Protective coatings for high-temperature polymer matrix composites

Abstract

Plasma-enhanced chemical vapor deposition was used to deposit silicon nitride on graphite-fiber-reinforced polyimide composites to protect against oxidation at elevated temperatures. The adhesion and integrity of the coating were evaluated by isothermal aging (371 C for 500 hr) and thermal cycling. The amorphous silicon nitride (a-SiN:H) coating could withstand stresses ranging from approximately 0.18 GPa (tensile) to -1.6 GPa (compressive) and provided a 30 to 80 percent reduction in oxidation-induced weight loss. The major factor influencing the effectiveness of a-SiN:H as a barrier coating against oxidation is the surface finish of the polymer composite.