) measurements reveal V OC -limiting recombination at the electron transport layer (ETL) contact. This, we find, stems from inhomogeneous surface potential and poor perovskite-ETL energetic alignment. Common monoammonium surface treatments fail to address this; instead we introduce diammonium molecules to modify the perovskite surface states and achieve a more uniform spatial distribution of surface potential. Using 1,3-propane diammonium (PDA), QFLS increases by 90 meV, enabling 1.79 eV PSCs with a certified 1.33 V V OC , and > 19% power conversion efficiency (PCE). Incorporating this layer into a monolithic all-perovskite tandem, we report a record V OC of 2.19 V (89% of the Detailed Balance V OC limit) and > 27% PCE (26.3% certified quasi-steady-state). Furthermore, these tandems retain more than 86% of their initial PCE after 500 hrs operation.
The energy landscape of reduced-dimensional perovskites (RDPs) can be tailored by adjusting their layer width (n). Recently, 2D/3D heterostructures containing n = 1 and 2 RDPs have produced PSCs with > 25% power conversion efficiency (PCE). Unfortunately, this method does not translate to inverted PSCs due to electron blocking at the 2D/3D interface. Here we report a method to increase the layer width of RDPs in 2D/3D heterostructures in order to address this problem. We discover that bulkier organics form 2D heterostructures more slowly, resulting in wider RDPs; and that small modifications to ligand design induce preferential growth of n ≥ 3 RDPs. Levering these insights, we developed efficient inverted PSCs (certified 23.91% quasi-steady state efficiency). Furthermore, unencapsulated devices operate at room temperature and ~50% relative humidity for over 1000 hrs without loss of PCE; and, when subjected to ISOS-L3 accelerated aging encapsulated devices retain 92% of PCE after 500 hrs.