Hoelzer, David T.

Publications and source records attributed to Hoelzer, David T..

At least 19 records
All sourcesNASA NTRSDOE OSTI
DOE OSTI2024

Report Summarizing the Mechanical Properties of a Large ODS Ferritic Alloy Ingot by Forging at High Temperatures for Future Mother Tube Production

Oxide dispersion strengthened (ODS) ferritic alloys are considered the benchmark fuel cladding and core structural material in advanced nuclear energy reactors that require high-temperature strength and creep properties and resistance to radiation damage. The ODS ferritic alloys including 14YWT are produced by mechanical alloying (MA), which is time-consuming and is associated with high manufacturing costs that are not beneficial to being used in advanced nuclear energy reactors. This report summarizes the accomplishments in FY24 in the INM program for producing an ODS ferritic alloy by high-deformation, high-temperature processing of reactive and ferritic alloy powders for advanced reactor fuel cladding applications. Following four hot forging experiments, it was concluded that several significant challenges were encountered that were difficult to overcome. These challenges were related to using high annealing temperatures for pressure assisted sintering processes to produce dense microstructures, but the high annealing temperatures result in long range diffusion of Ti through the bcc Fe lattice and react with the YIG particles that are distributed on the prior surfaces of the ferritic alloy powders. In addition, it was determined that the high deformations induced by forging at high temperatures were not very effective for fracturing the reactive YIG particles into smaller particles and distributing them into the interior of the ferritic alloy powders. Spark plasma sintering was attempted for shortening the time at high temperatures, which led to full densification but the microstructure characterization results still showed that Ti atoms diffused over long distances in the bcc Fe lattice and reacted with the YIG particles. Finally, a short 30 minute high intensity ball milling experiment was conducted on blended 14WT and YIG powders for inducing severe deformations that caused the initially spherical powders of 14WT decorated with the YIG particles on the surfaces to transform to flakes and fracturing of YIG particles into smaller particles that were incorporated into the bcc Fe lattice. Two forgings were performed with the high intensity milled powders: first annealing for 20 minutes at 850ºC followed by forging and second annealing for 20 minutes at 1,100ºC followed by forging. At 850ºC, Ti atoms are effectively immobile, thus allowing for densification albeit incomplete. The deformation by forging after annealing for 20 minutes at 1,100ºC favored dynamic recrystallization processes that led to nano-size grains with very high stored energy due to high dislocation density. The corresponding VH data showed significant hardening that correlated with estimated strengthening of ~1650 MPa. This hybrid processing approach combining high intensity ball milling of powder with annealing and forging showed the most promise for producing an oxide dispersing strengthened ferritic alloy.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Nanostructured Alumina-Forming Austenitic Alloy (NAFA) Production Using Advanced Manufacturing

Alumina-forming austenitic (AFA) alloys are well known for their exceptional corrosion-resistant properties due to the formation of a dense oxide scale beneficial in their application as a nuclear material. However, use of the alloys in core material applications is limited due to the high nickel-transmutation and helium generation rate in service, leading to swelling and reduced lifetimes. Enhancing the sink strength to pin gas bubbles and increasing gas management of the material may mitigate many of the degradation phenomena expected during alloy deployment (such as high-temperature helium embrittlement and cavity swelling for lead-cooled fast-reactor applications). Nanostructured materials are usually produced using a time-consuming and expensive batch process like mechanical alloying to achieve the fine homogenous distribution of nanoprecipitates throughout the matrix material. Integrating the nanoprecipitates in modern additive manufacturing processes has proven difficult, as the required nano-sizes or number densities cannot be achieved simultaneously. Efforts to increase the number density of precipitates by adding more precipitate-forming rare-earth elements led to agglomeration of such elements, while the nano-sized precipitates did not form in sufficient quantity when not enough rare-earth element was use. In this work a novel approach to advanced manufacturing and the fabrication of Nanostructured AFA (NAFA) materials was chosen. A dual precipitate-forming NAFA steel with a chemistry more suitable for advanced reactor applications was produced to create an environmentally resistant, high-sink-strength austenitic alloy for advanced reactor cladding applications.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Characteristics of oxide-dispersion strengthened alloys produced by high-temperature severe deformation

This study is to explore an economically attractive and technically feasible processing method for oxide-nanoparticle strengthened alloys for fusion reactor application. Despite many scientific merits of the advanced oxide-dispersion strengthened (ODS) alloys, such as the nanostructured ferritic alloy (NFA) 14YWT, the only viable production path for a high-quality NFA is the high-power mechanical alloying process. This process is often a multi-day high-speed ball milling of alloy powder with a small quantity of yttria (Y 2 O 3 ) powder, followed by the milled-powder consolidation using extrusion or other methods and additional thermomechanical processing (TMP) for property control. This complex production path, including the low-temperature mechanical alloying in particular, has limited technical advancement toward the cost-effective and scale-up production of ODS alloy components. To overcome such a practical limitation, we proposed to explore alternative low-cost processing routes using traditional thermomechanical processing (TMP) method only. Further, a series of continuous TMP cycles, which were designed to impose high-temperature severe plastic deformation (HT-SPD) conditions to the consolidated powder mixtures, were applied to achieve the effective distribution of oxide particles in nanograin structure and thus desirable mechanical properties. Since the reduced-activation ferritic-martensitic (RAFM) alloy powders (Fe-10Cr and Fe-14Cr alloys with various Y contents) are available in our inventory, we focused to utilize the new solid-state synthesis approach for controlling oxide (oxygen source) dissolution and nanoscale clustering in nanograin structure in those alloys. A combination of powder consolidation at 900 °C and continuous thermomechanical activation at 600 °C yielded two essential ODS alloy microstructure contents–nanograin structure and nanoparticle distribution–and thus demonstrated a good combination of strength and ductility.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Characterization of Large Batch 14YWT Heat (NFA-2) for JOYO Irradiations (Rev.1)

The development and deployment of advanced cladding materials in advanced reactors requires the collection of relevant performance data for each cladding concept. Novel cladding concepts typically undergo significant innovation and iteration over the course of their development, and intention should be given to providing a snapshot of present performance. Thus, a modern heat of the nanostructured ferritic alloy (NFA) 14YWT is produced using state-of-the-art procedures for impurity minimization combined with thermomechanical processing methods designed to optimize fracture toughness, tensile strength, and ductility. This new heat of 14YWT, NFA-2, will provide the Advanced Fuels Campaign with adequate material for upcoming irradiation and mechanical testing campaigns. This report outlines procurement of new gas atomized 14YWT powder, production of four new bars of 14YWT, and subsequent mechanical and microstructural property characterization.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗
DOE OSTI2024

Status report on HFIR irradiation of optimized alumina forming alloys

Properties of FeCrAl alloys under neutron irradiation are of interest because of these materials’ potential application as accident-tolerant fuel cladding in nuclear systems. In parallel, alumina-forming austenitic (AFA) alloys are of interest for use as structural materials in advanced nuclear systems for their potential higher resistance to embrittlement and high-temperature steam oxidation resistance. An irradiation campaign for fiscal year 2024 has been developed under the Advanced Fuels Campaign to perform irradiation testing of various FeCrAl and AFA alloys in Oak Ridge National Laboratory’s High Flux Isotope Reactor (HFIR). The goals of this irradiation campaign are to (1) study the impact of minor alloying elements on the neutron-irradiated mechanical properties of FeCrAl alloys and (2) collect neutron-irradiated mechanical properties on AFA alloys for comparison with those of FeCrAl alloys. This campaign will include both tensile and fracture toughness specimens tested following HFIR irradiation at temperatures representative of normal operating conditions in light-water reactors. The pre-irradiation characterization to date, the irradiation plan for the FeCrAl and AFA specimens, and the subsequent post-irradiation experimental test plan are presented in this report, along with the status of HFIR builds and scheduled insertion dates.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Nanostructured Alumina Forming Austenitic Alloy (NAFA) Production Using Mechanical Alloying and High-Temperature Consolidation

Alumina-forming austenitic (AFA) alloys are a promising class of nuclear materials because of their high-temperature oxidation/corrosion resistance and mechanical properties. Unfortunately, these alloys are limited in use for core material applications, and they are specifically limited for use as nuclear fuel cladding because of their high Ni-transmutation and helium generation rate in-service. Improving these alloys through a fine dispersion of oxide precipitates and thus increasing the effective irradiation sink strength of the alloy system may mitigate many of the degradation phenomena expected during alloy deployment. These phenomena include high-temperature helium embrittlement and cavity swelling for lead-cooled fast reactor applications. This work effort uses combination of conventional and advanced manufacturing approaches are being used to fabricate nanostructured AFA (NAFA) materials. As the first objective of this initiative, a conventional AFA was modified using mechanical alloying and extrusion to alter the precipitation characteristics to include a fine dispersion of nanoscale oxides intended to serve as traps for irradiation-induced point defects and transmuted He within the lattice. This analysis compared the efficacy of the conventional mechanical alloying and extrusion approach with the unalloyed AFA consolidated approach using hot isostatic pressing (HIP). It was found that, although the mechanical alloying approach is successful in producing a fine distribution of oxides within the first nanostructured AFA (NAFA-1), the distribution is heterogeneous because of the mild milling parameters used to prevent cold welding of powder to the spherical milling media. The additional dispersion of oxides, coupled with a higher volume fraction of other secondary phases in the NAFA-1, produces higher alloy strengths that range up to 600°C in comparison to the unalloyed HIP AFA, thus exceeding the operating temperature of lead-cooled fast reactors. However, the strength of the NAFA-1 is lower than that of the HIP AFA at 800°C, which is presumed to be a function of increased secondary phases from the nonoptimized AFA chemistry. Future work is planned on a newly procured NAFA-2 chemistry that is more suitable for advanced reactor applications exploring new manufacturing routes.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Progress on Producing an ODS Ferritic Alloy by High Deformation Processing of Reactive Powders

Oxide dispersion-strengthened (ODS) ferritic alloys, such as 14YWT, are considered as benchmarks for fuel cladding and core structural materials in advanced nuclear energy reactor systems that require high temperature strength and creep properties as well as resistance to radiation damage. Unfortunately, the popular processing method of mechanical alloying (MA) is time-consuming, incurs high manufacturing costs, and typically produces anisotropy in the microstructure and mechanical properties of ODS ferritic alloys. These considerations hinder their acceptance in many high-performance, high-temperature materials for advanced nuclear energy reactors. This work package is pursuing an alternative solid-state processing to MA involving high deformation at high temperatures for producing an ODS ferritic alloy for fuel cladding. This report summarizes the concept for this processing method and the progress toward selecting the reactive and ferritic alloy powders, preparing 316L stainless steel cans for filling with blended powder followed by degassing, and choosing the heat treatments and forging parameters for performing the first two forging experiments. The preliminary results of optical microscopy performed on polished samples that were cut in three orthogonal directions revealed remnant porosity in both samples. The analysis of the porosity using ImageJ revealed a lesser amount of ~2.49% in the HiLoMe-1 sample that was processed with the three heat treatments and forging parameters compared to ~5.70% for the Hi-1 sample that was processed with only the first sintering heat treatment and forging parameter. These initial results will provide insights that can be leveraged to improve the densification of the powders in future forging experiments that will be continued into FY24 for determining the optimum heat treatments and forging parameters coupled with detailed microstructure characterization studies for producing the ODS ferritic alloy.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2023

Progress on Design and Production of Oxide Dispersion–Strengthened Alumina-Forming Austenitic Alloys for Nuclear Applications

Alumina-forming austenitic (AFA) alloys are a promising class of nuclear materials due to their high-temperature oxidation/corrosion resistance and mechanical properties. Unfortunately, these alloys are limited in use for core material applications, specifically in their use as nuclear fuel cladding. Improving these alloys through a fine dispersion of oxide precipitates and thus increasing the effective irradiation sink strength of the alloy system may mitigate many of the degradation phenomena expected during alloy deployment (such as high-temperature helium embrittlement for lead-cooled fast reactor applications). This work package has started using a combination of conventional and advanced manufacturing approaches to the fabrication of oxide dispersion–strengthened (ODS) AFA materials. As such, this report summarizes progress to date in the fabrication of new compositions of these ODS AFA materials with a focus on reactor-specific design and a multifaceted manufacturing approach. Two different compositions of AFA gas-atomized powders were procured, and 200 g of each have been prepared using mechanical alloying with the expectation of high-temperature consolidation in Q1 of FY24. In addition, an approach to use reactive cover gases to promote additional precipitate formation has been developed for implementation in FY24 as a direct comparison with conventionally manufactured alloys.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2023

Downselection and Basic Properties of Additively Manufactured ODS Alloys

In the AMMT program the work package for development of new materials aimed to explore the advanced manufacturing techniques that are feasible for the manufacturing of advanced materials components. A merit-based feasibility study was attempted to identify an accelerated development path for dispersion strengthened (ODS) alloys by creatively combining additive manufacturing (AM) technologies with the recent advances in ODS materials and traditional manufacturing technologies. For the fiscal year, the primary tasks were focused to develop additive manufacturing (AM) and post-build processing route for oxide dispersion strengthened (ODS) ferritic (Fe-Cr alloy or 14YWT) and austenitic (Fe-Cr-Ni alloys or 316L and 316H) alloys and to perform basic microstructural and mechanical characterizations to provide feedbacks to the alloy and processing design. Further, the multi-laboratory effort created collaboratively a decision criteria matrix to evaluate and downselect the new materials processed by advanced manufacturing methods. This report is to describe the ODS alloy processing routes combining AM processes and post-build thermomechanical treatments, mechanical and microstructural characteristics of the newly developed materials, and the application results of the decision criteria matrix for the AM ODS alloys including a downselected material and feasible processing route. Key mechanical test results including tensile strength, tensile ductility, and fracture toughness data and are reported and explained. Higher strength was measured from the ferritic ODS alloys, while higher ductility and fracture toughness were measured from the austenitic ODS alloys. Many of the decision criteria were scored the same for the AM ferritic and austenitic ODS alloys, however, the generally known fact that the austenitic alloys have higher corrosion resistance and significantly better ductility. Although these scores are not significantly different to make them highly discernable, the austenitic ODS alloys were downselected to be the primary materials group in the future research on ODS materials in AMMT program.

36 MATERIALS SCIENCE↗
DOE OSTI2023

High-Temperature Creep Behavior of Thin-Walled FeCrAl Alloy Tubes

This report summarizes measured creep properties for FeCrAl alloy C26M measured using subsized specimens machined from prototypic thin-walled tubes. A representative tube fabricated in a previous large batch production effort was machined into dual-gauge axial specimens using electrical-discharge machining. Creep tests, comprising strain-rate jump tests (SRJ), jump stress (JS) and constant-stress (CS) tests, were conducted at temperatures ranging from 600-900ºC to determine creep mechanisms (elucidated from stress exponents) and activation energies to compare with prior data available in the literature at temperatures up to 650ºC. It was found that the results from the SRJ tests indicated that the highest stress exponent of 5.8 occurred at 600ºC, which decreased to the lowest stress exponent of 2.5 at 700ºC. At higher temperatures, the stress exponents increased slightly to a range of 2.9 to 4.3 between 750ºC and 900ºC. The high stress exponent value of 5.8 suggested dislocation glide creep mechanisms dominated creep deformation at 600ºC since high stress values were measured. The low stress exponent of 2.5 at 700ºC suggested diffusional creep mechanisms start to occur that aid in dislocation cross-slip and climb mechanisms. The slightly higher stress exponents of 2.9 to 3.9 may suggest different contributions of creep deformation mechanisms based on diffusional processes associated with Nabarro-Herring and Coble creep and dislocation creep that involve thermally activated cross-slip and climb mechanisms. These deformation mechanisms could have also been affected by the development of recovery and/or recrystallization processes in the microstructure of the C26M2 specimens. From the SJ and single CS tests, two sets of creep activation energies were calculated. The steady state creep values obtained from the SJ tests showed several abnormalities especially with the data at 850ºC. The comparison of the creep activation energies between the data from the SJ and CS tests showed higher creep rates for the SJ tests than the CS tests, indicating microstructure softening occurred in the C26M2 specimens during the SJ tests that led to the higher creep rates at stresses above the initial stress of 10 MPa. For the CS tests, the results showed steady increases in MCR with increasing temperature at each stress. The best linear fit to the MCR values at each stress was with data obtained at 800ºC, 850ºC and 900ºC. The lowest Q c value of 130.8 KJ/mole was observed with the highest stress of 25 MPa. As stress was lowered, the Q c values increased continuously to the highest value of 188.2 KJ/mole at 10 MPa. This trend suggests that the dominant creep mechanism is diffusional based dislocation climb since the decreasing activation energies with increasing stress promotes easier dislocation climb around obstacles. The comparison between the SJ and CS tests indicates that the best type of creep test performed on FeCrAl alloys such as C26M2 is the single CS test.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Metal forming and working of stabilized nanocrystalline Cu-Ta for electrical contacts

The commercialization of nanocrystalline metals and alloys is currently entering a renaissance period. Many of the processing and consolidation challenges that have haunted them are now more fully understood, opening the doors for stabilized nanocrystalline metals to be produced on a bulk scale. While challenges remain, the increased volume at which these materials are being supplied is for the first time allowing for investigations into more traditional methods of metal working, such as extruding, rolling, forming, and forging. Recently, the manufacturing science has been developed to allow nanocrystalline Cu-Ta alloys to progress to this point. This article therefore builds upon the last decade of evolutionary progression within the family of stabilized nanocrystalline Cu-Ta alloys by presenting some of the first findings related to scaled powder synthesis, production of billets, thin sheets, and foils. Here, the mechanical performance and physical properties relevant to forming electrical contacts and pins including, tensile, J-integral fracture toughness, Charpy Impact, bi-axial tension, and conductivity are reported. This introductory investigation into forming such a novel material, provides evidence to these alloys potential at bridging the gap between being a scientific curiosity to that of a real engineering material.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Understanding the Solution Dynamics and Binding of a PVDF Binder with Silicon, Graphite, and NMC Materials and the Influence on Cycling Performance

The impact of the binding, solution structure, and solution dynamics of poly(vinylidene fluoride) (PVDF) with silicon on its performance as compared to traditional graphite and Li 1.05 Ni 0.33 Mn 0.33 Co 0.33 O 2 (NMC) electrode materials was explored. Through refractive index (RI) measurements, the concentration of the binder adsorbed on the surface of electrode materials during electrode processing was determined to be less than half of the potentially available material resulting in excessive free binder in solution. Using ultrasmall-angle neutron scattering (USANS) and small-angle neutron scattering (SANS), it was found that PVDF forms a conformal coating over the entirety of the silicon particle. This is in direct contrast to graphite–PVDF and NMC–PVDF slurries, where PVDF only covers part of the graphite surface, and the PVDF chains make a network-like graphite–PVDF structure. Conversely, a thick layer of PVDF covers NMC particles, but the coating is porous, allowing for ion and electronic transport. The homogeneous coating of silicon breaks up percolation pathways, resulting in poor cycling performance of silicon materials as widely reported. These results indicate that the Si–PVDF interactions could be modified from a binder to a dispersant.

25 ENERGY STORAGE↗
DOE OSTI2022

High-Temperature Tensile and Creep Test Results on Thin Wall Tube Specimens of ODS Alloys 14YWT and OFRAC

High-temperature tensile and strain rate jump (SRJ) creep tests were conducted on axial specimens fabricated from thin wall tubes of the oxide dispersion strengthened (ODS) alloys 14YWT and OFRAC. The dimensions of the 14YWT thin wall tube was 10.7 mm OD, 0.5 mm WT and 0.92 m and of the OFRAC thin wall tube was 8.5 mm OD + 0.5 mm WT and 1.78 m in length. The axial specimens fabricated from the thin wall tubes were based on a dual-gauge design with gauge dimensions of 4 mm long and 2 mm wide. The tensile tests were conducted in air at 800ºC, 900ºC and 1,000ºC and the SRJ creep tests were conducted in air at 800ºC. Two axial specimens were used in each tensile and SRJ creep tests. The results of the tensile tests showed much lower yield stress (YS) compared to ultimate tensile strength (UTS) indicative of large work hardening properties. The results showed the UTS of OFRAC was higher than that of 14YWT by ~35 MPa at 800ºC. At 900ºC, the UTS of OFRAC and 14YWT was similar at 900ºC and at 1000ºC, the UTS of 14YWT was higher than that of OFRAC by ~10 MPa. The ductility properties of OFRAC were greater than that of 14YWT with higher values of uniform elongation (UE) and total elongation (TE) at all tensile test temperatures. The creep properties of 14YWT and OFRAC were evaluated by the strain rate jump test method at 800ºC. The stress exponent (n) for creep was obtained from the SRJ test data by plotting the values of the log strain rate against the log stress, which is measured from the stress-strain curve generated during the SRJ test. The results showed the highest stress exponents of n = 19.8 and n = 35.0 were measured from the two SRJ tests on 14YWT. The stress exponent measured from one successful SRJ test on OFRAC was n = 13.3, which was lower than that of 14YWT. Nevertheless, these high values of stress exponent are consistent with ODS ferritic alloys such as 14YWT and OFRAC since they indicate dislocation-particle interactions are the dominant creep mechanism for specific ranges of temperature and stress. The results obtained from the tensile and SRJ creep tests conducted on axial specimens in this study indicate that 14YWT and OFRAC retain high strengths at temperatures up to 1,000ºC and good creep performance at 800ºC.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Creep Behavior and Phase Equilibria in Model Precipitate Strengthened Alumina-Forming Austenitic Alloys

Abstract Creep-rupture behavior and microstructural response in alumina-forming austenitic (AFA) alloys with two different precipitation strengthening mechanisms, “Laves-phase + M 23 C 6 carbide” and “coherent L1 2 γ′-Ni 3 (Al,Ti),” were explored as “model” cases of multi-phase, multi-scale heat-resistant AFA alloys for 650–750°C use. These alloys will be used to guide and verify computational alloy design and life-prediction modeling under an on-going eXtremeMAT project through the Office of Fossil Energy and Carbon Management, US Department of Energy. Computational thermodynamics were used to design and predict the amounts of strengthening and deteriorating secondary phases at 750°C. Creep-rupture lives of the alloys tested at 750°C and 100 MPa were in a range of 4000–9000 h, and the microstructure at the gage/grip after creep-rupture testing was compared with isothermally aged alloys for 1500 h, as well as the calculated phases. Detailed microstructure characterization includes phase identification, volume fraction measurement, and compositional analysis, which were correlated with the creep-rupture properties. High-temperature oxidation resistance was also screened and compared with commercial, chromia-forming heat-resistant steels. These model alloys also provide the basis for further design and optimization of next generation AFA alloys with improved creep resistance.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Competitive adsorption within electrode slurries and impact on cell fabrication and performance

We ask why do battery researchers use 10-20 wt% binder in research cells when commercial chemistries use much less? This report seeks to explore this question by understanding the ordering and structure of polyimide binder with a silicon/pitch-carbon black electrode system. Correlating the effect of binder concentration on electrode architecture and electrochemical properties is vital to enhancing silicon anode cycle and calendar life. Using ultra-small angle neutron scattering (USANS) and binder adsorption isotherms an optimal region of polyimide (PI) binder coverage was found. Further, there is a preferential adsorption of PI to carbon black that has to be completed before PI binds to the silicon. Optimizing the concentration of binder leads to a 50% increase in capacity due to the optimization of binder-silicon-carbon interactions.

25 ENERGY STORAGE↗
DOE OSTI2021

Bubble formation in helium-implanted nanostructured ferritic alloys at elevated temperatures

Helium bubble formation was examined by scanning/transmission electron microscopy (S/TEM) in Fe-9/10Cr binary alloys and two dispersion strengthened nanostructured alloys (CNA3 and 14YWT containing 5–10 nm diameter carbide and oxide particles, respectively) after ex-situ and in-situ He implantation to ~10,000 appm at 500 to 900 °C. The combination of high-resolution STEM images and electron energy loss spectroscopy (EELS) revealed that the Y-Ti-O nanoparticles in 14YWT were uniformly distributed and exhibited a one-to-one relationship for bubble attachment to the nanoclusters. In the in-situ experiment at 900 °C, grain boundary cracking was severe in the Fe-10Cr model alloy, but not in the nanostructured alloys. From 500 to 900 °C, the bubble size generally increased with increasing irradiation temperature, while the bubble density decreased with increasing temperature. At the same temperatures, the bubble size in the implanted materials was in the order of Fe-9/10Cr > CNA3 > 14YWT, while the bubble density showed the opposite order. The observed bubble number densities for the nanostructured alloys are comparable to the nanoparticle density, suggesting that the nanoparticles in both alloys were effective in trapping He. Overall, our results indicate that very high He concentrations can be managed in nanostructured alloys by sequestering the helium into smaller bubbles (which leads to a lower volume swelling value) and to shield He from the grain boundaries. This can be attributed to the much higher sink strength associated with the nanoclusters or the He trapping ability between different types of nanoclusters.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Summary of Previous Mechanical Test Data on ODS Alloys 14YWT and OFRAC up to 1000ºC

The Nanostructured Ferritic Alloys (NFA) 14YWT and OFRAC were developed for future fission and fusion nuclear energy reactors requiring high-temperature mechanical properties that are tolerant to extreme neutron irradiation environments. The NFA contain a high concentration of Ti-, Y- and O-enriched nanoclusters (NC) and ultra-fine grains to achieve high temperature strength and creep properties and high sink strength for trapping irradiation induced point defects to minimize hardening and swelling and transmutated He atoms to form intragranular nano-size bubbles that prevent formation of coarse bubbles on grain boundaries that cause embrittlement. The mechanical properties of 14YWT and OFRAC have been acquired from tensile and creep tests conducted in the past at Oak Ridge National Laboratory. The development of 14YWT started in 2000, resulting in the production of numerous heats. Tensile properties were obtained from eleven heats of 14YWT from room temperature to 800ºC. Tensile data for the SM10 heat of 14YWT was extended to 1,000ºC. Initial development of OFRAC occurred in 2016. Tensile tests conducted from room temperature to 800ºC revealed similar properties of OFRAC with those obtained from the newer generation of 14YWT heats. The creep properties of 14YWT-SM10 evaluated using constant stress tensile and load time-to-failure tests at 800ºC showed low minimum creep rates with stresses of 200 and 100 MPa. The single time-to-failure test of 14YWT-SM10 at 800ºC and 100 MPa was terminated after 20,357 hours with no specimen failure and a low creep strain of ~0.24 %. The creep properties of OFRAC determined from strain-rate jump tests at were similar those of 14YWT-SM10. The stress exponent for 14YWT and OFRAC at 800ºC are similar and are consistent with threshold stress behavior. Since both 14YWT and OFRAC are candidates for fuel cladding in future fast reactors, several fabrication studies were recently conducted and have successfully demonstrated that thin wall tubes can be fabricated from 14YWT and OFRAC by cold pilger rolling and high precision tube rolling. The high temperature mechanical properties and feasibility of fabricating thin wall tubes make 14YWT and OFRAC candidates for application as heat pipes in advanced micro-reactors. The purpose of this report is to summarize the previously obtained tensile and creep data at temperatures up to 1000ºC for NFA 14YWT and OFRAC that have been acquired over the past 20 years at ORNL.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗