DOE OSTI2020

Microparticle impact-bonding modes for mismatched metals: From co-deformation to splatting and penetration

In this paper we present a comprehensive experimental campaign of high-velocity microparticle impacts with different combinations of particle and substrate materials to identify possible deformation regimes. Based on experimental observations of the impact sites, we identify three typical modes of behavior, namely, splatting, co-deformation, and penetration. We develop a theoretical framework to predict the operative bonding regime for a given particle/substrate combination, ranging from splatting and penetration at two extremes of a spectrum, and co-deformation in the center. We propose an impact ratio based on the materials’ properties, which can successfully quantify the spectrum. Co-deformation is expected when the ratio is around unity, while much larger or smaller ratios give rise to penetration and splatting, respectively.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Plasma and X-ray radiation-induced damage mechanisms in a tungsten heavy alloy

Tungsten-based materials are among the main candidate plasma-facing materials for future fusion reactors where extreme conditions of thermomechanical stresses, radiation, and energetic particles must be withstood. Here a hybrid X-pinch platform combined with a pulsed power machine was used to study damage mechanisms in 90W–4Cu–6Ni tungsten heavy alloy as a result of exposure to high energy density plasma, X-ray radiation, and the resulting thermal shock. It was found that the plasma-facing surface of the material undergoes severe melting and ablation with the extent of ablation being higher in the Cu–Ni phase than the W particles. Rapid melting and solidification transform the W particles into fine dendrite morphologies embedded in the Cu–Ni solid solution. Cracking was also observed in the subsurface layers at the interfaces between the W particles and the Cu-rich phase of the Cu–Ni matrix. X-ray radiation, on the other hand, cause slight melting on the surface without significant ablation and no cracking.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Particle size effects in metallic microparticle impact-bonding

In cold spray processing of metals, the critical velocity for particle bonding is dependent on both intrinsic material properties, such as density and (spall) strength, and extrinsic process parameters, such as the powder particle size. Here, we specifically isolate and investigate particle size effects on the critical velocity for bonding through laser- induced single particle impact experiments and finite element simulations. We also present a predictive framework to correlate particle size and critical velocity. We show that an increase in particle size leads to an increase in the temperature of the jet formed at the interface of the particle and the substrate. This increased temperature locally decreases the spall strength of the material which, in turn, decreases the critical velocity for larger particles.