Tritium species diffusion on and desorption from γ-LiAlO 2 (100) surface: A first-principles investigation
γ-LiAlO 2 enriched in the 6 Li isotope is a good candidate for tritium (T, 3 H) production in nuclear reactor. In this work, to better understand its 3 H production performance, first-principles calculations are performed to study the 3 H-related species diffusion on and desorption from the γ-LiAlO 2 (100) surface. For the diffusion process, we investigate the pathways and energy barriers for the T and OT diffusion on the pristine and defective γ-LiAlO 2 (100) surfaces. Our results reveal that the O and Li/Al atoms of the surface layer play important roles for T and OT diffusion, respectively. By comparing with its diffusion barrier in bulk γ-LiAlO 2 , the order of energy barrier for T diffusion is: bulk < surface < defective surface, which is reversed for OT diffusion. Space is the prime factor for OT diffusion, while diffusion-mediating atom instead of space becomes the key factor for T diffusion. For the desorption process, we investigate the 3 H-related species (T, OT, T 2 , and T 2 O) desorption from the γ-LiAlO 2 (100) surface. The desorption energies we obtained are so high that the desorption behavior of all the 3 H-related species is nearly prohibited. We expect the possible T 2 or T 2 O release from the large accumulation of 3 H atoms on the surface.
The optimal co-doping of SrFe 1-x Co x O 3-δ oxygen carriers in redox applications
Although the oxygen carrier SrCoO 3 has higher redox activity than SrFeO 3 , cobalt is both more expensive and scarcer than iron, which would hinder the wide implementation of SrCoO 3 . For these reasons, doping SrFeO 3 with Co is a potential compromise, benefitting the redox properties of SrFeO 3 , while still limiting the overall amount of cobalt being used. In this work, to find the optimal level of Co-doping, density functional theory calculations were performed to investigate the Co-doping effect on the oxygen vacancy formation and oxygen migration in SrFe 1- x Co x O 3- δ ( x = 0, 0.125, 0.25, 0.375, 0.5). Our findings show that the oxygen vacancy formation energies ( E f ) decrease with the increase of Co content resulting from the increased composition of the O-2p band at the Fermi level upon Co doping. In particular, the E f decreases nearly 0.5 eV between the x = 0 and x = 0.25 samples while E f only decreases 0.1 eV further as Co content is increased to x = 0.5. We obtain that x = 0.25 is an optimal cost/benefit ratio for Co doping, which is preserved at both low oxygen vacancy concentrations ( δ = 0.0625 values listed above) and at high concentrations of δ = 0.1875 and 0.375. Kinetically, the oxygen migration barrier has slight change upon Co doping due to the similar size of Co and Fe. Therefore, considering both redox activity and economics in reversible oxygen storage applications, x = 0.25 is suggested as the optimal Co-doping value in SrFe 1- x Co x O 3- δ .