NASA NTRSDate not supplied
Thermoplastic Composites (TPCs) are being increasingly considered for aerospace applications given their faster manufacturing cycles and lower cost. The NASA High-Rate Composite Aircraft Manufacturing (HiCAM) project aims to evaluate and mature thermoplastic manufacturing technologies to achieve a 4X – 6X increase in the production rate of Next Generation Single Aisle (NGSA) commercial aircraft. Within the purview of the NASA HiCAM project, this work investigates the response of thermoplastic composites under High Energy Dynamic Impact (HEDI) conditions. HEDI tests were conducted on panels fabricated with a carbon fiber reinforced low melt semi-crystalline resin TC1225 LMPAEK T700G (T700/LMPAEK) material system. A blunt metal projectile was chosen as the impactor which impacted the T700/LMPAEK panels over a range of impact velocities imparted by a gas gun test setup. As expected, lower velocity impacts caused the projectile to rebound, whereas higher velocity impacts resulted in the projectile penetrating the test panels. For the test cases in which the projectile rebounded, the predominant damage modes recorded with Ultrasonic (UT) scans included interlaminar delaminations which exhibited a “rotating fan” like structure when viewed in the through-thickness direction. Additionally, the dynamic deflection of the center point of the back face of the test panels and the velocity of the projectile was also measured during the test. Finite element models were developed to model a test case in which the projectile rebounded. These models were developed using LS-DYNA® wherein the primary objective was to evaluate the ability of the material model MAT299 to capture the dynamic response and damage modes in the T700/LMPAEK test panels. MAT299 is a Deformation Gradient Decomposition (DGD) based Continuum Damage Mechanics (CDM) material model. The interlaminar delaminations were modeled using the cohesive contact formulation available within LS-DYNA, wherein the mixed-mode fracture is captured via the Benzegaggh-Kenane (B-K) mode-dependent fracture energy interpolation law. The above-mentioned modeling methods have mostly been applied to thermoset composites and adapting them to TPCs involves addressing challenges associated with appropriately representing material behavior. Therefore, the proposed paper would discuss the systematic approach taken to adapt thermoset composites modeling practices for applications to TPCs, while appropriately addressing material behavior. The proposed paper would show that the predicted back face center point deflection correlated reasonably well with experimental data and the peak deflection was predicted to be within 5% of the experimental measurements. The projectile rebound velocity, while predicted to be higher than the experimental measurement, was within reasonable bounds. Additionally, it will be shown that the predicted delamination shapes were in reasonable agreement with experimental data.