Engineering topics
Haugan, T. J.
Publications and source records attributed to Haugan, T. J..
Magnetic and structural properties of the solid solution CuAl 2(1–x) Ga 2x O 4
CuAl 2 O 4 is a ternary oxide spinel with Cu 2+ ions (s = 1/2) primarily populating the A-site diamond sublattice. The compound is reported to display evidence of spin glass behavior but possess a non-frozen magnetic ground state below the transition temperature. On the other hand, the spinel CuGa 2 O 4 displays spin glass behavior at ~ 2.5 K with Cu 2+ ions more readily tending to the B-site pyrochlore sublattice. Therefore, we investigate the magnetic and structural properties of the solid solution CuAl 2(1-x) Ga 2x O 4 examining the evolution of the magnetic behavior as Al 3+ is replaced with a much larger Ga 3+ ion. Our results show that the Cu 2+ ions tend to migrate from tetrahedral to octahedral sites as the Ga 3+ ion concentration increases, resulting in a concomitant change in the glassy magnetic properties of the solution. Results indicate glassy behavior for much of the solution with a general trend towards decreasing magnetic frustration as the Cu 2+ ion shifts to the B-site. However, the x = 0.1 and 0.2 members of the system do not show glassy behavior down to our measurement limit (1.9 K) suggesting a delayed spin glass transition. We suggest that these two members are additional candidates for investigation to access highly frustrated exotic quantum states.
AC loss and contact resistance of different CICC cable patterns: Experiments and numerical modeling
Not Available
AC loss and contact resistance in REBCO CORC ® , Roebel, and stacked tape cables
Abstract Many high-temperature superconductor (HTS) applications require superconducting cables with high currents while operating in an alternating magnetic field. HTS cables should be composed of numerous superconducting tapes to achieve the required current capacity. Alternating current and magnetic fields cause AC losses in such cables and can provoke conductor instability. AC losses and contact resistances were measured of several cable designs based on commercially available REBCO tapes at the University of Twente. The AC loss was measured under identical conditions for eight REBCO conductors manufactured according to three types of cabling methods—CORC ® (Conductor on Round Core), Roebel, and stacked tape, including a full-size REBCO CICC (cable in conduit conductor). The measurements were done at T = 4.2 K without transport current in a sinusoidal AC magnetic field of 0.4 T amplitude and frequencies from 5 to 55 mHz. The AC loss was measured simultaneously by calibrated gas flow calorimeter utilizing the helium boil-off method and by the magnetization method using pick-up coils. Also, the AC loss of two CORC® conductors and a Roebel cable was measured at 77 K. Each conductor was measured with and without background field of 1 T. The measured AC coupling loss in the CORC ® and Roebel conductors is negligible at 4.2 K for the applied conditions while at 77 K coupling loss was observed for all conductors. The absence of coupling loss at 4.2 K can be explained by shielding of the conductor interior; this is confirmed with measurement and calculation of the penetration field of CORC ® and Roebel cables. The inter-tape contact resistance was measured for CORC ® and stacked tape samples at 4.2 and 77 K. It was demonstrated that a short heat treatment of CORC ® conductor with solder-coated tapes activates tape-to-tape soldering and decreases the contact resistance. The reduction of contact resistance by two orders in magnitude to tens of nΩm is comparable with the interstrand contact resistance in ITER Nb 3 Sn type conductors.