Exploring uranium oxidation in glue vapor to help avoid catastrophic slivers on NIF targets

Depleted uranium (DU) hohlraums are utilized for indirect drive fusion experiments at Lawrence Livermore National Laboratory. The production process for DU hohlraums is intricate, involving complex sputtering, machining, and leaching techniques. Achieving low-stress and defect-free hohlraums presents significant challenges. Recent failures have revealed that some uranium flakes, known as slivers, detach from the diagnostic windows and fall onto the capsule. These catastrophic failures were observed only after target assembly, leading to the hypothesis that oxidation of the DU by glue vapor might be the cause. A study investigating the impact of glue vapor on DU hohlraums found that spallation occurred in three out of seven sample hohlraums after three weeks. The slivers observed in these samples were consistent with those seen in assembled targets. This marks the first experimental reproduction of such catastrophic slivering failures. Consequently, future studies can now focus on sliver mitigation and the precise diagnosis of the failure mode.

70 PLASMA PHYSICS AND FUSION TECHNOLOGY↗

DOE OSTI2022

First graded metal pushered single shell capsule implosions on the National Ignition Facility

Graded metal pushered single shell (PSS) capsules are predicted to be a viable alternative to low-Z capsule indirect drive inertial confinement fusion (ICF) implosions for achieving high fusion yields [MacLaren et al., Phys. Plasmas 28, 122710 (2021)]. The first experiments with Be/Cr-graded metal PSS capsules indicate that the implementation of the principle design feature, the graded density inner metal layer, has succeeded in producing a stable implosion with performance in agreement with predictions. With 50% Cr concentration in the pusher, PSS capsules have greater than ~2× higher shell densities during stagnation for enhanced core confinement and radiation trapping at ~35% lower shell implosion velocities than low-Z capsules. High-energy >30 keV inflight shell radiography recorded 215 km/s implosion velocities and show that implosion Legendre mode P 2 asymmetry can be tuned via inner-to-outer beam wavelength separation, similar to other implosions. Shell radiographs and neutron core images show similar P 2 asymmetry, suggesting no symmetry swings between peak implosion velocity and stagnation times. Despite the modest implosion velocities, gas-filled deuterium–tritium capsule implosions generate 10 15 neutron yields at relatively modest core ion temperatures of 2.75 keV, indicating that in spite of the high-density inner layer, the implosions have been stabilized by the design density gradient. When compared with hydrodynamic simulations, the measured yield-over-simulated is 35% due to fuel–pusher mix and other perturbations such as the capsule fill tube. Finally, simple analytical scalings of hot spot pressure and neutron yield show that PSS implosions reach similar performance at lower implosion velocities and higher shell densities to low-Z ICF capsules.

70 PLASMA PHYSICS AND FUSION TECHNOLOGY↗