Development of polyphenylquinoxaline graphite composites

Abstract

This exploratory program was divided into four basic tasks. The initial phase was devoted toward investigating processing variables associated with previously developed PPO resins. These polymers were derived from p-bis(phenyl glyoxalyl)benzene reacted with 3,3'-diamino benzidine and/or 3,3',4,4'-tetramino benzophenone. Four new phenyl quinoxaline polymers were synthesized and characterized in Tasks 2 and 3. These consisted of a hydroxyl group containing PPQ synthesized from 3,3'-diamino benzidine (DAB), m-bis(phenyl glyoxal)benzene and m-bis(p'-hydroxy phenyl glyoxalyl) benzene; a cyano group containing PPQ from the reaction of DAB and p-bis(p'-cyano phenoxy phenyl glyoxalyl)benzene; an end-capped block copolymer; and a polymer from the reaction of 3,3',4,4'-tetraamino benzo phenone and m-bis(phenyl glyoxalyl)benzene. The latter two polymers were chosen for composite studies in the latter two tasks of the program. Mechanical properties of the graphite reinforced PPQ composites were determined over the temperature range of +21 C to 316 C. Flexural strengths of the HMS graphite fiber composites were in excess of 8.97 X 10 to the 8th power N/sq m (130,000 psi) at +21 C (70 F) with over 50% strength retention at +316 C.