Kazaroff, J. M.

Publications and source records attributed to Kazaroff, J. M..

12 records

NASA NTRS1990

A life comparison of tube and channel cooling passages for thrust chambers

The life analysis used to compare copper tubes and milled copper channels for rocket engine cooling passages is described. Copper tubes were chosen as a possible replacement for the existing milled copper channel configuration because (1) they offer increased surface area for additional enthalpy extraction; (2) they have ideal pressure vessel characteristics; and (3) the shape of the tube is believed to allow free expansion, thus accommodating the strain resulting from thermal expansion. The analysis was a two-dimensional elastic-plastic comparison, using a finite element method, to illustrate that, under the same thermal and pressure loading, the compliant shape of the tube increases the life of the chamber. The analysis indicates that for a hot-gas-side-wall temperature of 100 F the critical strain decreases from 1.25 percent in the channel to 0.94 percent in the tube. Since the life of rocket thrust chambers is most often limited by cyclic strain or strain range, this decrease corresponds to an expected tube life which is nearly twice the channel life.

Jankovsky, R. S.↗

NASA NTRS1989

Iridium-coated rhenium thrusters by CVD

Operation of spacecraft thrusters at increased temperature reduces propellant requirements. Inasmuch as propellant comprises the bulk of a satellite's mass, even a small percentage reduction makes possible a significant enhancement of the mission in terms of increased payload. Because of its excellent high temperature strength, rhenium is often the structural material of choice. It can be fabricated into free-standing shapes by chemical vapor deposition (CVD) onto an expendable mandrel. What rhenium lacks is oxidation resistance, but this can be provided by a coating of iridium, also by CVD. This paper describes the process used by Ultramet to fabricate 22-N (5-lbf) and, more recently, 445-N (100-lbf) Ir/Re thrusters; characterizes the CVD-deposited materials; and summarizes the materials effects of firing these thrusters. Optimal propellant mixture ratios can be employed because the materials withstand an oxidizing environment up to the melting temperature of iridium, 2400 C (4350 F).

Harding, J. T.↗

NASA NTRS1981

Heat exchanger and method of making

A heat exchanger of increased effectiveness is disclosed. A porous metal matrix is disposed in a metal chamber or between walls through which a heat transfer fluid is directed. The porous metal matrix has internal bonds and is bonded to the chamber in order to remove all thermal contact resistance within the composite structure. Utilization of the invention in a rocket chamber is disclosed as a specific use. Also disclosed is a method of constructing the heat exchanger.

Fortini, A.↗

NASA NTRS1980

Compact, super heat exchanger

Heat exchanger uses porous media to enhance heat transfer through walls of cooling channels, thereby lowering wall temperature. Porous media within cooling channel increases internal surface area from which heat can be transferred to coolant. Comparison data shows wall has lower temperature and coolant has higher temperature when porous medium is used within heat exchanger. Media can be sintered powedered metal, metal fibers, woven wire layers, or any porous metal having desired permeability and porosity.

Fortini, A.↗

NASA NTRS1980

Heat exchanger and method of making

A heat exchange of increased effectiveness is disclosed. A porous metal matrix is disposed in a metal chamber or between walls through which a heat-transfer fluid is directed. The porous metal matrix has internal bonds and is bonded to the chamber in order to remove all thermal contact resistance within the composite structure. Utilization of the invention in a rocket chamber is disclosed as a specific use. Also disclosed is a method of constructing the heat exchanger.

Fortini, A.↗

NASA NTRS1978

Heat exchanger and method of making

A heat exchanger of increased effectiveness is disclosed. A porous metal matrix is disposed in a metal chamber or between walls through which a heat-transfer fluid is directed. The porous metal matrix has internal bonds and is bonded to the chamber in order to remove all thermal contact resistance within the composite structure. Utilization of the invention in a rocket chamber is disclosed as a specific use. Also disclosed is a method of constructing the heat exchanger.

Fortini, A.↗

NASA NTRS1978

Investigation of the effect of ceramic coatings on rocket thrust chamber life

Two cylindrical rocket thrust chamber cylinders were coated with a 0.203 mm layer of zirconium oxide using a process that employed electrodeposition of metal to a spray-coated mandrel. The cylinders were cyclically tested using hydrogen-oxygen propellants at a nominal chamber pressure of 4.14 MN/sq m to show the effect of the coating on life. Both cylinders failed prematurely due to causes unrelated to the coatings. Post destructive analysis showed no cooling passage wall deformation. Where erosion of the coating occurred, the coating thickness stabilized at 0.061 mm within 80 cycles and remained well adhered throughout the tests. The hot-gas-side metal wall temperature and the theoretical maximum effective strain were reduced by 80 and 92%, respectively, where the coating was 0.203 mm thick and by 40 and 50%, respectively, where the coating was 0.061 mm thick compared to an uncoated cylinder. The 50 and 92% reductions in maximum effective strain resulted in theoretical lives of 1900 cycles and greater than 10,000 cycles, respectively, compared to 300 cycles for the uncoated cylinder.

Quentmeyer, R. J.↗

NASA NTRS1978

Investigation of the effect of ceramic coatings on rocket thrust chamber life

Cylindrical rocket thrust chamber cylinders were coated with a 0.203 mm (0.008 in.) layer of zirconium oxide using a process that employed electrodeposition of metal to a spray coated mandrel. The cylinders were cyclically tested using hydrogen oxygen propellants at a nominal chamber pressure of 4.14 MN/sq m (600 psia) to show the effect of the coating on life. Both cylinders failed prematurely due to causes unrelated to the coatings. Post destructive analysis showed no cooling passage wall deformation. Where erosion of the coating occurred, the coating thickness stabilized at 0.061 mm (0.0024 in.) within 80 cycles and remained well adhered throughout the tests.

Quentmeyer, R. J.↗

NASA NTRS1974

Fabrication of thick structures by sputtering

Deposit, 5500-gram of Cu-0.15 wt % Zr alloy, sputtered onto copper cylinder to average thickness of 12.29 mm. Structure was achieved with high-rate sputter deposition for about 100 hours total sputtering time. Material had twice the strength of unsputtered material at temperatures to 723 K and equivalent strength at nearly 873 K.

Kazaroff, J. M.↗

NASA NTRS1974

Fabrication of liquid-rocket thrust chambers by electroforming

Electroforming has proven to be an excellent fabrication method for building liquid rocket regeneratively cooled thrust chambers. NASA sponsored technology programs have investigated both common and advanced methods. Using common procedures, several cooled spool pieces and thrust chambers have been made and successfully tested. The designs were made possible through the versatility of the electroforming procedure, which is not limited to simple geometric shapes. An advanced method of electroforming was used to produce a wire-wrapped, composite, pressure-loaded electroformed structure, which greatly increased the strength of the structure while still retaining the advantages of electroforming.

Duscha, R. A.↗

NASA NTRS1974

High strength, wire-reinforced electroformed structures

Using half-round reinforcing wires, electrodeposited matrix metal readily fills spaces between wires in intimate contact with wires and without voids. Procedure combines advantages of electroforming with high-strength of commonly available wire to produce non-welded shell structures for high pressure uses.

Kazaroff, J. M.↗

NASA NTRS1970

Properties of Hot Pressed Titanium Alloy Powders for Cryogenic Applications.

Evaluation of strength and toughness of hot-pressed titanium alloy powders at room and at cryogenic temperatures. The purpose was to determine how the mechanical properties of solid bodies formed from powder would compare with wrought specimens of the same size and with the same chemical analysis. It was found that of five titanium powder-making processes investigated, only the Rotating Electrode Process (REP) was capable of producing ELI-grade titanium alloy powder. Blocks hot-pressed from spherical REP powders had tensile properties equivalent to or better than those obtained from wrought bar.

Friedman, G. I.↗