Magnetic and structural properties of the solid solution CuAl 2(1–x) Ga 2x O 4

Abstract

CuAl 2 O 4 is a ternary oxide spinel with Cu 2+ ions (s = 1/2) primarily populating the A-site diamond sublattice. The compound is reported to display evidence of spin glass behavior but possess a non-frozen magnetic ground state below the transition temperature. On the other hand, the spinel CuGa 2 O 4 displays spin glass behavior at ~ 2.5 K with Cu 2+ ions more readily tending to the B-site pyrochlore sublattice. Therefore, we investigate the magnetic and structural properties of the solid solution CuAl 2(1-x) Ga 2x O 4 examining the evolution of the magnetic behavior as Al 3+ is replaced with a much larger Ga 3+ ion. Our results show that the Cu 2+ ions tend to migrate from tetrahedral to octahedral sites as the Ga 3+ ion concentration increases, resulting in a concomitant change in the glassy magnetic properties of the solution. Results indicate glassy behavior for much of the solution with a general trend towards decreasing magnetic frustration as the Cu 2+ ion shifts to the B-site. However, the x = 0.1 and 0.2 members of the system do not show glassy behavior down to our measurement limit (1.9 K) suggesting a delayed spin glass transition. We suggest that these two members are additional candidates for investigation to access highly frustrated exotic quantum states.