Enhancement of Nanostructured Ferritic Alloy 14YWT Properties via Heat Treatment for Post-Consolidation Processing

The nanostructured ferritic alloy 14YWT is a promising candidate for in-core use in generation IV nuclear reactors, due to a dense dispersion of insoluble, ultrafine-scale Y-Ti-O nano-oxides, which provide a high degree of irradiation tolerance and thermal stability. This work investigates the effects of heat treatment on the workability of 14YWT, along with the effect of processing history on abnormal grain structures and radial microstructural uniformity. In this study, a 14YWT rod consolidated at 850 °C was heat treated in argon at 1100 °C, 1150 °C, 1200 °C, or 1250 °C for 1 or 8 hours and changes in mechanical properties and microstructure were examined using microhardness and electron backscattered diffraction (EBSD). Two distinct types of large abnormal grains were observed, each with unique processing origins, including one with high and the other with low strain energy. Consolidation via direct extrusion resulted in radial microstructural gradients, where the center of the rod was softer with larger grain sizes and lower strain energies. These gradients persisted and intensified throughout heat treatment. Based upon this work, the recommended heat treatment for increased workability with minimal microstructural change is 1150 °C for 1 hours.

36 MATERIALS SCIENCE↗

Extensive nanoprecipitate morphology transformation in a nanostructured ferritic alloy due to extreme thermomechanical processing

Nano-oxide precipitates in a modern nanostructured ferritic alloy were investigated after extreme thermomechanical processing into a thin-walled tube geometry. It was found that the morphology of the precipitates changed from spherical to rod-shaped, with some increasing to aspect ratios of up to 9, despite the precipitate volume fraction (0.3%) and number density (> 10 23 m -3 ) of precipitates remaining unchanged. High-resolution electron microscopy showed that the precipitates likely remained coherent with the Fe-matrix, while atom probe tomography confirmed that the precipitate compositions remained unaffected by the transformation. The morphological change was attributed to the shearable nature of the (Y,Ti,O)-rich precipitates, indicating they should be considered as “soft” obstacles to dislocation motion. The elongation was most pronounced in larger (>5 nm) precipitates, which may be caused by preferential dissolution of the smallest (1–3 nm) precipitates followed by the competition between re-precipitation and solute diffusion to larger precipitates during recovery heat treatments.

36 MATERIALS SCIENCE↗

Shear Punch Testing of Neutron-Irradiated HT-9 and 14YWT

Shear punch mechanical testing was performed on neutron-irradiated HT-9 and 14YWT alloys, comparing the traditional ferritic/martensitic steel with the advanced oxide dispersion strengthened nanostructured ferritic alloy. The samples were irradiated at various temperatures between 380°C and 520°C. In HT-9, on increasing the irradiation temperature, the 1% offset shear stress and maximum shear stress decreased. The advanced 14YWT alloy was less sensitive to irradiation temperature with respect to irradiation hardening. However, it still exhibited irradiation hardening at each temperature.

36 MATERIALS SCIENCE↗