Hu, Enyuan

Publications and source records attributed to Hu, Enyuan.

At least 55 records · Page 3
All sourcesNASA NTRSDOE OSTI
DOE OSTI2023

Enhancing lithium storage performance of bimetallic oxides anode by synergistic effects

Spinel bimetallic transition metal oxide anode such as ZnMn 2 O 4 , has drawn increasing interest due to attractive bimetal interaction and high theoretical capacity. While it suffers from huge volume expansion and poor ionic/electronic conductivity. Nanosizing and carbon modification can alleviate these issues, while the optimal particle size within host is unclear yet. We here propose an in-situ confinement growth strategy to fabricate pomegranate-structured ZnMn 2 O 4 nanocomposite with calculated optimal particle size in mesoporous carbon host. Theoretical calculations reveal favorable interatomic interactions between the metal atoms. Further, by the synergistic effects of structural merits and bimetal interaction, the optimal ZnMn 2 O 4 composite achieves greatly improved cycling stability (811 mAh g -1 at 0.2 A g -1 after 100 cycles), which can maintain its structural integrity upon cycling. X-ray absorption spectroscopy analysis further confirms delithiated Mn species (Mn 2 O 3 but little MnO). Briefly, this strategy brings new opportunity to ZnMn 2 O 4 anode, which could be adopted to other conversion/alloying-type electrodes.

25 ENERGY STORAGE↗
DOE OSTI2023

Unraveling the convoluted and dynamic interphasial mechanisms on Li metal anode

Accurate understanding of the chemistry of solid-electrolyte interphase (SEI) is key to developing new electrolytes for high-energy batteries using lithium metal (Li-0) anodes(1). SEI is generally believed to be formed by the reactions between Li-0 and electrolyte(2,3). However, our new study shows this is not the whole story. Through synchrotron-based X-ray diffraction and pair distribution function analysis, we reveal a much more convoluted formation mechanism of SEI, which receives considerable contributions from electrolyte, cathode, moisture and native surface species on Li-0, with highly dynamic nature during cycling. Using isotope labelling, we traced the origin of LiH to electrolyte solvent, moisture and a new source: the native surface species (LiOH) on pristine Li-0. When lithium accessibility is very limited as in the case of anode-free cells, LiOH develops into plate-shaped large crystals during cycling. Alternatively, when the lithium source is abundant, as in the case of Li||NMC811 cells, LiOH reacts with Li-0 to form LiH and Li2O. While the desired anion-derived LiF-rich SEI is typically found in the concentrated electrolytes or their derivatives, we found it can also be formed in low-concentration electrolyte via the crosstalk effect, emphasizing the importance of formation cycle protocol and opening up opportunities for low-cost electrolyte development.

Polzin, Bryant J.↗
DOE OSTI2023

Electrolyte design for Li-ion batteries under extreme operating conditions

The ideal electrolyte for the widely used LiNi 0.8 Mn 0.1 Co 0.1 O 2 (NMC811)||graphite lithium-ion batteries is expected to have the capability of supporting higher voltages (≥4.5 volts), fast charging (≤15 minutes), charging/discharging over a wide temperature range (±60 degrees Celsius) without lithium plating, and non-flammability. No existing electrolyte simultaneously meets all these requirements and electrolyte design is hindered by the absence of an effective guiding principle that addresses the relationships between battery performance, solvation structure and solid-electrolyte-interphase chemistry. Here we report and validate an electrolyte design strategy based on a group of soft solvents that strikes a balance between weak Li+-solvent interactions, sufficient salt dissociation and desired electrochemistry to fulfil all the aforementioned requirements. Remarkably, the 4.5-volt NMC811||graphite coin cells with areal capacities of more than 2.5 milliampere hours per square centimetre retain 75 per cent (54 per cent) of their room-temperature capacity when these cells are charged and discharged at -50 degrees Celsius (-60 degrees Celsius) at a C rate of 0.1C, and the NMC811||graphite pouch cells with lean electrolyte (2.5 grams per ampere hour) achieve stable cycling with an average Coulombic efficiency of more than 99.9 per cent at -30 degrees Celsius. The comprehensive analysis further reveals an impedance matching between the NMC811 cathode and the graphite anode owing to the formation of similar lithium-fluoride-rich interphases, thus effectively avoiding lithium plating at low temperatures. Additionally, this electrolyte design principle can be extended to other alkali-metal-ion batteries operating under extreme conditions.

25 ENERGY STORAGE↗
DOE OSTI2023

All-temperature zinc batteries with high-entropy aqueous electrolyte

Electrification of transportation and rising demand for grid energy storage continue to build momentum around batteries across the globe. However, the supply chain of Li-ion batteries is exposed to the increasing challenges of resourcing essential and scarce materials. Therefore, incentives to develop more sustainable battery chemistries are growing. Here, in this paper, we show an aqueous ZnCl 2 electrolyte with introduced LiCl as supporting salt. Once the electrolyte is optimized to Li 2 ZnCl 4 ∙9H 2 O, the assembled Zn–air battery can sustain stable cycling over the course of 800 hours at a current density of 0.4 mA cm -2 between -60 °C and +80 °C, with 100% Coulombic efficiency for Zn stripping/plating. Even at -60 °C, >80% of room-temperature power density can be retained. Advanced characterization and theoretical calculations reveal a high-entropy solvation structure that is responsible for the excellent performance. The strong acidity allows ZnCl 2 to accept donated Cl - ions to form ZnCl 4 2- anions, while water molecules remain within the free solvent network at low salt concentration or coordinate with Li ions. Our work suggests an effective strategy for the rational design of electrolytes that could enable next-generation Zn batteries.

25 ENERGY STORAGE↗
DOE OSTI2022

Tuning discharge voltage by Schottky electron barrier in P2-Na 2/3 Mg 0.205 Ni 0.1 Fe 0.05 Mn 0.645 O 2

Recently, Mg doped Na metal oxide layered cathode compounds have attracted strong interest for Na-ion battery applications. We report a new type of asymmetric phase evolution between charge and discharge is found to show much-enhanced discharge voltage in P2-Na 2/3 Mg 0.205 Ni 0.1 Fe 0.05 Mn 0.645 O 2 over the parent cathode compound. P2 solid solution is found to show an abnormal coexistence with O2-P2 two-phase reaction during discharge with simultaneous reduction of O, Ni, and Fe redoxes, distinct from the conventional P2-O2 two-phase reaction in the charge. Our analysis suggests that the P2 and O2 two-phase boundary forms a novel unidirectional Schottky barrier to impede electron and Na diffusions in discharge only, thus making the kinetically preferred P2 solid solution phase abnormally coexist with the two-phase region for high discharge voltage and low polarization. Our work demonstrates tuning dynamic evolution of electronic Schottky barrier as a new dimension for advanced kinetic design of high-performance battery cathode materials.

25 ENERGY STORAGE↗
DOE OSTI2022

Synergistic effects of chlorine substitution in sulfide electrolyte solid state batteries

All-solid-state battery is considered as one of the most promising competitors to Li ion batteries. Two widely known performance metrics for solid electrolytes, among others, are ionic conductivity and stability. In this study, it is found that both can be improved by the synergistic effects of chlorine substitution in sulfide-based solid electrolytes. Particularly, instabilities arising from both bulk decompositions and interfacial reactions to electrodes can be better inhibited in the chlorine substituted sulfide solid electrolytes through the increased susceptibility to the mechanical constriction induced enhancement of voltage stability. As a result, the stability window of some chlorine-rich Li-argyrodites can be systematically higher than some other chlorine-deficient or chlorine-free electrolytes, especially under the implementation of the mechanical constriction battery assembly and test conditions. Thus, a solid-state battery system of 4 V to 5 V-class cathodes paired with lithium metal anode is demonstrated using these chlorine-rich Li-argyrodites without additional coatings. Furthermore, since Cl composition modulates the stability and instability of Li-argyrodite at low voltages, it allows us to design a multilayer configuration with a hierarchy of Li metal stabilities to demonstrate the stable cycling at relatively high current densities for solid-state batteries. It is found that a moderate Cl composition in the electrolyte is the best to inhibit Li dendrite penetration as the central electrolyte layer, emphasizing a slightly increased “instability” as the hidden performance metric of relevance here, in addition to the two well-known metrics of stability and ionic conductivity. The understanding of the chlorine substitution effect in sulfide electrolytes provides an important design principle for all-solid-state batteries.

25 ENERGY STORAGE↗
DOE OSTI2022

Lithium halide cathodes for Li metal batteries

Lithium halides cathodes potentially offer a high energy density at a low cost for rechargeable batteries. However, these cathodes suffer from quick capacity decay in organic electrolytes and the failiure mechanism remains elusive. Here, we report that liquefying the halogen or interhalogen compounds is a prerequisite for achieving high reversibility for the lithium halides cathodes. The gas or solid halogen can be liquefied by using interhalogen compounds with different electronegativity or changing the temperature. As a proof of concept, reversible LiCl conversion-intercalation chemistry in organic electrolyte is demonstrated by using either redox coupling with less electronegative I/Br to form liquid ICl/BrCl or reducing the temperature to -30oC. Further, the LiCl-LiBr-graphite cathodes in 1.6M lithium difluoro(oxalato)borate/1.6M lithium triflate in diglyme electrolytes achieve a high reversible specific capacity of 250 mAh/g at 3.7 V with an energy density being comparable to or higher than transition metal oxide cathodes at a much lower cost.

25 ENERGY STORAGE↗
DOE OSTI2022

Ultra-fast non-equilibrium synthesis of cathode materials for Li-ion batteries

Synthesis of cathode materials plays an important role in determining the production efficiency, cost and performance of lithium-ion batteries. However, the conventional synthesis methods always experience a slow heating rate and involve a complicated multi-step reaction process and sluggish reaction dynamics, leading to high energy and long time consuming. Herein, we report a high-temperature shock (HTS) strategy for the ultra-fast synthesis of cathode materials in seconds. The HTS process experiences an ultra-high heating rate, leading to a non-equilibrium reaction and fast reaction kinetics and avoiding high energy and long time consuming. Mainstream cathode materials (such as LiMn 2 O 4 , LiCoO 2 , LiFePO 4 , and Li-rich layered oxide/NiO heterostructured material) are successfully synthesized with pure phases, oxygen vacancies, ultra-small particle sizes and good electrochemical performance. In conclusion, the HTS process not only provides an efficient synthesis approach for cathode materials but also can be extended beyond lithium-ion batteries.

25 ENERGY STORAGE↗
DOE OSTI2022

Use of Ethylene Carbonate Free Ester Solvent Systems with Alternative Lithium Salts for Improved Low-Temperature Performance in NCM622∣∣ Graphite Li-ion Batteries

An investigation of alternative lithium salts, lithium tetrafluoroborate (LiBF 4 ), lithium difluoro(oxalato)borate (LiDFOB) and lithium hexafluorophosphate (LiPF 6 ), in novel ester-based (methyl acetate/fluoroethylene carbonate- MA/FEC or methyl propionate/fluoroethylene carbonate- MP/FEC) electrolyte formulations has been conducted in LiNi 0.6 Co 0.2 Mn 0.2 O 2 (NCM622)/graphite cells to improve low temperature cycling performance of lithium ion batteries at −20 °C. Improved low temperature performance was observed with all the lithium salts in MA/FEC electrolyte while comparable room temperature (25 °C) capacities were observed with LiPF 6 salt only. Detailed ex-situ analysis of surface films generated with LiBF 4 , LiDFOB and LiPF 6 in ester-based electrolytes reveals that the solid electrolyte interphase (SEI) is predominately composed of lithium salt decompaction products and addition of 10% FEC (by volume%) may not be sufficient at forming a protective SEI.

25 ENERGY STORAGE↗
DOE OSTI2022

Enabling Conversion-Type Iron Fluoride Cathode by Halide-Based Solid Electrolyte

The practical application of low-cost and energy-dense iron fluoride cathodes has been hindered by the first cycle electrochemical irreversibility, cycling instability, and large voltage hysteresis. Here, we report that these challenges may be overcome by the utilization of halide-based solid electrolytes (SEs). The excellent electrochemical stability of halide-based SEs enables a complete conversion and deconversion of FeF 2 which cannot be achieved with sulfide-based SEs. Due to restricted and reversible decomposition of SE, prevention of Fe dissolution, mechanical confinement of active material, as well as improved electrode kinetics, solid-state FeF 2 cathode with halide-based SE demonstrated superior electrochemical performance compared with FeF 2 electrodes in liquid electrolytes, with a high 1st cycle coulombic efficiency (~100 %), high specific capacity (~600 mAh/g), long cycle life (>100 cycles) and high-rate performance (up to 2C). In conclusion, our results suggest solidifying the batteries may be a viable approach to addressing the long-standing key challenges of iron fluoride cathodes.

25 ENERGY STORAGE↗
DOE OSTI2022

High Current-Density-Charging Lithium Metal Batteries Enabled by Double-Layer Protected Lithium Metal Anode

The practical application of lithium (Li) metal anode (LMA) is still hindered by non-uniformity of solid electrolyte interphase (SEI), formation of "dead" Li, and continuous consumption of electrolyte although LMA has an ultrahigh theoretical specific capacity and a very low electrochemical redox potential. Herein, we report a facile protection strategy for LMA using a double layer (DL) coating that consists of a polyethylene oxide (PEO)-based bottom layer which is highly stable with LMA and promotes uniform ion flux, and a cross-linked polymer-based top layer which prevents solvation of PEO layer in electrolytes. Li deposited on DL-coated Li (DL@Li) exhibits a smoother surface and much larger size than that deposited on bare Li. The LiF/Li 2 O enriched SEI layer generated by the salt decomposition on top of DL@Li further suppresses the side reactions between Li and electrolyte. Driven by the abovementioned advantageous features, the DL@Li||LiNi 0.6 Mn 0.2 Co 0.2 O 2 cells demonstrate capacity retention of 92.4% after 220 cycles at a current density of 2.1 mA cm -2 (C/2 rate) and stability at a high charging current density of 6.9 mA cm -2 (1.5C rate). These results indicate that the DL protection is promising to overcome the rate limitation of LMAs and high energy-density Li metal batteries.

25 ENERGY STORAGE↗
DOE OSTI2022

High-Entropy and Superstructure-Stabilized Layered Oxide Cathodes for Sodium-Ion Batteries

Layered transition metal oxides are appealing cathodes for sodium-ion batteries due to their overall advantages in energy density and cost. But their stabilities are usually compromised by the complicated phase transition and the oxygen redox, particularly when operating at high voltages, leading to poor structural stability and substantial capacity loss. Here, in this study, an integrated strategy combing the high-entropy design with the superlattice-stabilization to extend the cycle life and enhance the rate capability of layered cathodes is reported. It is shown that the as-prepared high-entropy Na 2/3 Li 1/6 Fe 1/6 Co 1/6 Ni 1/6 Mn 1/3 O 2 cathode enables a superlattice structure with Li/transition metal ordering and delivers excellent electrochemical performance that is not affected by the presence of phase transition and oxygen redox. It achieves a high reversible capacity (171.2 mAh g –1 at 0.1 C), a high energy density (531 Wh kg –1 ), extended cycling stability (89.3% capacity retention at 1 C for 90 cycles and 63.7% capacity retention at 5 C after 300 cycles), and excellent fast-charging capability (78 mAh g –1 at 10 C). This strategy would inspire more rational designs that can be leveraged to improve the reliability of layered cathodes for secondary-ion batteries.

25 ENERGY STORAGE↗
DOE OSTI2022

Localized Hydrophobicity in Aqueous Zinc Electrolytes Improves Zinc Metal Reversibility

The rechargeability of aqueous zinc metal batteries is plagued by parasitic reactions of the zinc metal anode and detrimental morphologies such as dendritic or dead zinc. To improve the zinc metal reversibility, hereby we report a new solution structure of aqueous electrolyte with hydroxyl-ions scavengers and hydrophobicity localized in solvent clusters. In this work we show that although hydrophobicity sounds counterintuitive for an aqueous system, hydrophilic pockets may be encapsulated inside a hydrophobic outer layer and a hydrophobic anode-electrolyte interface can be generated through the addition of a cation-philic, strongly anion-phobic, and OH - -reactive diluent. The localized hydrophobicity enables less active water and less absorbed water on the Zn anode surface, which suppresses the parasitic water reductions; while the hydroxyl-ion-scavenging functionality further minimizes undesired passivation layer formation, thus leading to superior reversibility (an average Zn plating/stripping efficiency of 99.72% for 1000 cycles) and lifetime (80.6% capacity retention after 5000 cycles) of zinc batteries.

25 ENERGY STORAGE↗
DOE OSTI2022

Dual Passivation of Cathode and Anode through Electrode–Electrolyte Interface Engineering Enables Long-Lifespan Li Metal–SPAN Batteries

The reliability and durability of lithium metal (Li 0 )–sulfur batteries are largely limited by the undesired Li 0 plating-stripping irreversibility and the detrimental polysulfide dissolution, yet approaches that can simultaneously address the above anodic and cathodic problems are scarce. In this study, we report the stable operation of a Li 0 -SPAN (sulfurized polyacrylonitrile) battery via an anode–cathode dual-passivation approach. By combination of a fluorinated localized high concentration electrolyte (LHCE) and a Li 3 N-forming additive (TMS-N 3 ), robust and highly conductive electrode passivation layers are formed in situ on the surface of both the Li 0 anode and the SPAN cathode. The resulting highly reversible, dendrite-free, and high-density Li 0 plating morphology enables a high Coulombic efficiency of 99.4%. Advanced tender energy X-ray spectroscopy also reveals the eliminated Li 2 S formation and minimized polysulfide dissolution in SPAN cathodes, leading to a high capacity of 580 mAh/g SPAN and stable cycling with negligible capacity decay (0.7%) for 800 cycles. This electrode–electrolyte interphase engineering strategy has tackled the major limitations of Li–S batteries in both ether- and carbonate-based electrolyte systems and under a wide temperature range from –10 to +50 °C, thus providing insightful guidelines for the rational design of highly durable and high-energy-density Li 0 -S batteries.

25 ENERGY STORAGE↗
DOE OSTI2022

Batteries (2021 Annual Progress Report)

This document summarizes the progress of VTO battery R&D projects supported during the fiscal year 2021 (FY 2021). In FY 2021, the DOE VTO battery R&D funding was approximately $\$$115 million. Its R&D focus was on the development of high-energy batteries for EVs as well as very high-power devices for hybrid vehicles. The electrochemical energy storage roadmap (which can be found at the EERE Roadmap web page2) describes ongoing and planned efforts to develop electrochemical storage technologies for EVs. To advance battery technology, which can in turn improve market penetration of PEVs, the program investigates various battery chemistries to overcome specific technical barriers, e.g., battery cost, performance, life (both the calendar life and the cycle life), its tolerance to abusive conditions, and its recyclability/sustainability. VTO R&D has had considerable success, lowering the cost of EV battery packs to $\$$185/kWh in 2019 (representing more than 80% reduction since 2008) yet even further cost reduction is necessary for EVs to achieve head-to-head cost competitiveness with ICEs (without Federal subsidies). In addition, today’s batteries also need improvements in such areas as their ability to accept charging at a high rate, referred to as extreme fast charging (XFC) (15 minute charge) – to provide a “refueling” convenience similar to ICEs, and the ability to operate adequately at low temperatures. Research into “next-gen lithium-ion” batteries which would provide such functionalities is one of the R&D focus areas. VTO is funding research on both “next gen” chemistries (which employ an alloy anode and/or a high voltage cathode) and beyond lithium-ion (BLI) chemistries (which can, for example, employ a lithium metal anode).

25 ENERGY STORAGE↗
DOE OSTI2022

Enhancing Li + Transport in NMC811||Graphite Lithium–Ion Batteries at Low Temperatures by Using Low–Polarity–Solvent Electrolytes

LiNi x Co y MnzO 2 (x+y+z=1)||graphite lithium-ion battery (LIB) chemistry promises practical applications. However, its low-temperature (≤ –20°C) performance is poor because the increased resistance encountered by Li + transport in and across the bulk electrolytes and the electrolyte/electrode interphases induces capacity loss and battery failures. Though tremendous efforts have been made, there is still no effective way to reduce the charge transfer resistance (R ct ) which dominates low-temperature LIBs performance. In this work, we propose a strategy of using low-polarity-solvent electrolytes which have weak interactions between the solvents and the Li + to reduce R ct , achieving facile Li + transport at sub-zero temperatures. The exemplary electrolyte enables LiNi 0.8 Mn 0.1 Co 0.1 O 2 ||graphite cells to deliver a capacity of ≈113 mAh g –1 (98% full-cell capacity) at 25°C and to remain 82% of their room-temperature capacity at –20°C without lithium plating at 1/3C. They also retain 84% of their capacity at –30°C and 78% of their capacity at –40°C and show stable cycling at 50°C.

25 ENERGY STORAGE↗