Temperature dependent interfacial microstructure in HIP-bonded Al6061/Zr joints

Pressing (HIP) at 450 °C and 560 °C under 103 MPa for 90 minutes to evaluate interfacial diffusion and microstructural evolution. Sound metallurgical bonding was achieved at both temperatures, with Zr serving as an effective diffusion barrier. Microstructural analysis revealed the the formation of a (Al,Si)3Zr intermetallic layer at the Al/Zr interface, whose thickness increased from ~100 nm at 450 °C to ~2100 nm at 560 °C, consistent with temperature-driven diffusion kinetics. The thin and continuous reaction layer observed at 450 °C indicates controlled interdiffusion and minimal reaction zone growth, favorable for maintaining interface stability and ductility. At 560 °C, enhanced atomic mobility led to pronounced intermetallic development, confirming diffusion-controlled growth behavior. These results provide valuable insights for optimizing Al/Zr interface design and diffusion barrier performance in advanced structural and energy systems.

Al/Zr interface↗

DOE OSTI2024

2D Nitrogen‐Doped Graphene Materials for Noble Gas Separation

Abstract Noble gases, notably xenon, play a pivotal role in diverse high‐tech applications. However, manufacturing xenon is an inherently challenging task, due to its unique properties and trace abundance in the Earth's atmosphere. Consequently, there is a pressing need for the development of efficient methods for the separation of noble gases. Using mild fluorographene chemistry, nitrogen‐doped graphene (GNs) materials are synthesized with abundant aromatic regions and extensive nitrogen doping within the vacancies and holes of the aromatic lattice. Due to the organized interlayer “nanochannels”, nitrogen functional groups, and defects within the two‐dimensional (2D) structures, GNs exhibits effective selectivity for Xe over Kr at low pressure. This enhanced selectivity is attributed to the stronger binding affinity of Xe to GN compared to Kr. The adsorption is governed by London dispersion forces, as revealed by theoretical calculations using symmetry‐adapted perturbation theory (SAPT). Investigation of other GNs differing in nitrogen content, surface area, and pore sizes underscores the significance of nitrogen functional groups, defects, and interlayer nanochannels over the surface area in achieving superior selectivity. This work offers a new perspective on the design and fabrication of functionalized graphene derivatives, exhibiting superior noble gas storage and separation activity exploitable in gas production technologies.

Šedajová, Veronika↗

DOE OSTI2023

TiltEM User Manual

The ability to automate the scanning transmission electron microscope (S/TEM) is tantamount to addressing next generation artificial intelligence, machine learning, and materials modeling capabilities. Constant utilization of these high-end capital equipment purchases also serves the requirements of the Department of Energy (DOE) to be fiscally responsible to the public. The development of an automated multi-modal tilt series algorithm for dark field/bright field S/TEM imaging plus chemical identification with energy dispersive x-ray spectroscopy has been achieved at PNNL. A tilt series workflow has now been generated which allows for autonomous collection of imaging and compositional information simultaneously. This advancement is due in large part to a transition from the rigid and microscope specific JEOL hardware environment, to the more adaptable GMS environment. This has thereby led to a greater degree of flexibility in the application of this method across platforms in addition to substantial time savings to the user.

47 OTHER INSTRUMENTATION↗

DOE OSTI2023

Characterization of boundary precipitation in a heavy ion irradiated tungsten heavy alloy under the simulated fusion environment

In the concerted effort to identify materials capable of surviving the adverse environment of a fusion reactor interior, tungsten heavy alloys have been put forth as leading candidates. Experimental trials and behavioral studies have yielded positive results for their adoption by taking advantage of the alloy’s unique balance of inherently high fracture toughness and low sputter yields; yet due to their relative novelty in the fusion community, there remains a lack of understanding on the response of these materials to the extended high temperature irradiation environment of the reactor interior. Further, to alleviate this issue and provide the necessary data on the behavior of tungsten heavy alloys to the simulated fusion environment, a 90W-7Ni-3Fe alloy has been subjected to elevated temperature sequential Ni + and He + ion irradiations to mimic the expected displacement damage and gas production expected after five years of service as a plasma facing material component. Atomic-scale structural analyses and nanoscale chemical mapping have identified the formation of two distinct precipitation structures, a surface localized η-carbide and an a-W 2 C type tungsten carbide, both of which appear to originate at the bi-phase interface between W and the ductile phase. This irradiation assisted and induced precipitate formation respectively is anticipated to adversely affect these materials by selective embrittlement at bi-phase interfaces leading to a reduction in the material’s overall fracture toughness during prolonged high temperature irradiation. It is asserted that any potential exposure to C during fusion reactor operational service should be minimized as to prevent the formation of these phases.

36 MATERIALS SCIENCE↗