Acceptance criteria for welds in ASTM A106 grade B steel pipe and plate

Based on the RECERT Program findings, NASA-Langley funded a fatigue study of code-unacceptable welds. Usage curves were developed which were based on the structural integrity of the welds. The details of this study are presented in NASA CR-178114. The information presented is a condensation and reinterpretation of the information in NASA CR-178114. This condensation and reinterpretation generated usage curves for welds having: (1) indications 0.20 -inch deep by 0.40-inch long, and (2) indications 0.195-inch deep by 8.4-inches long. These curves were developed using the procedures used in formulating the design curves in Section VIII, Division 2 of the American Society of Mechanical Engineers Boiler and Pressure Vessel Code.

Hudson, C. M.↗
NASA NTRS1986

References and conference proceedings towards the understanding of fracture mechanics

A list of books, reports, periodicals, and conference proceedings, as well as individual papers, centered on specific aspects of fracture phenomenon has been compiled by the ASTM Committee E-24 on Fracture Testing. A list of basic references includes the articles on the development of fracture toughness, evaluation of stress intensity factors, fatigue crack growth, fracture testing, fracture of brittle materials, and fractography. Special attention is given to the references on application of fracture mechanics to new designs and on reevaluation of failed designs, many of them concerned with naval and aircraft structures.

Toor, P. M.↗
NASA NTRS1984

Methods for assessing the structural reliability of brittle materials

Failure from contact-induced surface flaws is considered along with controlled indentation flaws for construction of toughness and fatigue master maps, fatigue properties of ceramics with natural and controlled flaws, and a statistical analysis of size and stress state effects on the strength of an alumina ceramic. Attention is also given to dynamic and static fatigue of a machinable glass ceramic, the effect of multiregion crack growth on proof testing, and a fracture mechanics analysis of defect sizes. Other topics explored are related to the effect of temperature and humidity on delayed failure of optical glass fibers, subthreshold indentation flaws in the study of fatigue properties of ultrahigh-strength glass, the lifetime prediction for hot-pressed silicon nitride at high temperatures, static fatigue in high-performance ceramics, and requirements for flexure testing of brittle materials.

Freiman, S. W.↗
NASA NTRS1983

Pressure system recertification at NASA-Langley Research Center

Langley Research Center pressure systems are being recertified to ensure safe operation of these systems. The procedures for recertifying these pressure systems are reviewed. Generally, the analysis and inspection requirements outlined in the appropriate national consensus codes are followed. In some instances where the requirements of these codes are not met. The systems are analyzed further, repaired, modified and/or tested to demonstrate their structural integrity.

Hudson, C. M.↗
NASA NTRS1982

A compendium of sources of fracture toughness and fatigue crack growth data for metallic alloys. II

A compendium is presented of sources for metallic alloy fracture toughness and fatigue crack growth data, which concentrates on technical reports as the primary source of references and updates the previous Hudson and Seward (1978) compendium references on technical journals. Where available, the accession numbers which are used as code numbers for the ordering of the reports from their publishers are given. The sources of these reports include the AIAA Technical Information Service, the Defense Technical Information Center, the National Technical Information Service, and NASA.

Hudson, C. M.↗
NASA NTRS1981

Methods and models for predicting fatigue crack growth under random loading

Papers are presented in the volume summarizing the baseline data, methodology, procedures, and results of a round-robin analysis which was conducted to predict the fatigue crack growth in 2219-T851 aluminum center-cracked specimens subjected to flight loading in random cycle-by-cycle format. The objective of the analysis was to assess whether data from constant-amplitude fatigue crack growth tests on center-cracked specimens can be used to predict fatigue crack growth lives under random loading. The following approaches are discussed in detail: a root-mean-square approach, a crack-closure model, a multi-parameter yield zone model, and a load-interaction model.

Chang, J. B.↗
NASA NTRS1981

A root-mean-square approach for predicting fatigue crack growth under random loading

A method for predicting fatigue crack growth under random loading which employs the concept of Barsom (1976) is presented. In accordance with this method, the loading history for each specimen is analyzed to determine the root-mean-square maximum and minimum stresses, and the predictions are made by assuming the tests have been conducted under constant-amplitude loading at the root-mean-square maximum and minimum levels. The procedure requires a simple computer program and a desk-top computer. For the eleven predictions made, the ratios of the predicted lives to the test lives ranged from 2.13 to 0.82, which is a good result, considering that the normal scatter in the fatigue-crack-growth rates may range from a factor of two to four under identical loading conditions.

Hudson, C. M.↗
NASA NTRS1979

NASA-Langley Research Center's participation in a round-robin comparison between some current crack-propagation prediction methods

A round-robin study was conducted which evaluated and compared different methods currently in practice for predicting crack growth in surface-cracked specimens. This report describes the prediction methods used by the Fracture Mechanics Engineering Section, at NASA-Langley Research Center, and presents a comparison between predicted crack growth and crack growth observed in laboratory experiments. For tests at higher stress levels, the correlation between predicted and experimentally determined crack growth was generally quite good. For tests at lower stress levels, the predicted number of cycles to reach a given crack length was consistently higher than the experimentally determined number of cycles. This consistent overestimation of the number of cycles could have resulted from a lack of definition of crack-growth data at low values of the stress intensity range. Generally, the predicted critical flaw sizes were smaller than the experimentally determined critical flaw sizes. This underestimation probably resulted from using plane-strain fracture toughness values to predict failure rather than the more appropriate values based on maximum load.

Hudson, C. M.↗
NASA NTRS1977

Recertification of the air and methane storage vessels at the Langley 8-foot high-temperature structures tunnel

This center operates a number of sophisticated wind tunnels in order to fulfill the needs of its researchers. Compressed air, which is kept in steel storage vessels, is used to power many of these tunnels. Some of these vessels have been in use for many years, and Langley is currently recertifying these vessels to insure their continued structural integrity. One of the first facilities to be recertified under this program was the Langley 8-foot high-temperature structures tunnel. This recertification involved (1) modification, hydrotesting, and inspection of the vessels; (2) repair of all relevant defects; (3) comparison of the original design of the vessel with the current design criteria of Section 8, Division 2, of the 1974 ASME Boiler and Pressure Vessel Code; (4) fracture-mechanics, thermal, and wind-induced vibration analyses of the vessels; and (5) development of operating envelopes and a future inspection plan for the vessels. Following these modifications, analyses, and tests, the vessels were recertified for operation at full design pressure (41.4 MPa (6000 psi)) within the operating envelope developed.

Hudson, C. M.↗
NASA NTRS1976

A literature review and inventory of the effects of environment on the fatigue behavior of metals

The current state of knowledge of the effects of gas environments (at atmospheric pressure and below) on the fatigue behavior of metals is reviewed. Among the topics considered are the mechanisms proposed to explain the differences observed in the fatigue behavior of vacuum- and air-tested specimens, the effects of environment on the surface topography of fatigue cycled specimens, the effect of environment on the various phases of the fatigue phenomenon, the effect of prolonged exposure to vacuum on fatigue life, the variation of fatigue life with decreasing gas pressure, and gas evolution during fatigue cycling. Analysis of the findings of this review indicates that hydrogen embrittlement is primarily responsible for decreased fatigue resistance in humid environments, and that dislocations move more easily during tests in vacuum than during test in air. It was found that fatigue cracks generally initiated and propagated more rapidly in air than in vacuum. Prolonged exposure to vacuum does not adversely affect fatigue resistance. The variation of fatigue life with decreasing gas pressure is sometimes stepped and sometimes continuous.

Hudson, C. M.↗
NASA NTRS1975

An investigation of fracture toughness, fatigue-crack growth, sustained-load flaw growth, and impact properties of three pressure vessel steels

The elastic fracture toughness of the three steels is shown to not decrease significantly with decreasing temperature from room temperature to about 244 K (-20 F.). The elastic fracture toughness of the three steels increased with increasing specimen width and thickness. The fatigue-crack-growth data for all three steels fall into relatively narrow scatter bands on plots of rate against stress-intensity range. An equation is shown to predict the upper bounds of the scatter bands reasonably well. Charpy impact energies decreased with decreasing temperature in the nominal temperature range from room temperature to 244 K (-20 F). The nil-ductility temperatures of the steels are discussed.

Hudson, C. M.↗
NASA NTRS1973

A study of fatigue and fracture in 7075-T6 aluminum alloy in vacuum and air environments

Axial load fatigue life, fatigue-crack propagation, and fracture toughness experiments were conducted on sheet specimens made of 7075-T6 aluminum alloy. These experiments were conducted at pressures ranging from atmospheric to 5 x 10 to the minus 8th torr. Analysis of the results from the fatigue life experiments indicated that for a given stress level, lower air pressures produced longer fatigue lives. At a pressure of 5 x 10 to the minus 8th torr fatigue lives were 15 or more times as long as at atmospheric pressure. Analysis of the results from the fatigue crack propagation experiments indicated that for small stress intensity factor ranges the fatigue crack propagation rates were up to twice as high at atmospheric pressure as in vacuum. The fracture toughness of 7075-T6 was unaffected by the vacuum environment. Fractographic examination showed that specimens tested in both vacuum and air developed fatigue striations. Considerably more striations developed on specimens tested at atmospheric pressure, however.

Hudson, C. M.↗
NASA NTRS1973

Effect of specimen thickness of fatigue-crack-growth behavior and fracture toughness of 7075-T6 and 7178-T6 aluminum alloys

A study was made to determine the effects of specimen thickness on fatigue crack growth and fracture behavior of 7075-T6 and 7178-T6 aluminum alloy sheet and plate. Specimen thicknesses ranged from 5.1 to 12.7 mm (0.20 to 0.50 in.) for 7075-T6 and from 1.3 to 6.4 mm (0.05 to 0.25 in.) for 7178-T6. The stress ratios R used in the crack growth experiments were 0.02 and 0.50. For 7075-T6, specimen thickness had relatively little effect on fatigue-crack growth. However, the fracture toughness of the thickness of the thickest gage of 7075-T6 was about two-thirds of the fracture toughness of the thinner gages of 7075-T6. For 7178-T6, fatigue cracks generally grew somewhat faster in the thicker gages than in the thinnest gage. The fracture toughness of the thickest gage of 7178-T6 was about two-thirds of the fracture toughness of the thinner gages of 7178-T6. Stress intensity methods were used to analyze the experimental results. For a given thickness and value of R, the rate of fatigue crack growth was essentially a single-valued function of the stress intensity range for 7075-T6 and 7178-T6. An empirical equation developed by Forman, Kearney, and Engle fit the 7075-T6 and 7178-T6 crack growth data reasonably well.

Hudson, C. M.↗
NASA NTRS1972

Investigation of the effect of vacuum environment on the fatigue and fracture behavior of 7075-T6.

Axial-load fatigue-life, fatigue-crack propagation, and fracture-toughness experiments were conducted on sheet specimens made of 7075-T6 aluminum alloy. These experiments were conducted at air pressures ranging from 101 kN/sq m to 7 micronewtons/sq m to determine the effect of air pressure on fatigue behavior. Analysis of the results from the fatigue-life experiments indicated that for a given stress level, the lower the air pressure was the longer the fatigue life. At a pressure of 7 micronewtons/sq m, fatigue lives were 15 to 30 times longer than at 101 kN/sq m. Analysis of the results from the fatigue-crack-growth experiments indicates that at low values of stress-intensity range, the fatigue-crack-growth rates were approximately twice as high at atmospheric pressure as in vacuum. However, at higher values of stress-intensity range, the fatigue-crack-growth rates were nominally the same in vacuum and at atmospheric pressure.

Hudson, C. M.↗
NASA NTRS1972

An Experimental Investigation of the Effects of Vacuum Environment on the Fatigue Life, Fatigue-Crack-Growth Behavior, and Fracture Toughness of 7075-T6 Aluminum Alloy

Axial load fatigue life, fatigue-crack propagation, and fracture toughness tests were conducted on 0.090-inch thick specimens made of 7075-T6 aluminum alloy. The fatigue life and fatigue-crack propagation experiments were conducted at a stress ratio of 0.02. Maximum stresses ranged from 33 to 60 ksi in the fatigue life experiments, and from 10 to 40 ksi in the fatigue-crack propagation experiments, and fatigue life experiments were conducted at gas pressures of 760, 0.5, 0.05, and 0.00000005 torr. Fatigue-crack-growth and fracture toughness experiments were conducted at gas pressures of 760 and 5 x 10 to the minus 8th power torr. Residual stress measurements were made on selected fatigue life specimens to determine the effect of such stresses on fatigue life. Analysis of the results from the fatigue life experiments indicated that fatigue life progressively increased as the gas pressure decreased. Analysis of the results from the fatigue-crack-growth experiments indicates that at low values of stress-intensity range, the fatigue crack growth rates were approximately twice as high in air as in vacuum. Fracture toughness data showed there was essentially no difference in the fracture toughness of 7075-T6 in vacuum and in air.

Hudson, C. M.↗