Engineering topics

Harding, David R.

Publications and source records attributed to Harding, David R..

5 records

DOE OSTI2024

Two–Photon Printing of Base–Catalyzed Resins Involving Thiol–Michael Network Formation

Two-photon printing is accomplished using a photobase generator, 2-(2-nitrophenyl)-propyloxycarbony tetramethyl guanidine, to locally catalyze thiol-ene coupling between multifunctional monomers while mitigating chain-growth polymerization with free radical scavengers. Microstructures printed from base-catalyzed resins exhibit higher resolution (linewidths < 400 nm) and lower print error (<3%) than analogous microstructures printed using a photosensitive, free radical initiator. Further, Raman spectroscopy reveals that resins polymerized using the photobase generator in the presence of free radical scavengers exhibit higher selectivity of thiol-ene coupling over radical polymerization, resulting in stiffer, more uniform polymer networks. The base-catalyzed resins are capable of producing 3D microstructures printed with high accuracy and minimal post-processing defects. As a result, a direct comparison between free radical and base-initiated resins highlights the need for mindful consideration of how chemical reaction pathway influences printability and network end-properties when designing resins.

36 MATERIALS SCIENCE↗

DOE OSTI2024

Nanofabrication and inspection of fuel capsules for inertial confinement fusion

3D nanofabrication via Two-Photon Polymerization (TPP) provides a unique capability of flexibly fabricating complex structures over 1D-3D dimensions and µm-cm scales with resolutions below 100 nm. In the past years, the Laser-Assisted Nano Engineering (LANE) Group at the University of Nebraska-Lincoln (UNL) has been working closely with the Laboratory of Laser Energetics (LLE) in developing practical TPP approaches to fabricating various target structures for Inertial Confinement Fusion (ICF). At the same time, fuel capsules for ICF experiments should be inspected for surface and wall-embedded defects. Plastics materials [e.g., for example polystyrene (PS)] are the common materials used to make fuel capsules. However, during their manufacturing, capsules usually contain defects (vacuoles) embedded inside the shell walls, which may distort the implosion processes and influence the ICF performance of the capsules. The size of vacuoles is usually in a range from 100 to 2000 nm. Coherent anti-Stokes Raman scattering (CARS) microscope offers the capabilities of inspecting and characterizing the capsule defects. Furthermore, cryo-CARS microscopy was developed to explore how fuel isotope distributed inside target when icing that could not be diagnosed before.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Understanding the fusion yield dependencies in OMEGA DT-layered implosion experiments using a physics-based statistical mapping model

Improving the performance of inertial confinement fusion implosions requires physics models that can accurately predict the response to changes in the experimental inputs. Good predictive capability has been demonstrated for the fusion yield using a statistical mapping of simulated outcomes to experimental data [Gopalaswamy et al., Nature 565(771), 581–586 (2019)]. In this paper, a physics-based statistical mapping approach is used to extract and quantify all the major sources of degradation of fusion yield for direct-drive implosions on the OMEGA laser. Here, the yield is found to be dependent on the age of the deuterium tritium fill, the ℓ = 1 asymmetry in the implosion core, the laser beam-to-target size ratio, and parameters related to the hydrodynamic stability. A controlled set of experiments were carried out where only the target fill age was varied while keeping all other parameters constant. The measurements were found to be in excellent agreement with the fill age dependency inferred using the mapping model. In addition, a new implosion design was created, guided by the statistical mapping model by optimizing the trade-offs between increased laser energy coupling at larger target size and the degradations caused by the laser beam-to-target size ratio and hydrodynamic instabilities. When experimentally performed, an increased fusion yield was demonstrated in targets with larger diameters.

70 PLASMA PHYSICS AND FUSION TECHNOLOGY↗

NASA NTRS1995

Temperature dependence of the biaxial modulus, intrinsic stress and composition of plasma deposited silicon oxynitride films

Silicon oxynitride films were deposited by plasma-enhanced chemical-vapor deposition. The elemental composition was varied between silicon nitride and silicon dioxide: SiO(0.3)N(1.0), SiO(0.7)N(1.6), SiO(0.7)N(1.1), and SiO(1.7)N(0.%). These films were annealed in air, at temperatures of 40-240 C above the deposition temperature (260 C), to determine the stability and behavior or each composition. the biaxial modulus, biaxial intrinsic stress, and elemental composition were measured at discrete intervals within the annealing cycle. Films deposited from primarily ammonia possessed considerable hydrogen (up to 38 at.%) and lost nitrogen and hydrogen at anneal temperatures (260-300 C) only marginally higher than the deposition temperature. As the initial oxygen content increased a different mechanism controlled the behavior or the film: The temperature threshold for change rose to approximately equal to 350 C and the loss of nitrogen was compensated by an equivalent rise in the oxygen content. The transformation from silicon oxynitride to silica was completed after 50 h at 400 C. The initial biaxial modulus of all compositions was 21-3- GPa and the intrinsic stress was -30 to 85 MPa. Increasing the oxygen content raised the temperature threshold where cracking first occurred; the two film compositions with the highest initial oxygen content did not crack, even at the highest temperature (450 C) investigated. At 450 C the biaxial modulus increased to approximately equal to 100 GPa and the intrinsic stress was approximately equal to 200 MPa. These increases could be correlated with the observed change in the film's composition. When nitrogen was replaced by oxygen, the induced stress remained lower than the biaxial strength of the material, but, when nitrogen and hydrogen were lost, stress-relieving microcracking occurred.

Harding, David R.↗

NASA NTRS1993

Protective coatings for high-temperature polymer matrix composites

Plasma-enhanced chemical vapor deposition was used to deposit silicon nitride on graphite-fiber-reinforced polyimide composites to protect against oxidation at elevated temperatures. The adhesion and integrity of the coating were evaluated by isothermal aging (371 C for 500 hr) and thermal cycling. The amorphous silicon nitride (a-SiN:H) coating could withstand stresses ranging from approximately 0.18 GPa (tensile) to -1.6 GPa (compressive) and provided a 30 to 80 percent reduction in oxidation-induced weight loss. The major factor influencing the effectiveness of a-SiN:H as a barrier coating against oxidation is the surface finish of the polymer composite.

Harding, David R.↗