Engineering topics

Hill, S. G.

Publications and source records attributed to Hill, S. G..

16 records

NASA NTRS1991

Advanced thermoplastic resins, phase 2

High temperature structural resins are required for use on advanced aerospace vehicles as adhesives and composite matrices. NASA-Langley developed polyimide resins were evaluated as high temperature structural adhesives for metal to metal bonding and as composite matrices. Adhesive tapes were prepared on glass scrim fabric from solutions of polyamide acids of the semicrystalline polyimide LARC-CPI, developed at the NASA-Langley Research Center. Using 6Al-4V titanium adherends, high lap shear bond strengths were obtained at ambient temperature (45.2 MPa, 6550 psi) and acceptable strengths were obtained at elevated temperature (14.0 MPa, 2030 psi) using the Pasa-Jell 107 conversion coating on the titanium and a bonding pressure of 1.38 MPa (200 psi). Average zero degree composite tensile and compressive strengths of 1290 MPa (187 ksi) and 883 MPa (128 ksi) respectively were obtained at ambient temperature with unsized AS-4 carbon fiber reinforcement.

Brown, A. M.↗

NASA NTRS1991

Advanced thermoplastic resins, phase 1

Eight thermoplastic polyimide resin systems were evaluated as composite matrix materials. Two resins were selected for more extensive mechanical testing and both were versions of LaRC-TPI (Langley Research Center - Thermoplastic Polyimide). One resin was made with LaRC-TPI and contained 2 weight percent of a di(amic acid) dopant as a melt flow aid. The second system was a 1:1 slurry of semicrystalline LaRC-TPI powder in a polyimidesulfone resin diglyme solution. The LaRC-TPI powder melts during processing and increases the melt flow of the resin. Testing included dynamic mechanical analysis, tension and compression testing, and compression-after-impact testing. The test results demonstrated that the LaRC-TPI resins have very good properties compared to other thermoplastics, and that they are promising matrix materials for advanced composite structures.

Hendricks, C. L.↗

NASA NTRS1989

Space station protective coating development

A generic list of Space Station surfaces and candidate material types is provided. Environmental exposures and performance requirements for the different Space Station surfaces are listed. Coating materials and the processing required to produce a viable system, and appropriate environmental simulation test facilities are being developed. Mass loss data from the original version of the atomic oxygen test chamber and the improved facility; additional environmental exposures performed on candidate materials; and materials properties measurements on candidate coatings to determine the effects of the exposures are discussed. Methodologies of production, and coating materials, used to produce the large scale demonstration articles are described. The electronic data base developed for the contract is also described. The test chamber to be used for exposure of materials to atomic oxygen was built.

Pippin, H. G.↗

NASA NTRS1987

Evaluation of high temperature structural adhesives for extended service, phase 5

The evaluation of 3 experimental polymers from NASA-Langley and a commercially produced polymer from Mitsui Toatsu Chemicals as high temperature structural adhesives is presented. A polyphenylquinoxaline (PPQ), polyimide (STPI/LaRC-2), and a polyarylene ether (PAE-SO2) were evaluated as metal-to-metal adhesives. Lap shear, crack extension, and climbing drum peel specimens were fabricated from all three polymers and tested after thermal, combined thermal/humidity, and stressed hydraulic fluid (Skydrol) exposure. The fourth polymer, LARC-TPI was evaluated as an adhesive for titanium honeycomb sandwich structure. All three experimental polymers performed well as metal-to-metal adhesives from 219 K (-65 F) to 505 K (450 F), including humidity exposure. Structural adhesive strength was also maintained at 505 K for a minimum of 3000 hours. LaRC-TPI was evaluated as a high temperature (505 K) adhesive for titanium honeycomb sandwich structure. The LaRC-TPI bonding process development concentrated on improving the honeycomb core-to-skin bond. The most promising approach of those evaluated combined a LaRC-TPI polymer solution with a semi-crystalline LaRC-TPI powder for adhesive film fabrication and fillet formation.

Hendricks, C. L.↗

NASA NTRS1985

Evaluation of high temperature structural adhesives for extended service, phase 4

The evaluation of three phenylquinoxaline polymers as high temperature structural adhesives is presented. These included an experimental crisskubjabke oiktner (X-PQ) and two experimental materials (PPQ-2501) and (PPQ-HC). Lap shear, crack extension, and climing drum peel specimens were fabricated from all three polymers, and tested after thermal, combined thermal/humidity, and stressed Skydrol exposure. All three polymers generally performed well as adhesives at initial test temperatures from 219K (-67 F) to 505K (450 F) and after humidity exposure. The 644K (700 F) cured test specimens exhibited superior Skydrol resistance and thermal stability at 505K (450 F) when compared to the 602K (625 F) cured test specimens.

Hendricks, C. L.↗

NASA NTRS1985

Evaluation of a high temperature adhesive for fabricating graphite/PMR-15 polyimide structures

Tests are conducted to measure shear strength, shear modulus and flatwise tensile strength of the A7F (amide-imide modified LARC-13) adhesive system. An investigation is also conducted to determine the effect of geometric material parameters, and elevated temperature on the static strength of standard joints. Single-lap and double-lap composite joints, and single, double and step lap composite to metal joints are characterized. A series of advanced joints consisting of preformed adherends, adherends with scalloped edges and joints with hybrid interface plies are tested and compared to baseline single and double-lap designs.

Hill, S. G.↗

NASA NTRS1984

Evaluation of high temperature structural adhesives for extended service

High temperature stable adhesive systems were evaluated for potential Supersonic Cruise Research (SCR) vehicle applications. The program was divided into two major phases: Phase I 'Adhesive Screening' evaluated eleven selected polyimide (PI) and polyphenylquinoxaline (PPQ) adhesive resins using eight different titanium (6Al-4V) adherend surface preparations; Phase II 'Adhesive Optimization and Characterization' extensively evaluated two adhesive systems, selected from Phase I studies, for chemical characterization and environmental durability. The adhesive systems which exhibited superior thermal and environmental bond properties were LARC-TPI polyimide and polyphenylquinoxaline both developed at NASA Langley. The latter adhesive system did develop bond failures at extended thermal aging due primarily to incompatibility between the surface preparation and the polymer. However, this study did demonstrate that suitable adhesive systems are available for extended supersonic cruise vehicle design applications.

Hendricks, C. L.↗

NASA NTRS1984

Evaluation of high temperature structural adhesives for extended service

The preliminary evaluation of crosslinked polyphenyl quinoxaline (X-PPQ), LARC-TPI, ethyl terminated polysulfone (ETPS), and crosslinked polyimide (X-PI) as adhesives is presented. Lap shear strength stability under thermal, combined thermal/humidity, and stressed and unstressed Skydrol exposure was determined. The X-PPQ, LARC-TPI, and X-PI exhibited good adhesive performance at 505K (450 F) after 1000 hours at 505K. These three polymers also performed well after exposure to combined elevated temperature/high humidity, as well as, to Skydrol while under stress. The ETPS exhibited good ambient temperature adhesive properties, but performed poorly under all other exposure conditions, presumably due to inadequate chain extension and crosslinking.

Hendricks, C. L.↗

NASA NTRS1983

Evaluation of high temperature structural adhesives for extended service

Hill, S. G.↗

NASA NTRS1982

Evaluation of high temperature structural adhesives for extended service

The evaluation, selection, and demonstration of structural adhesive systems for supersonic cruise research applications, and establishment of environmental durability of selected systems for up to 20,000 hours is described. Ten candidate adhesives were initially evaluated. During screening and evaluation, these candidates were narrowed to three of the most promising for environmental durability testing. The three adhesives were LARC-13, PPQ, and NR056X. The LARC-13 was eliminated because of a lack of stability at 505 K. The NRO56X was removed from the market. The LARC-TPI was added after preliminary evaluation and an abbreviated screening test. Only PPQ and LARC-TPI remained as the reasonable candidates late into the durability testing. Large area bond panels were fabricated to demonstrate the processibility of the selected systems. Specifications were prepared to assure control over critical material and process parameters. Surface characterization concentrated primarily upon titanium surface treatments of 10 volt chronic acid anodize, 5 volt chromic acid anodize and PASA-JELL. Failure analysis was conducted on lap shear adhesive bond failures which occurred in PPQ and LARC-13 test specimens after 10,000 hours at 505 K.

Hill, S. G.↗

NASA NTRS1981

Evaluation of high temperature structural adhesives for extended service

Eight different Ti-6Al-4V surface treatments were investigated for each of 10 candidate resins. Primers (two for each resin) were studied for appropriate cure and thickness and initial evaluation of bond joints began using various combinations of the adhesive resins and surface treatments. Surface failure areas of bonded titanium coupons were analyzed by electron microscopy and surface chemical analysis techniques. Results of surface characterization and failure analysis are described for lap shear bond joints occurring with adhesive systems consisting of: (1) LARC-13 adhesive, Pasa jell surface treatment; (2) LARC-13 adhesive, 10 volt CAA treatment; (3) PPQ adhesive, 10 volt CAA treatment; and (4) PPQ adhesive, 5 volt CAA treatment. The failure analysis concentrated on the 10,000 hr 505K (450 F) exposed specimens which exhibited adhesive failure. Environmental exposure data being generated on the PPQ-10 volt CAA and the LARC-TPI-10 volt CAA adhesive systems is included.

Hill, S. G.↗

NASA NTRS1981

Evaluation of high temperature structural adhesives for extended service

The long term thermal aging data initiated in Phase 1 is reported. All candidate adhesive systems have exhibited significant degradation in bond properties after 505K (450 F) 10,000 hour exposure. Failures appear to be adhesive in the oxide layer. Phase 2 chemical characterization, cure cycle studies, baseline data, preliminary specifications, and environmental exposure data generated on polyphenyquinoxaline is presented. Similar but limited data on LARC-13 and NR056X adhesives is reported.

Hill, S. G.↗

NASA NTRS1980

LARC-13 adhesive development

A LARC-13 type adhesive system was developed and property data obtained that demonstrated improved thermomechanical properties superior to base LARC-13 adhesive. An improved adhesive for 589 K (600 F) use was developed by physical or chemical modification of LARC-13. The adhesive was optimized for titanium and composite bonding, and a compatible surface preparation for titanium and composite substrates was identified. The data obtained with the improved adhesive system indicated it would meet the 589 K (600 F) properties desired for application on space shuttle components. Average titanium lap shear data were: (1) 21.1 MPa (3355 psi) at RT, (2) 13.0 MPa (1881 psi) at 600 F, and (3) 16.4 MPa (2335) after aging 125 hours at 600 F and tested at 600 F.

Hill, S. G.↗

NASA NTRS1980

Evaluation of high-temperature structural adhesives for extended service

Candidate high-temperature stable resin formulations were evaluated for adhesive properties when bonded to titanium treated with various surface preparations. The adhesive formulations included LARC-13, NR150 A2, NR150 B2, NR056X, FM-34, HR-602, and polyphenylquinoxaline. Eight titanium surface preparations were compared for resulting bond strength with the candidate adhesives. After initial evaluation, three adhesive systems (comprised of adhesive, primer, and titanium surface preparation) were selected for further screening. The screening (still in progress) includes cure-cycle optimization and bond properties from 219 K (-65 F) to 505 K (450 F), after isothermal aging at 505 K (450 F) up to 15,000 hours, and after humidity aging at 322 K 9120 F)/ 95 percent R. H. for up to 2000 hours. Larger-area bond capability of the three adhesive system can be demonstrated by fabrication of 30.5 cm (12 in) square titanium honeycomb sandwich and metal-to-metal bonded panels.

Hendricks, C. L.↗

NASA NTRS1980

LARC-13 adhesive development

The paper reports the results of a program whose objective was to modify physically and chemically LARC-13 resin in order to obtain an improved adhesive for 589 K applications. The project was directed, in particular, toward Space Shuttle applications such as the body flap in which the designers could take the advantage of the excellent strength-to-weight ratio of advanced composites. Improved resins were obtained by substitution of m, m-prime-diaminodiphenylmethane with metaphenylene diamine in the original LARC-13 chemistry. Test results for the new adhesives are presented.

Hill, S. G.↗

NASA NTRS1974

Development of polyphenylquinoxaline graphite composites

This exploratory program was divided into four basic tasks. The initial phase was devoted toward investigating processing variables associated with previously developed PPO resins. These polymers were derived from p-bis(phenyl glyoxalyl)benzene reacted with 3,3'-diamino benzidine and/or 3,3',4,4'-tetramino benzophenone. Four new phenyl quinoxaline polymers were synthesized and characterized in Tasks 2 and 3. These consisted of a hydroxyl group containing PPQ synthesized from 3,3'-diamino benzidine (DAB), m-bis(phenyl glyoxal)benzene and m-bis(p'-hydroxy phenyl glyoxalyl) benzene; a cyano group containing PPQ from the reaction of DAB and p-bis(p'-cyano phenoxy phenyl glyoxalyl)benzene; an end-capped block copolymer; and a polymer from the reaction of 3,3',4,4'-tetraamino benzo phenone and m-bis(phenyl glyoxalyl)benzene. The latter two polymers were chosen for composite studies in the latter two tasks of the program. Mechanical properties of the graphite reinforced PPQ composites were determined over the temperature range of +21 C to 316 C. Flexural strengths of the HMS graphite fiber composites were in excess of 8.97 X 10 to the 8th power N/sq m (130,000 psi) at +21 C (70 F) with over 50% strength retention at +316 C.

Hoggatt, J. T.↗