Exploring uranium oxidation in glue vapor to help avoid catastrophic slivers on NIF targets

Abstract

Depleted uranium (DU) hohlraums are utilized for indirect drive fusion experiments at Lawrence Livermore National Laboratory. The production process for DU hohlraums is intricate, involving complex sputtering, machining, and leaching techniques. Achieving low-stress and defect-free hohlraums presents significant challenges. Recent failures have revealed that some uranium flakes, known as slivers, detach from the diagnostic windows and fall onto the capsule. These catastrophic failures were observed only after target assembly, leading to the hypothesis that oxidation of the DU by glue vapor might be the cause. A study investigating the impact of glue vapor on DU hohlraums found that spallation occurred in three out of seven sample hohlraums after three weeks. The slivers observed in these samples were consistent with those seen in assembled targets. This marks the first experimental reproduction of such catastrophic slivering failures. Consequently, future studies can now focus on sliver mitigation and the precise diagnosis of the failure mode.