Fatigue Failure Modes of the Grain Size Transition Zone in a Dual Microstructure Disk

Mechanical property requirements vary with location in nickel-based superalloy disks. In order to maximize the associated mechanical properties, heat treatment methods have been developed for producing tailored grain microstructures. In this study, fatigue failure modes of a grain size transition zone in a dual microstructure disk were evaluated. A specialized heat treatment method was applied to produce varying grain microstructure in the bore to rim portions of a powder metallurgy processed nickel-based superalloy disk. The transition in grain size was concentrated in a zone of the disk web, between the bore and rim. Specimens were extracted parallel and transversely across this transition zone, and multiple fatigue tests were performed at 427 C and 704 C. Grain size distributions were characterized in the specimens, and related to operative failure initiation modes. Mean fatigue life decreased with increasing maximum grain size, going out through the transition zone. The scatter in limited tests of replicates was comparable for failures of uniform gage specimens in all transition zone locations examined.

Gabb, Timothy P.↗

NASA NTRS2006

Accelerated Life Structural Benchmark Testing for a Stirling Convertor Heater Head

For proposed long-duration NASA Space Science missions, the Department of Energy, Lockheed Martin, Infinia Corporation, and NASA Glenn Research Center are developing a high-efficiency, 110 W Stirling Radioisotope Generator (SRG110). A structurally significant limit state for the SRG110 heater head component is creep deformation induced at high material temperature and low stress level. Conventional investigations of creep behavior adequately rely on experimental results from uniaxial creep specimens, and a wealth of creep data is available for the Inconel 718 material of construction. However, the specified atypical thin heater head material is fine-grained with a heat treatment that limits precipitate growth, and little creep property data for this microstructure is available in the literature. In addition, the geometry and loading conditions apply a multiaxial stress state on the component, far from the conditions of uniaxial testing. For these reasons, an extensive experimental investigation is ongoing to aid in accurately assessing the durability of the SRG110 heater head. This investigation supplements uniaxial creep testing with pneumatic testing of heater head-like pressure vessels at design temperature with stress levels ranging from approximately the design stress to several times that. This paper presents experimental results, post-test microstructural analyses, and conclusions for four higher-stress, accelerated life tests. Analysts are using these results to calibrate deterministic and probabilistic analytical creep models of the SRG110 heater head.

Krause, David L.↗

NASA NTRS2005

Nickel Base Superalloy Turbine Disk

A low solvus, high refractory alloy having unusually versatile processing mechanical property capabilities for advanced disks and rotors in gas turbine engines. The nickel base superalloy has a composition consisting essentially of, in weight percent, 3.0-4.0 N, 0.02-0.04 B, 0.02-0.05 C, 12.0-14.0 Cr, 19.0-22.0 Co, 2.0-3.5 Mo, greater than 1.0 to 2.1 Nb, 1.3 to 2.1 Ta,3.04.OTi,4.1 to 5.0 W, 0.03-0.06 Zr, and balance essentially Ni and incidental impurities. The superalloy combines ease of processing with high temperature capabilities to be suitable for use in various turbine engine disk, impeller, and shaft applications. The Co and Cr levels of the superalloy can provide low solvus temperature for high processing versatility. The W, Mo, Ta, and Nb refractory element levels of the superalloy can provide sustained strength, creep, and dwell crack growth resistance at high temperatures.

Gabb, Timothy P.↗

NASA NTRS2005

Effects of High-Temperature Exposures on the Fatigue Life of Disk Superalloys Examined

Tests used to characterize the low-cycle-fatigue resistance of disk superalloys are usually performed at cyclic frequencies of 0.33 Hz or faster. However, service conditions for disks in some aerospace and land-based gas turbine engines can produce major cycle periods extending from minutes to hours and days. Over a service life, this can produce total service times near the maximum temperature that exceed 100 hr for aerospace applications and 100,000 hr for land-based applications. Such time-dependent effects of realistic mission cycles on fatigue resistance can be significant in superalloy disks, and need to be considered for accurate disk life prediction. The purpose of this study at the NASA Glenn Research Center was to examine the effects of extended exposures and extended cycle periods on the fatigue resistance of two disk superalloys. Current alloy Udimet 720 (Special Metals Corporation, Huntington, WV) disk material was provided by Solar Turbines/Caterpillar Co., and advanced alloy ME3 was provided by the NASA Ultra-Efficient Engine Technologies (UEET) Project, in powder-metallurgy-processed, supersolvus heat-treated form. Fatigue specimens were fully machined and exposed in air at temperatures of 650 to 704 C for extended times. Then, they were tested using conventional fatigue tests with a total strain range of 0.70 percent and a minimum-to-maximum strain ratio of zero to determine the effects of prior exposure on fatigue resistance. Subsequent tests with extended dwells at minimum strain in each fatigue cycle were performed to determine cyclic exposure effects.

Gabb, Timothy P.↗

NASA NTRS2004

Distribution of Inclusion-Initiated Fatigue Cracking in Powder Metallurgy Udimet 720 Characterized

In the absence of extrinsic surface damage, the fatigue life of metals is often dictated by the distribution of intrinsic defects. In powder metallurgy (PM) alloys, relatively large defects occur rarely enough that a typical characterization with a limited number of small volume fatigue test specimens will not adequately sample inclusion-initiated damage. Counterintuitively, inclusion-initiated failure has a greater impact on the distribution in PM alloy fatigue lives because they tend to have fewer defects than their cast and wrought counterparts. Although the relative paucity of defects in PM alloys leads to higher mean fatigue lives, the distribution in observed lives tends to be broader. In order to study this important failure initiation mechanism without expending an inordinate number of specimens, a study was undertaken at the NASA Glenn Research Center where known populations of artificial inclusions (seeds) were introduced to production powder. Fatigue specimens were machined from forgings produced from the seeded powder. Considerable effort has been expended in characterizing the crack growth rate from inclusion-initiated cracks in seeded PM alloys. A rotating and translating positioning system, with associated software, was devised to map the surface inclusions in low-cycle fatigue (LCF) test bars and to monitor the crack growth from these inclusions. The preceding graph illustrates the measured extension in fatigue cracks from inclusions on a seeded LCF test bar subjected to cyclic loading at a strain range of 0.8 percent and a strain ratio (max/min) of zero. Notice that the observed inclusions fall into three categories: some do not propagate at all (arrest), some propagate with a decreasing crack growth rate, and a few propagate at increasing rates that can be modeled by fracture mechanics. The following graph shows the measured inclusion-initiated crack growth rates from 10 interrupted LCF tests plotted against stress intensities calculated for semi-elliptical cracks with the observed surface lengths. The expected scatter in the crack growth rates for stress intensity ranges near threshold is observed. These data will be used to help determine the distribution in growth rates of cracks emanating from inclusions as well as the proportion of cracks that arrest under various loading conditions.

Bonacuse, Peter J.↗

NASA NTRS2004

Effects of High Temperature Exposures on Fatigue Life of Disk Superalloys

The effects on fatigue life of high temperature exposures simulating service conditions were considered for two disk superalloys. Powder metallurgy processed, supersolvus heat treated Udimet (trademark) 720 and ME3 fatigue specimens were exposed in air at temperatures of 650 to 704 C, for times of 100 h to over 1000 h. They were then tested using conventional fatigue tests at 650 and 704 C, to determine the effects of exposure on fatigue resistance. Cyclic dwell verification tests were also performed to contrast the effects of intermixed exposures and fatigue cycles. The prior exposures reduced life by up to 70% and increased the scatter in life, compared to unexposed levels. Cyclic dwell tests reduced lives even more. Fractographic evaluations indicated the failure mode was shifted by the exposures and cyclic dwells from predominantly internal to often surface crack initiations. The increased scatter in life was related to the competition between internal crack initiations at inclusions or large grains producing longer lives, and surface crack initiations at an environmentally affected surface layer producing shorter lives.

Gabb, Tim P.↗

NASA NTRS2003

Versatile Turbine Disk Alloy Designed and Processed for Higher Temperature Applications

Advanced turbine engine configurations using higher temperature combustor and airfoil concepts require compressor and turbine disks that can withstand temperatures higher than the 650 C typical of current engines. This requires disk alloy and processing improvements. A versatile disk alloy was needed that could be given either fine grain heat treatments for high strength and fatigue and creep resistance up to 704 C or given coarse grain heat treatments for high strength and creep and dwell crack-growth resistance at higher temperatures. This alloy could produce disks with uniform microstructures and properties, as well as with varied, optimized microstructures at disk bore and rim sections. A series of experimental disk alloys were designed and processed to give subscale disks about 13 cm in diameter and 4 cm thick. These alloys had varying levels of key elements to affect mechanical properties and change the "solvus" solution heat-treatment temperature necessary to produce coarse grain microstructures. Disks were given coarse grain heat treatments followed by rapid oil quenching and slower fan air quenching. These heat treatments were intended to simulate the cooling paths of rapidly cooled full-scale disks at the outermost rim and interior bore locations, respectively. Preliminary quench tests of tensile specimens and coin-size minidisks had indicated that alloys having high solvus temperatures were more prone to cracking during rapid quenching from coarse grain heat treatments. These findings were confirmed in the subscale disks, where such alloys did form undesirable quench cracks. Mechanical tests were performed on specimens from subscale disks given these coarse grain heat treatments, as well as on specimens given a fine grain heat treatment. Tensile, creep, and crack growth tests were performed at 704 C and higher temperatures. A versatile alloy was identified that had a low solvus temperature for resistance to quench cracking as well as an optimal combination of high levels of strengthening refractory elements that produced balanced high mechanical properties for both fine grain and coarse grain microstructures. This low-solvus, high-refractory (LSHR) alloy has been scaled-up to produce prototype full-scale turbine disks typical of regional jet turbofan engines. Disks were successfully heat treated to give uniform coarse grain and uniform fine grain microstructures. Additional disks were given a NASA dual microstructure heat treatment (DMHT) that intentionally varied the solution heat-treatment temperatures between the disk rim and bore (re f. 1). The disk rim was heated to a high enough temperature to produce a coarse grain microstructure, while the bore was maintained at a lower temperature to produce a fine grain microstructure (see the figure). This DMHT can produce optimal high strength, fatigue, and creep resistance up to 704 C in the cooler running disk bore, and high strength, creep resistance, and dwell crack growth resistance at higher temperatures for the hotter disk rim. Extensive mechanical testing is being initiated to compare the mechanical properties of the uniform and DMHT disks.

Gabb, TImothy P.↗

NASA NTRS2003

Superalloy Disk With Dual-Grain Structure Spin Tested

Advanced nickel-base disk alloys for future gas turbine engines will require greater temperature capability than current alloys, but they must also continue to deliver safe, reliable operation. An advanced, nickel-base disk alloy, designated Alloy 10, was selected for evaluation in NASA s Ultra Safe Propulsion Project. Early studies on small test specimens showed that heat treatments that produced a fine grain microstructure promoted high strength and long fatigue life in the bore of a disk, whereas heat treatments that produced a coarse grain microstructure promoted optimal creep and crack growth resistance in the rim of a disk. On the basis of these results, the optimal combination of performance and safety might be achieved by utilizing a heat-treatment technology that could produce a fine grain bore and coarse grain rim in a nickel-base disk. Alloy 10 disks that were given a dual microstructure heat treatment (DMHT) were obtained from NASA s Ultra-Efficient Engine Technology (UEET) Program for preliminary evaluation. Data on small test specimens machined from a DMHT disk were encouraging. However, the benefit of the dual grain structure on the performance and reliability of the entire disk still needed to be demonstrated. For this reason, a high temperature spin test of a DMHT disk was run at 20 000 rpm and 1500 F at the Balancing Company of Dayton, Ohio, under the direction of NASA Glenn Research Center personnel. The results of that test showed that the DMHT disk exhibited significantly lower crack growth than a disk with a fine grain microstructure. In addition, the results of these tests could be accurately predicted using a two-dimensional, axisymmetric finite element analysis of the DMHT disk. Although the first spin test demonstrated a significant performance advantage associated with the DMHT technology, a second spin test on the DMHT disk was run to determine burst margin. The disk burst in the web at a very high speed, over 39 000 rpm, in line with the predicted location and speed. Furthermore, significant growth of the disk was observed before failure, in line with predictions, clearly demonstrating the reliability and safety of the DMHT technology. Although successful spin testing in Ultra Safe's Nickel Disk Program represents a significant milestone for DMHT technology, realistic engine operation will require repeated loading of a DMHT nickel disk. For this reason, a cyclic spin test study of DMHT nickel disk technology has been proposed to start in fiscal year 2003 under NASA's Aviation Safety Program. The goal of this program will be to determine the fatigue failure mechanism in DMHT nickel disks, thereby demonstrating the reliability and safety of DMHT technology under repetitive loading conditions encountered in realistic engine operation.

Gayda, John↗

NASA NTRS2002

Mechanical Testing of IN718 Lattice Block Structures

Lattice block construction produces a flat, structurally rigid panel composed of thin ligaments of material arranged in a three-dimensional triangulated truss-like structure. Low-cost methods of producing cast metallic lattice block panels are now available that greatly expand opportunities for using this unique material system in today's high-performance structures. Additional advances are being made in NASA's Ultra Efficient Engine Technology (UEET) program to extend the lattice block concept to superalloy materials. Advantages offered by this combination include high strength, light weight, high stiffness, and elevated temperature capabilities. Recently under UEET, the nickel-based superalloy Inconel 718 (IN718) was investment cast into lattice block panels with great success. To evaluate casting quality and lattice block architecture merit, individual ligaments, and structural subelement specimens were extracted from the panels. Tensile tests, structural compression, and bending strength tests were performed on these specimens. Fatigue testing was also completed for several bend test specimens. This paper first presents metallurgical and optical microscopy analysis of the castings. This is followed by mechanical test results for the tensile ligament tests and the subelement compression and bending strength tests, as well as for the fatigue tests that were performed. These tests generally showed comparable properties to base IN718 with the same heat treatment, and they underscored the benefits offered by lattice block materials. These benefits might be extended with improved architecture such as face sheets.

Krause, David L.↗

NASA NTRS2001

The Tensile Properties of Advanced Nickel-Base Disk Superalloys During Quenching Heat Treatments

There is a need to increase the temperature capabilities of superalloy turbine disks. This would allow full utilization of higher temperature combustor and airfoil concepts under development. One approach to meet this goal is to modify the processing and chemistry of advanced alloys, while preserving the ability to use rapid cooling supersolvus heat treatments to achieve coarse grain, fine gamma prime microstructures. An important step in this effort is to understand the key high temperature tensile properties of advanced alloys as they exist during supersolvus heat treatments. This could help in projecting cracking tendencies of disks during quenches from supersolvus heat treatments. The objective of this study was to examine the tensile properties of two advanced disk superalloys during simulated quenching heat treatments. Specimens were cooled from the solution heat treatment temperatures at controlled rates, interrupted, and immediately tensile tested at various temperatures. The responses and failure modes were compared and related to the quench cracking tendencies of disk forgings.

Gabb, Timothy P.↗