Impact of Thermoplastic Composites: Testing and Modeling

Abstract

Thermoplastic Composites (TPCs) are being increasingly considered for aerospace applications given their faster manufacturing cycles and lower cost. The NASA High-Rate Composite Aircraft Manufacturing (HiCAM) project aims to evaluate and mature thermoplastic manufacturing technologies to achieve a 4X – 6X increase in the production rate of Next Generation Single Aisle (NGSA) commercial aircraft. Within the purview of the NASA HiCAM project, this work investigates the response of thermoplastic composites under High Energy Dynamic Impact (HEDI) conditions. HEDI tests were conducted on panels fabricated with a carbon fiber reinforced low melt semi-crystalline resin TC1225 LMPAEK T700G (T700/LMPAEK) material system. A blunt metal projectile was chosen as the impactor which impacted the T700/LMPAEK panels over a range of impact velocities imparted by a gas gun test setup. As expected, lower velocity impacts caused the projectile to rebound, whereas higher velocity impacts resulted in the projectile penetrating the test panels. For the test cases in which the projectile rebounded, the predominant damage modes recorded with Ultrasonic (UT) scans included interlaminar delaminations which exhibited a “rotating fan” like structure when viewed in the through-thickness direction. Additionally, the dynamic deflection of the center point of the back face of the test panels and the velocity of the projectile was also measured during the test. Finite element models were developed to model a test case in which the projectile rebounded. These models were developed using LS-DYNA® wherein the primary objective was to evaluate the ability of the material model MAT299 to capture the dynamic response and damage modes in the T700/LMPAEK test panels. MAT299 is a Deformation Gradient Decomposition (DGD) based Continuum Damage Mechanics (CDM) material model. The interlaminar delaminations were modeled using the cohesive contact formulation available within LS-DYNA, wherein the mixed-mode fracture is captured via the Benzegaggh-Kenane (B-K) mode-dependent fracture energy interpolation law. The above-mentioned modeling methods have mostly been applied to thermoset composites and adapting them to TPCs involves addressing challenges associated with appropriately representing material behavior. Therefore, the proposed paper would discuss the systematic approach taken to adapt thermoset composites modeling practices for applications to TPCs, while appropriately addressing material behavior. The proposed paper would show that the predicted back face center point deflection correlated reasonably well with experimental data and the peak deflection was predicted to be within 5% of the experimental measurements. The projectile rebound velocity, while predicted to be higher than the experimental measurement, was within reasonable bounds. Additionally, it will be shown that the predicted delamination shapes were in reasonable agreement with experimental data.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

Sreenivasa R Voleti, Prabhakar M Rao, Joseph Michael Pereira. Impact of Thermoplastic Composites: Testing and Modeling. https://ntrs.nasa.gov/citations/20230012776

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Characterization of Low-Velocity Impact Damage in Toughened Non-Crimp Fabric Laminates

The damage response of resin-infused composites was investigated using quasi-static indentation (QSI) and instrumented drop-weight impact testing. The test specimens were composed of six layers of non-crimp fabrics where each layer contained +45°, 90°, −45°, and 0° plies. The goals of the testing were to identify damage responses that may differ from traditional thermoset materials and provide damage characterization data to evaluate current damage prediction analyses and aid improvements to current damage models. The damage was characterized using X-ray computed tomography (CT) and ultrasonic testing (UT). Incremental QSI loading was used on a single specimen to investigate damage growth in nine steps at progressively higher loads. Realtime acoustic emission data were used to determine the unloading points. Unlike typical thermoset composites, the force-displacement was smooth and showed no obvious indications of damage. The primary damage consisted of large lines of fiber fracture on the plies near the impact surface and delaminations through the thickness. Nine specimens were impacted at nominal impact energies of 25 ft-lbs, 30 ft-lbs, and 35 ft-lbs. The force histories at each energy followed nearly identical paths. Again, no obvious signs of damage were observed in any of the force histories. The general damage response in the dynamic tests was similar to the QSI-loaded specimens. However, repeat specimens impacted with a given impact energy showed variations in the damage. Some characteristics of the damage response were different than those typically observed in thermoset composites and will need to be evaluated using current analysis methods.

Composite Materials↗

Dynamic Crush Performance of Thermoplastic and Resin Infused Thermoset Triaxially Braided Composite Structures

Dynamic crush tests were conducted on triaxially braided composite tubes and C-channel structural elements to measure their relative energy absorbing characteristics. The elements were manufactured from triaxially braided [0/+60/-60] T700 fiber preforms with two different resin systems, a PR520 thermoset resin and a LM-PAEK thermoplastic resin. T700/PR520 composite tubes and C-channel elements were manufactured using a resin infusion process. T700GC/LMPAEK composite tubes were manufactured by braiding slit tape prepreg onto cylindrical mandrels. Consolidation pressure was applied through thermally activated shrink tape in an oven. The energy absorbing characteristics of the composite elements were measured using a pneumatically actuated sled with a flat-faced impacting mass, which provided several independent measurements of force, displacement, and energy absorption. The parameter primarily used for comparison between the systems was the specific energy absorption (SEA), a measure of energy absorbed per unit crushed length. The T700/LMPAEK tubes performed slightly better than T700/PR520 tubes, with an approximately 9% higher SEA. T700/PR520 tubes had over 20% higher SEA than C-channels made from the same material. Additional tests were conducted on tubes using a tapered-conical impactor to force the tubes to fail in circumferential tension. This type of impact significantly reduced the energy absorption.

Composite Materials↗

Modeling of Response of Thermoplastic Composites Under High Energy Impact

This work investigates the response of a thermoplastic panel under high energy ballistic impact. The composite material system is a carbon fiber reinforced low melt semi-crystalline resin TC1225 LMPAEK T700G (T700/LMPAEK3). Several high energy dynamic impact tests were performed where an aluminum projectile impacted various panels at different impact velocities. For this work, the test performed at an impact velocity of 73.2 m/s was investigated. The projectile rebounded upon impact, and the damage to the panel was characterized through ultrasonic and CT-scanning. Response of the panel under impact and the associated damage is discussed. Numerical simulation of the impact process was performed using the LS-DYNA® computer code [1] with a new material model MAT_COMPOSITE_DAMAGE_DGD (MAT 299), a modification over MAT 261 material model in terms of an improved representation of damage coupling and additional capability for strain rate effects. Delaminations were modeled using cohesive zone contact formulation in LS-DYNA®, wherein the mixed-mode fracture is captured via the Benzegaggh-Kenane (B-K) mode-dependent fracture energy interpolation law. Simulation of this impact test demonstrates a good match of results in terms of panel deflection and panel-projectile interactions. The overall extent of delaminations was under-predicted by the simulation. This work forms the basis to model tests performed at higher velocities, involving projectile penetration of panel.

Composite Materials↗